, Volume 41, Issue 17, pp 5417–5423 | Cite as

Effect of rolling and epitaxial ferrite on the tensile properties of low alloy steel

  • E. Ahmad
  • M. Sarwar
  • T. Manzoor
  • N. Hussain
Article

Abstract

A low alloy steel containing 0.09% C was thermomechanically processed at the intercritical annealing temperature of 790 °C to produce dual-phase microstructure from 50% of austenite. After applying different rolling reductions at this temperature, the specimens were quenched in boiling water to promote the growth of epitaxial ferrite. Warm rolling at 790 °C decreased the hardenability of austenite due to increased in interfacial area of austenite and ferrite. Tensile strength was improved by increasing the rolling reductions both in longitudinal and transverse directions without any significant loss in ductility attributed to the presence of epitaxial ferrite. Microvoid formation in the necked region and their percentage area fraction was measured. The correlation between the area fractions of microvoids formation with strain in the necked region ultimately defined the mode of failure.

Keywords

Ferrite Austenite Martensite Pearlite Dual Phase Steel 

References

  1. 1.
    Dinda S, Di Cello JA, Kasper AS (1975) In: Microalloyin 75. Union Carbide, Washington, p 33Google Scholar
  2. 2.
    Rashid MS (1979) In: Davenport AT (ed) Formable HSLA and dual phase steels. AIME, New York, NY, pp 1–24Google Scholar
  3. 3.
    Owen WS (1980) Met Technol 7:1CrossRefGoogle Scholar
  4. 4.
    Bittence JC (1978) Mater Eng 87(5):39Google Scholar
  5. 5.
    Sarwar M, Priestner R (1996) J Mater Sci 31:2091CrossRefGoogle Scholar
  6. 6.
    Ahmad E, Priestner R (1998) J Mater Eng Perform 7(6):772CrossRefGoogle Scholar
  7. 7.
    Ahmad E, Manzoor T, Liaqat Ali K, Akhter JI (2000) J Mater Eng Perform 9(3):306CrossRefGoogle Scholar
  8. 8.
    Sin S, Pugh M (2002) Mater Sci Eng 335(1–2):298CrossRefGoogle Scholar
  9. 9.
    Erdogen M, Tekeli S (2002) Mater Des 23:597CrossRefGoogle Scholar
  10. 10.
    Lawson R, Matlock DK, Krauss G (1980) Metallography 13:71CrossRefGoogle Scholar
  11. 11.
    Speich GR, Miller RI (1979) In: Kot RA, Morris JW (eds), Structures and properties of dual phase steels. TMS-AIME, Warrendale, PA pp 145Google Scholar
  12. 12.
    Ajmal M, Priestner R (1988) In: Tamura I (ed) Int. Conf. Phys. Met. T. M. P. Steel and other Metal. ISIJ, pp 642–691Google Scholar
  13. 13.
    Priestner R (1987). Conf. Proc., Phase Transformation87. Institute of Metals, CambridgeGoogle Scholar
  14. 14.
    Tanaka T (1985) Intern Metal Rev 4:185Google Scholar
  15. 15.
    Steinbrunner DL, Matlock DK, Krauss G (1988) Met Trans 19(A):579CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2006

Authors and Affiliations

  1. 1.Nuclear Materials DivisionPINSTECHIslamabadPakistan

Personalised recommendations