Microwave assisted synthesis of nanocrystalline YAG

  • B. Vaidhyanathan
  • J. G. P. Binner
Article

Abstract

Using nitrate precursors, a novel microwave assisted citrate gel process for the preparation of nanocrystalline yttrium aluminium garnet (YAG) phase has been developed. Synthesis of single phase polycrystalline YAG was achieved at temperatures as low as 600 °C using the microwave methodology whilst conventional approaches currently available require ≥1000 °C. The microwave prepared YAG powder was characterised using X-ray diffraction, FTIR spectroscopy, TEM and EDAX. The microwave method was found to yield YAG particles of ∼40 nm diameter, whilst the conventional route yielded 150 nm particles. Also substantial morphological differences were observed between the YAG particles and their agglomerates produced by the different processing methods.

Keywords

Yttrium Aluminium Garnet Primary Particle Size YAlO3 Yttrium Nitrate Bulk Nucleation 

Notes

Acknowledgements

The authors thank the EPSRC in the UK for financial support.

References

  1. 1.
    Zhang J, Ning J, Liu X, Pan Y, Huang L (2003) Mater Res Bull 38:1249CrossRefGoogle Scholar
  2. 2.
    Lu Q, Dong W, Wang H, Wang X (2002) J Amer Ceram Soc 85:490CrossRefGoogle Scholar
  3. 3.
    Vaqueiro P, Lopez-Quintela MA (1998) J Mater Chem 8:161CrossRefGoogle Scholar
  4. 4.
    Gowda GJ (1986) Mater Sci Lett 5:1029CrossRefGoogle Scholar
  5. 5.
    Vaidhyanathan B, Singh AP, Agrawal DK, Roy R, Ganguly C (2001) J Amer Ceram Soc 84:1197CrossRefGoogle Scholar
  6. 6.
    Vaidhyanathan B, Annapoorani K, Binner JGP, Raghavendra R (2003) In: Foltz D, Booske JH, Clark DE, Gerling JF (eds) Microwave processing and applications. The American Ceramic Society, Westerville, OH, p 423Google Scholar
  7. 7.
    Vaidhyanathan B, Agrawal DK, Roy R (2000) J Mater Res 15:974CrossRefGoogle Scholar
  8. 8.
    Yamaguchi O, Takeoka K, Hirota K, Takano H, Hayashida A (1992) J Mater Sci Lett 27:1261CrossRefGoogle Scholar
  9. 9.
    Apte P, Burke H, Pickup H (1992) J Mater Res 7:706CrossRefGoogle Scholar
  10. 10.
    Panneer Selvam M, Subanna GN, Rao KJ (2001) J Mater Res 16:2773CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2006

Authors and Affiliations

  1. 1.Institute of Polymer Technology and Materials EngineeringLoughborough UniversityLoughboroughUK

Personalised recommendations