Utilization of technogenic material from an oil-processing company in the production of building ceramics
Utilization of Waste
- 27 Downloads
- 1 Citations
Abstract
The results of studying the possibility of using a technogenic material (catalyst) in the production of building ceramics are discussed. The physicochemical properties and structural parameters of ceramic samples are given. In the case of introducing the catalyst in a molding mixture, the firing temperature should be increased and the amount of the catalyst should not exceed 7–10%.
Keywords
Physicochemical Property Ceramic Sample Firing Temperature Molding Mixture Technogenic Material
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
Preview
Unable to display preview. Download preview PDF.
References
- 1.N. A. Vil’bitskaya, S. P. Golovanova, A. P. Zubekhin, N. D. Yatsenko, Steklo Keram., No. 4, 21–23 (2002) (Glass and Ceram., 59(3–4)).Google Scholar
- 2.G. I. Yakovlev, “Ceramic materials based on acid fluoride,” Steklo Keram., No. 9, 18–20 (2002) (Glass and Ceram., 59(9–10)).Google Scholar
- 3.S. Yu. Goberis and A. B. Shtuopis, “Study of refractory concrete containing oil-processing waste catalyst,” Ogneup. Tekh. Keram., No. 1, 19–22 (1997).Google Scholar
- 4.G. S. Souza, R. S. Santos, and J. N. F. Holanda, “Recycling of a petroleum waste in ceramic bodies,” Mater. Sci. Forum, 418, 743–747 (2003).CrossRefGoogle Scholar
- 5.R. Žurauskinė, R. Mačiulaitis, F. Petrikaitis, “Usability of Lithuanian fusible clay for sintered ceramic,” Civil Eng., VII(3), 191–196 (2001).Google Scholar
Copyright information
© Springer Science+Business Media, Inc. 2006