Removal of chromium(VI) and orange II from aqueous solution using magnetic polyetherimide/sugarcane bagasse

  • Hejun GaoEmail author
  • Jia Du
  • Yunwen Liao
Original Research
  • 19 Downloads

Abstract

A novel biological magnetic adsorbent was successfully constituted with sugarcane bagasse (SCB), polyetherimide (PEI) and Fe3O4. The physicochemical properties of the adsorbent (Fe3O4@PEI/SCB) were investigated by SEM, BET, VSM, XRD, TGA, FT-IR, XPS, TEM and UV–Vis. The adsorption capacity was measured using Cr(VI) and orange II as adsorbates. The effects of initial pH, dosage, contact time, and ionic strength on the adsorption capacity were investigated in detail. Fe3O4@PEI/SCB is a mesoporous material and the mass ratio of Fe3O4:PEI:SCB is about 5:2:15. Adsorption capacity could reach 182.28 mg/g and 1893.57 mg/g for Cr(VI) and orange II at room temperature, respectively. Fe3O4@PEI/SCB is a green and economical material, which is very easily regenerated, reused, and separated in the adsorption. The most important factor is the ionic strength and major adsorption interaction was electrostatic in this work.

Graphical abstract

Keywords

Sugarcane bagasse Magnetic Adsorption Chromium(VI) Dye 

Notes

Acknowledgments

This work was supported by the Applied Basic Research Programs of Science and Technology Department of Sichuan Province, China (2015JY0042, 2018JY0115), the Key Fund Project of Education Department of Sichuan Province, China (15ZA0147), the Fundamental Research Funds of China West Normal University, China (14E015), and supported by the Meritocracy Research Funds of China West Normal University (17YC013).

Supplementary material

10570_2019_2301_MOESM1_ESM.docx (1.5 mb)
Supplementary material 1 (DOCX 1535 kb)

References

  1. Avila M, Burks T, Akhtar F et al (2014) Surface functionalized nanofibers for the removal of chromium(vi) from aqueous solutions. Chem Eng J 245:201–209Google Scholar
  2. Baio JE, Weidner T, Brison J et al (2009) Amine terminated sams: investigating why oxygen is present in these films. J Electron Spectrosc 172(1–3):2–8Google Scholar
  3. Bedin KC, Martins AC, Cazetta AL et al (2016) KOH-activated carbon prepared from sucrose spherical carbon: adsorption equilibrium, kinetic and thermodynamic studies for Methylene Blue removal. Chem Eng J 286:476–484Google Scholar
  4. Beheshti H, Irani M, Hosseini L et al (2016) Removal of Cr(VI) from aqueous solutions using chitosan/MWCNT/Fe3O4 composite nanofibers-batch and column studies. Chem Eng J 284:557–564Google Scholar
  5. Chakraborty S, Chowdhury S, Saha PD (2012) Batch removal of crystal violet from aqueous solution by H2SO4 modified sugarcane bagasse: equilibrium, kinetic, and thermodynamic profile. Sep Sci Technol 47(13):1898–1905Google Scholar
  6. Chen J, Yan LG, Yu HQ et al (2016) Efficient removal of phosphate by facile prepared magnetic diatomite and illite clay from aqueous solution. Chem Eng J 287:162–172Google Scholar
  7. Erdem E, Karapinar N, Donat R (2004) The removal of heavy metal cations by natural zeolites. J Colloid Interface Sci 280(2):309–314Google Scholar
  8. Fan J, Zhang J, Zhang C et al (2011) Adsorption of 2,4,6-trichlorophenol from aqueous solution onto activated carbon derived from loosestrife. Desalination 267(2–3):139–146Google Scholar
  9. Fu F, Wang Q (2011) Removal of heavy metal ions from wastewaters: a review. J Environ Manag 92(3):407–418Google Scholar
  10. Gao H, Wang Y, Zheng L (2013a) Hydroxyl-functionalized ionic liquid-based cross-linked polymer as highly efficient adsorbent for anionic azo dyes removal. Chem Eng J 234:372–379Google Scholar
  11. Gao H, Zhao S, Cheng X et al (2013b) Removal of anionic azo dyes from aqueous solution using magnetic polymer multi-wall carbon nanotube nanocomposite as adsorbent. Chem Eng J 223:84–90Google Scholar
  12. Gao H, Wang Y, Zheng L (2014) Removing Cr(VI) from aqueous solutions using a functional ionic liquid-based cross-linked polymer. J Environ Manag 137:81–85Google Scholar
  13. Garg UK, Kaur MP, Sud D et al (2009) Removal of hexavalent chromium from aqueous solution by adsorption on treated sugarcane bagasse using response surface methodological approach. Desalination 249(2):475–479Google Scholar
  14. Gu C, Jia H, Li H et al (2010) Synthesis of highly reactive subnano-sized zero-valent iron using smectite clay templates. Environ Sci Technol 44(11):4258–4263Google Scholar
  15. Homagai PL, Ghimire KN, Inoue K (2010) Adsorption behavior of heavy metals onto chemically modified sugarcane bagasse. Bioresour Technol 101(6):2067–2069Google Scholar
  16. Hozhabr Araghi S, Entezari MH, Chamsaz M (2015) Modification of mesoporous silica magnetite nanoparticles by 3-aminopropyltriethoxysilane for the removal of Cr(VI) from aqueous solution. Microporous Mesoporous Mater 218:101–111Google Scholar
  17. Ip AWM, Barford JP, McKay G (2009) Reactive Black dye dsorption/desorption onto different adsorbents: effect of salt, surface chemistry, pore size and surface area. J Colloid Interface Sci 337(1):32–38Google Scholar
  18. Jiang W, Cai Q, Xu W et al (2014) Cr(VI) adsorption and reduction by humic acid coated on magnetite. Environ Sci Technol 48(14):8078–8085Google Scholar
  19. Kalderis D, Bethanis S, Paraskeva P et al (2008) Production of activated carbon from bagasse and rice husk by a single-stage chemical activation method at low retention times. Bioresour Technol 99(15):6809–6816Google Scholar
  20. Khan TA, Chaudhry SA, Ali I (2015) Equilibrium uptake, isotherm and kinetic studies of Cd(II) adsorption onto iron oxide activated red mud from aqueous solution. J Mol Liq 202:165–175Google Scholar
  21. Khoo EC, Ong ST, Ha ST (2012) Removal of basic dyes from aqueous environment in single and binary systems by sugarcane bagasse in a fixed-bed column. Desalin Water Treat 37(1–3):215–222Google Scholar
  22. Li Y, Sun J, Du Q et al (2014) Mechanical and dye adsorption properties of graphene oxide/chitosan composite fibers prepared by wet spinning. Carbohyd Polym 102:755–761Google Scholar
  23. Liou TH (2004) Evolution of chemistry and morphology during the carbonization and combustion of rice husk. Carbon 42(4):785–794Google Scholar
  24. Ma J, Yu F, Zhou L et al (2012) Enhanced adsorptive removal of methyl orange and methylene blue from aqueous solution by alkali-activated multiwalled carbon nanotubes. ACS Appl Mater Interfaces 4(11):5749–5760Google Scholar
  25. Ma S, Zhan S, Jia Y et al (2015) Superior antibacterial activity of Fe3O4–TiO2 nanosheets under solar light. ACS Appl Mater Interfaces 7(39):21875–21883Google Scholar
  26. Manikandan A, Vijaya JJ, Mary JA et al (2014) Structural, optical and magnetic properties of Fe3O4 nanoparticles prepared by a facile microwave combustion method. J Ind Eng Chem 20(4):2077–2085Google Scholar
  27. Noreen S, Bhatti HN (2014) Fitting of equilibrium and kinetic data for the removal of Novacron Orange P-2R by sugarcane bagasse. J Ind Eng Chem 20(4):1684–1692Google Scholar
  28. Pan Y, Wang J, Sun C et al (2016) Fabrication of highly hydrophobic organic–inorganic hybrid magnetic polysulfone microcapsules: a lab-scale feasibility study for removal of oil and organic dyes from environmental aqueous samples. J Hazard Mater 309:65–76Google Scholar
  29. Paul ML, Samuel J, Das SB et al (2012) Studies on Cr(VI) removal from aqueous solutions by nanoalumina. Ind Eng Chem Res 51(46):15242–15250Google Scholar
  30. Peng S, Meng H, Ouyang Y et al (2014) Nanoporous magnetic cellulose–chitosan composite microspheres: preparation, characterization, and application for Cu(II) adsorption. Ind Eng Chem Res 53:2106–2113Google Scholar
  31. Pereira MFR, Soares SF, Órfão JJM et al (2003) Adsorption of dyes on activated carbons: influence of surface chemical groups. Carbon 41(4):811–821Google Scholar
  32. Poursaberi T, Hassanisadi M (2013) Magnetic removal of reactive black 5 from wastewater using ionic liquid grafted-magnetic nanoparticles. Clean Soil Air Water 41(12):1208–1215Google Scholar
  33. Qi W, Zhao Y, Zheng X et al (2016) Adsorption behavior and mechanism of Cr(VI) using Sakura waste from aqueous solution. Appl Surf Sci 360:470–476Google Scholar
  34. Rengaraj S, Kim Y, Joo CK et al (2004) Removal of copper from aqueous solution by aminated and protonated mesoporous aluminas: kinetics and equilibrium. J Colloid Interface Sci 273(1):14–21Google Scholar
  35. Sargın İ, Kaya M, Arslan G et al (2015) Preparation and characterisation of biodegradable pollen–chitosan microcapsules and its application in heavy metal removal. Bioresour Technol 177:1–7Google Scholar
  36. Shard AG, Whittle JD, Beck AJ et al (2004) A NEXAFS examination of unsaturation in plasma polymers of allylamine and propylamine. J Phys Chem B 108(33):12472–12480Google Scholar
  37. Shen W, Mu Y, Xiao T et al (2016) Magnetic Fe3O4–FeB nanocomposites with promoted Cr(VI) removal performance. Chem Eng J 285:57–68Google Scholar
  38. Song M, Xu J (2013) Preparation of polyethylenimine-functionalized graphene oxide composite and its application in electrochemical ammonia sensors. Electroanal 25(2):523–530Google Scholar
  39. Terlingen JGA, Feijen J, Hoffman AS (1993) Immobilization of surface active compounds on polymer supports using glow discharge processes: 1. Sodium dodecyl sulfate on poly(propylene). J Colloid Interface Sci 155(1):55–65Google Scholar
  40. Uslu G, Tanyol M (2006) Equilibrium and thermodynamic parameters of single and binary mixture biosorption of lead (II) and copper (II) ions onto Pseudomonas putida: effect of temperature. J Hazard Mater 135(1–3):87–93Google Scholar
  41. Wang Y, Zou B, Gao T et al (2012) Synthesis of orange-like Fe3O4/PPy composite microspheres and their excellent Cr(VI) ion removal properties. J Mater Chem 22:9034–9040Google Scholar
  42. Wang J, Pan K, He Q et al (2013) Polyacrylonitrile/polypyrrole core/shell nanofiber mat for the removal of hexavalent chromium from aqueous solution. J Hazard Mater 244:121–129Google Scholar
  43. Wang H, Yuan X, Wu Y et al (2015) Facile synthesis of polypyrrole decorated reduced graphene oxide–Fe3O4 magnetic composites and its application for the Cr(VI) removal. Chem Eng J 262:597–606Google Scholar
  44. Weng CH, Lin YT, Hong DY et al (2014) Effective removal of copper ions from aqueous solution using base treated black tea waste. Ecol Eng 67:127–133Google Scholar
  45. Wu Y, Zhang M, Zhao H et al (2014) Functionalized mesoporous silica material and anionic dye adsorption: MCM-41 incorporated with amine groups for competitive adsorption of Acid Fuchsine and Acid Orange II. RSC Adv 4(106):61256–61267Google Scholar
  46. Xu Q, Sardon H, Chan JMW et al (2015) Polyurethane-coated silica particles with broad-spectrum antibacterial properties. Polym Chem 6(11):2011–2022Google Scholar
  47. Yang J, Chen H, Gao J et al (2016) Synthesis of Fe3O4/g-C3N4 nanocomposites and their application in the photodegradation of 2,4,6-trichlorophenol under visible light. Mater Lett 164:183–189Google Scholar
  48. Yu JX, Wang LY, Chi RA et al (2013) Competitive adsorption of Pb2+ and Cd2+ on magnetic modified sugarcane bagasse prepared by two simple steps. Appl Surf Sci 268:163–170Google Scholar
  49. Zhang L, Chen L, Liu X et al (2015) Effective removal of azo-dye orange II from aqueous solution by zirconium-based chitosan microcomposite adsorbent. RSC Adv 5(114):93840–93849Google Scholar
  50. Zhong QQ, Yue QY, Li Q et al (2014) Removal of Cu(II) and Cr(VI) from wastewater by an amphoteric sorbent based on cellulose-rich biomass. Carbohyd Polym 111:788–796Google Scholar

Copyright information

© Springer Nature B.V. 2019

Authors and Affiliations

  1. 1.Chemical Synthesis and Pollution Control Key Laboratory of Sichuan ProvinceChina West Normal UniversityNanchongChina
  2. 2.Institute of Applied ChemistryChina West Normal UniversityNanchongChina

Personalised recommendations