Hydrolysis of cellulose to glucose by supercritical water and silver mesoporous zeolite catalysts

  • S. G. Aspromonte
  • A. Romero
  • A. V. Boix
  • E. Alonso
Original Research
  • 18 Downloads

Abstract

The hydrolysis of cellulose into glucose is a critical step for the conversion of lignocellulosic biomass into fuels and chemical products. The combination of supercritical water hydrolysis in ultrafast reactors, with the subsequent hydrolysis of the cello-oligosaccharides on silver-exchanged mesoporous mordenite zeolite, offers the possibility of a clear enhancement in the conversion of cellulose and in glucose formation. Complete dissolution of cellulose is achieved in the supercritical step and 81.8% of formed oligosaccharides are hydrolyzed in the catalytic step, with a yield into glucose of 77.0%. A fraction of Al is octahedrally coordinated, indicating a distribution of acid sites after the silver exchange. A deactivation of the catalyst between the first and third reaction cycle is observed, with a reduction in hydrolyzed carbon from 81.8% up to 45.6%. However, the selectivity to glucose only varies from 94.1 to 81.8%. Afterwards, the activity remains constant up to the fifth cycle. The presence of Ag(0) particles, together with the formation of coke, are responsible for the partial blockage of the pores of the support and loss of catalytic activity.

Graphical abstract

Keywords

Hydrolysis of cellulose Mordenite Glucose Biomass Silver Mesoporous zeolite 

Notes

Acknowledgments

This work was supported by Spanish Government through the Research Project CTQ2015-64892-R (MINECO/FEDER) and ANPCyT (PICT 2014-2445) and CONICET (PIP 11220090100190, PIP 11220130100062). The authors also acknowledge the financial support received from UNL. They are grateful to ANPCyT for the purchase of the SPECS multi-technique analysis instrument (PME8-2003). Thanks are given to Fernanda Mori and Magali Borne for the XPS and NMR measurements, respectively.

References

  1. Abdelrasoul A, Zhang H, Cheng CH, Doan H (2017) Applications of molecular simulations for separations and adsorption in zeolites. Microporous Mesoporous Mater 242:294–348CrossRefGoogle Scholar
  2. Amama PB, Pint CL, Kim SM, McJilton L, Eyinc KG, Stach EA, Hauge RH, Maruyama B (2010) Influence of alumina type on the evolution and activity of alumina-supported Fe catalysts in single-walled carbón nanotube carpet growth. ACS Nano 4:895–904CrossRefGoogle Scholar
  3. Aspromonte SG, Miró EE, Boix AV (2012a) Effecy of Ag–Co interactions in the mordenite on the NOx SCR with butane and toluene. Catal Commun 28:105–110CrossRefGoogle Scholar
  4. Aspromonte SG, Miró EE, Boix AV (2012b) FTIR studies of butane, toluene and nitric oxide adsorption on Ag exchanged NaMordenite. Adsorption 18:1–12CrossRefGoogle Scholar
  5. Aspromonte SG, Mizrahi MD, Schneeberger FA, Ramallo-López JM, Boix AV (2013) Study of the nature and location of silver in Ag-exchanged mordenite catalysts. Characterization by spectroscopic techniques. J Phys Chem C 117:25433–25442CrossRefGoogle Scholar
  6. Aspromonte SG, Mizrahi MD, Alonso E, Ramallo-López JM, Boix AV (2017) Co/MCM41 catalyst in the COProx reaction prepared by supercritical CO2 reactive deposition. Microporous Mesoporous Mater 239:147–157CrossRefGoogle Scholar
  7. Ausavasukhi A, Suwannaran S, Limtrakul J, Sooknoi T (2008) Reversible interconversion behavior of Ag species in AgHZSM-5:XRD, 1H MAS NMR, TPR, TPHE, and catalytic studies. Appl Catal A: Gen 345:89–96CrossRefGoogle Scholar
  8. Benaliouche F, Boucheffa Y, Ayrault P, Mignard S (2008) NH3-TPD and FTIR spectroscopy of pyridine adsorption studies for characterization of Ag- and Cu-exchanged X zeolites. Microporous Mesoporous Mater 111:80–88CrossRefGoogle Scholar
  9. Boix AV, Miró EE, Lombardo EA, Fierro JLG (2008) The inhibiting effect of extra-framework Al on monolithic Co-ZSM5 catalysts used for NOx SCR. Catal Today 133–135:428–434CrossRefGoogle Scholar
  10. Brunauer S, Emmett PH, Teller E (1938) Adsorption of gases in multimolecular layers. JACS 60:309–319CrossRefGoogle Scholar
  11. Cai HL, Li CZ, Wang AQ, Xu GL, Zhang T (2012) Zeolite-promoted hydrolysis of cellulose in ionic liquid, insight into the mutual behavior of zeolite, cellulose and ionic liquid. Appl Catal B: Environ 123–124:333–338CrossRefGoogle Scholar
  12. Cantero D, Bermejo M, Cocero M (2013) High glucose selectivity in pressurized water hydrolysis of cellulose using ultra-fasr reactor. Bioresour Technol 135:697–703CrossRefGoogle Scholar
  13. Cantero DA, Sánchez Tapia Á, Bermejo MD (2015a) Pressure and temperatura effect on cellulose hydrolysos in pressurized water. Chem Eng J 276:145–154CrossRefGoogle Scholar
  14. Cantero DA, Vaquerizo L, Mato F, Bermejo MD, Cocero MJ (2015b) Energetic approach of biomass hydrolysis in supercritical water. Bioresour Technol 179:136–143CrossRefGoogle Scholar
  15. Cejka J, Corma A, Zones S (2010) Zeolites and catalysis: synthesis, reactions and applications. Wiley-VCH, WeinheimCrossRefGoogle Scholar
  16. Chheda JN, Huber GW, Dumesic JA (2007) Liquid-phase catalytic processing of biomass-derived oxygenated hydrocarbons to fuels and chemicals. Angew Chem Int Ed 46:7164–7183CrossRefGoogle Scholar
  17. Chimentao RJ, Lorente E, Gispert-Guirado F, Medina F, López F (2014) Hydrolysis of dilute acid-pretreated cellulose under mild hydrothermal conditions. Carbohydr Polym 111:116–124CrossRefGoogle Scholar
  18. Cho HJ, Dornath P, Fan W (2014) Synthesis of hierarchical Sn-MFI as Lewis acid catalysts for isomerization of cellulosic sugars. ACS Catal 4:2029–2037CrossRefGoogle Scholar
  19. do Couto Fraga A, Bittencourt Quitete CP, Ximenes VL, Falabella Sousa-Aguiar E, Botelho Rego M (2016) Biomass derived solid acids as effective hydrolysis catalysts. J Mol Catal A: Chem 422:248–257CrossRefGoogle Scholar
  20. Fang Z, Zhang F, Zeng HY, Guo F (2011) Production of glucose by hydrolysis of cellulose at 423 K in the presence of activated hydrotalcite nanoparticles. Bioresour Technol 102:8017–8021CrossRefGoogle Scholar
  21. Gardner DW, Huo J, Hoff TC, Johnson RL, Shanks BH, Tessonnier JP (2015) Insights into the hydrothermal stability of ZSM-5 under relevant biomass conversion reaction conditions. ACS Catal 5:4418–4422CrossRefGoogle Scholar
  22. Hu L, Lin L, Wu Z, Zhou S, Liu S (2015) Chemocatalytic hydrolysis of cellulose into glucose over solid acid catalysts. Appl Catal B: Environ 174–175:225–243CrossRefGoogle Scholar
  23. Inumaru K, Ishihara T, Kamiya Y, Okuhara T, Yamanaka S (2007) Water-tolerant, highly active solid acid catalysts composed of the kegging-type polyoxometalate H3PW12O40 immobilized in hydrophobic nanospaces of organomodified mesoporous silica. Angew Chem Int Ed 46:7625–7628CrossRefGoogle Scholar
  24. Kobayashi H, Komanoya T, Hara K, Fukuoka A (2010) Water-tolerant mesoporous-carbon-supported ruthenium catalysts for the hydrolysis of cellulose to glucose. Chemsuschem 3:440–443CrossRefGoogle Scholar
  25. Meynen V, Cool P, Vansant EF (2009) Verified syntheses of mesoporous materials. Microporous Mesoporous Mater 125:170–223CrossRefGoogle Scholar
  26. Mignoni ML, Petkowicz DI, Fernandez Machado NRC, Pergher SBC (2008) Synthesis of mordenite using kaolin as Si and Al source. Appl Clay Sci 41:99–104CrossRefGoogle Scholar
  27. Morales-de la Rosa S, Campos-Martin JM, Fierro JLG (2018) Chemical hydrolysis of cellulose into fermentable sugars through ionic liquids and antisolvent pretreatments using heterogeneous catalysts. Catal Today 302:87–93CrossRefGoogle Scholar
  28. Pang J, Wang A, Zheng M, Zhang T (2010) Hydrolysis of cellulose into glucose over carbons sulfonated at elevated temperatures. Chem Commun 46:6935–6937CrossRefGoogle Scholar
  29. Ravenelle RM, Diallo FZ, Crittenden JC, Sievers C (2012) Effects of metal precursors on the stability and observed reactivity of Pt/γ-Al2O3 catalysts in aqueous phase reactions. Chem Cat Chem 4:492–494Google Scholar
  30. Saha B, Abu-Omar MM (2014) Advances in 5-hydroxymethylfurfural production from biomass in biphasic solvents. Green Chem 16:24–38CrossRefGoogle Scholar
  31. Sales EA, Benhamida B, Caizergues V, Lagier J-P, Fiévet F, Bozon-Verduraz F (1998) Alumina-supported Pd, Ag and Pd–Ag catalysts: preparation through the polyol process, characterization and reactivity in hexa-1,5-diene hydrogentation. Appl Catal A: Gen 172:273–283CrossRefGoogle Scholar
  32. Song S, Di L, Wu G, Dai W, Guan N, Li L (2017) Meso-Zr-Al-beta zeolite as a robust catalyst for cascade reactions in biomass valorization. Appl Catal B: Environ 205:393–403CrossRefGoogle Scholar
  33. Stepanov AG (2016) Basics of solid-state NMR for application in zeolite science. In: Sels B, Kustov L (eds) Zeolites and zeolite-like materials, 1st edn. Elsevier, Amsterdam, pp 137–188Google Scholar
  34. Suganuma S, Nakajima K, Kitano M, Yagamuchi D, Kato H, Hayashi S, Hara M (2008) Hydrolysis of cellulose by amorphous carbon bearing SO3H, COOH, and OH groups. J Am Chem Soc 130:12787–12793CrossRefGoogle Scholar
  35. Tian J, Wang J, Zhao S, Jiang C, Zhang X, Wang X (2010) Hydrolysis of cellulose by the heteropoly acid H3PW12O40. Cellulose 17:587–594CrossRefGoogle Scholar
  36. Waterhouse GIN, Metson JB, Bowmaker GA (2007) Synthesis, vibrational spectra and thermal stability of Ag3O4 and related Ag7O8X salts. Polyhedron 26:3310–3322CrossRefGoogle Scholar
  37. Westermann A, Azambre B, Koch A (2012) Effect of Ag, Pd and Co promoters on the Selective Catalytic Reduction (SCR) of NOx by ethanol over sulfated ceria-zirconia catalysts. Catal Today 19:65–74CrossRefGoogle Scholar
  38. Yamaguchi D, Kitano M, Suganuma S, Nakajima K, Kato H, Hara M (2009) Hydrolysis of cellulose by a solid acid catalyst under optimal reaction conditions. J Phys Chem C 113:3181–3188CrossRefGoogle Scholar
  39. Zapata PA, Faria J, Ruiz MP, Jentoft RE, Resasco DE (2012) Hydrophobic zeolites for biofuel upgrading reactions at the liquid–liquid interface in water/oil emulsions. J Am Chem Soc 134:8570–8578CrossRefGoogle Scholar
  40. Zhang Z, Zhao ZK (2009) Solid acid and microwave-assisted hydrolysis of cellulose in ionic liquid. Carbohydr Res 344:2069–2072CrossRefGoogle Scholar

Copyright information

© Springer Nature B.V. 2019

Authors and Affiliations

  1. 1.Instituto de Investigaciones en Catálisis y Petroquímica – INCAPE (FIQ, UNL-CONICET)Santa FeArgentina
  2. 2.High Pressure Processes Group –Chemical Engineering and Environmental Technology Dpt.Universidad de ValladolidValladolidSpain

Personalised recommendations