Antibacterial finishing of cotton fabrics based on thiol-maleimide click chemistry
- 55 Downloads
Cotton fabrics with durable antibacterial properties were prepared by a novel method of thiol-maleimide click reaction. Firstly, 3-Mercaptopropyltriethoxysilane was utilized as a modifier to generate thiol groups on the cotton surface. Then, these thiol groups reacted with N-phenyl-male-imide through thiol-maleimide click chemistry. The surface morphology of the treated fabrics and the reaction mechanism were characterized by FT-IR, Raman, EDS, XPS and SEM. Antibacterial activities, mechanical properties and thermal performance of treated cotton fabrics were also investigated. The Escherichia coli antibacterial rate of treated cotton was 99.56% and the Staphylococcus aureus antibacterial rate of treated cotton was 98.91%, with only a slight decrease after 10 cycles of standard washing, to 88.69 and 87.66%, respectively. These results demonstrated that this treatment effectively endowed cotton fabrics with durable antibacterial properties due to the chemical bonding formed between the antibacterial agent and the substrate. In addition, the treated cotton fabrics maintained good mechanical properties and thermal stability.
KeywordsAntibacterial agent N-phenyl-male-imide Cotton fabrics Thiol-maleimide click chemistry
The research was supported by the Fundamental Research Funds for the Central Universities (No. 16D110518) and National Natural Science Foundation of China (No. 51403032).
- Csw B, Al-Azzawi AM, Mahdi SAR et al (2013) Synthesis and evaluation of antimicrobial activity of several new maleimides to benzothiazole moiety. Baghdad Sci J 10:658–672Google Scholar
- Li Y, Li W, Qian Z, Zhang L, Dong L, Wang L, Tang S (2017) Synthesis of N-phenylmaleimide/styrene/alpha methyl styrene/maleic anhydride tetrapolymers and its modification to ABS resin. Polym Mater Sci Eng 33:1–6. https://doi.org/10.16865/j.cnki.1000-7555.2017.06.001
- Singh D, Chauhan NPS, Mozafari M, Hiran BL (2016) High-temperature resistive free radically synthesized chloro-substituted phenyl maleimide antimicrobial polymers. J Macromol Sci Part D—Rev Polym Process 55:1916–1939Google Scholar
- Wang Y, Wang W, Liu B, Yu D (2017) Preparation of durable antibacterial and electrically conductive polyacrylonitrile fibers by copper sulfide coating. J Appl Polym Sci 134:45496. https://doi.org/10.1002/app.45496