Esterified cellulose nanocrystals as reinforcement in poly(lactic acid) nanocomposites
- 81 Downloads
Biopolymers are of huge interest as they carry potential to minimize the environmental hazards caused by synthetic materials. Poly(lactic acid) (PLA) reinforced by cellulose nanocrystals (CNCs) has shown promising results. To obtain the optimum characteristics of PLA-CNC nanocomposites, a superior compatibility between PLA and CNCs is paramount. The application of chemical surface modification technique is an essential step to improve the interaction between hydrophilic CNCs and hydrophobic PLA. In this study, a time-efficient esterification technique using valeric acid was introduced to improve the compatibility between CNCs and PLA. Masterbatches were prepared using spin-coating method to ensure the maximum dispersion of CNCs through PLA and to decrease the drying time. Nanocomposites were prepared using extrusion and injection molding. The degree of substitution for modified CNCs was calculated as 0.35. Transmission electron microscopy exhibited esterified CNCs (e-CNCs) in the nanoscale with rod shape structure. Thermal stability improved by 15% in nanocomposites containing 3% e-CNCs, whereas untreated CNCs didn’t alter the thermal stability to a notable extent. A substantial increase of 200% was observed in crystallinity of nanocomposites reinforced with 3% e-CNCs. The incorporation of CNCs into PLA resulted in an increase in storage modulus and a decrease in tan δ intensity which was more profound in PLA-e-CNCs. The tensile strength of PLA-e-CNCs composites was found to be superior to composites reinforced with untreated CNCs. The results confirmed that a combination of time-efficient esterification and spin-coated masterbatch was a successful approach to uniformly disperse CNCs in PLA matrix.
KeywordsPoly(lactic acid) Cellulose nanocrystals Esterification Masterbatch Mechanical properties Thermal properties
The authors would like to acknowledge funding from the NSF- EPSCoR (Grant No. 11A1355466) for supporting this work.
- ASTM D (2008) 638-03: standard test method for tensile properties of plastics current edition approved Apr 1:1–16Google Scholar
- Dong L-L, He L, Tao G-H, Hu C (2013) High yield of ethyl valerate from the esterification of renewable valeric acid catalyzed by amino acid ionic liquids RSC. Advances 3:4806–4813Google Scholar
- Halász K, Csóka L (2013) Plasticized biodegradable poly (lactic acid) based composites containing cellulose in micro-and nanosize. J Eng. https://doi.org/10.1155/2013/329379
- Organization WH (1997) Evaluations of the Joint FAO/WHO Expert Commitee on Food Additives (JECFA). Accessed 16 Feb 2018Google Scholar
- Parit M (2016) Thermoplastic polymer nanocomposites. Master thesis, Chemical Eng Dept, Auburn University, Auburn, Alabama, United StatesGoogle Scholar
- Paula EL, Mano V, Duek EAR, Pereira FV (2015) Hydrolytic degradation behavior of PLLA nanocomposites reinforced with modified cellulose nanocrystals. Quim Nova 38:1014–1020Google Scholar
- Poletto M, Pistor V, Zattera AJ (2013) Structural characteristics and thermal properties of native cellulose. In: Van De Ven TGM (ed) Cellulose-fundamental aspects. InTechGoogle Scholar
- Rosilo H, Kontturi E, Seitsonen J, Kolehmainen E, Ikkala O (2013) Transition to reinforced state by percolating domains of intercalated brush-modified cellulose nanocrystals and poly (butadiene) in cross-linked composites based on thiol–ene click chemistry. Biomacromol 14:1547–1554CrossRefGoogle Scholar