Highly hydrophilic and anti-fouling cellulose thin film composite membrane based on the hierarchical poly(vinyl alcohol-co-ethylene) nanofiber substrate
- 492 Downloads
Thin film composite (TFC) membrane is one of the most promising technologies in the purification field. In this study, a novel highly hydrophilic and anti-fouling cellulose TFC membrane was prepared based on the hierarchical poly(vinyl alcohol-co-ethylene) (PVA-co-PE) nanofiber substrate. The morphology and hydrophilicity of the hierarchical PVA-co-PE nanofiber substrate and the cellulose TFC membrane were analyzed by SEM, FESEM, and contact angle goniometry. To optimize the performance of cellulose TFC membrane, the effects of coagulation bath, cellulose concentration and thickness of cellulose layer on the filtration efficiency, water flux as well as the mechanical property were studied. The anti-fouling property of the cellulose TFC membrane was analyzed by testing the change in the flux of membrane during repeated bovine serum albumin (BSA) filtrating and fouling process. The results show that the filtration efficiency of cellulose TFC membrane to BSA with the diameter of 2–10 nm could be above 97 %. Due to the hydrophilicity of the top cellulose layer, the cellulose TFC membrane exhibits excellent anti-fouling property by showing the 100 % flux recovery ratio.
KeywordsCellulose Thin film composite membrane Hydrophilicity Anti-fouling Hierarchical PVA-co-PE nanofiber substrate
The authors were thankful to the financial support of National Nature Science Foundation (51403166, 51473129 and 51273152), “863’’ Special Project on Functional Nanomaterials (2013AA031802), Nature Science Foundation of Hubei Province (2014CFB759) and Program for New Century Excellent Talents in University (NCET-12-0711).
- Cadotte JE, Cobian KE, Forester RH, Petersen RJ (1976) Continued evaluation of in situ-formed condensation polymers for reverse osmosis membranes. Office of Water Research and technology, Washington, DC, NTIS Report No. PB-253193, NTIS Issue No. 197616Google Scholar
- Cadotte JE, Steuck MJ, Petersen RJ (1978) Research on in situ-formed condensation polymer for reverse osmosis membranes. Office of Water Research and technology, Washington, DC, NTIS Report No. PB-288387, NTIS Issue No. 197905Google Scholar