Effect of Formic Acid Treatment on the Structure and Catalytic Activity of Co3O4 for N2O Decomposition

  • Yongzhao WangEmail author
  • Xuhui Wei
  • Xiaobo Hu
  • Wei Zhou
  • Yongxiang ZhaoEmail author
Article
  • 1 Downloads

Abstract

Co3O4 catalyst was prepared by means of precipitation method and its precursor was treated with formic acid to prepare H-Co3O4 catalyst. Their catalytic activities for N2O catalytic decomposition were studied. The results show that H-Co3O4 catalyst exhibits much higher catalytic activity than Co3O4, which may result from the larger BET surface area, especially the more amount of surface Co3+, enhanced reducibility and promoted desorption ability of oxygen species.

Graphical Abstract

Keywords

Co3O4 N2O catalytic decomposition Formic acid treatment Precipitation method 

Notes

Acknowledgements

Authors gratefully acknowledge the financial support from Shanxi provincial key research and development plan project (201603D121018-1); the National Natural Science Foundation of China (21673132); and the Key Laboratory of Applied Surface and Colloid Chemistry (Shaanxi Normal University 2016019).

Compliance with Ethical Standards

Conflict of interest

The authors declare no conflict of interests.

References

  1. 1.
    Strokal M, Kroeze C (2014) Curr Opin Environ Sustain 9:108–121Google Scholar
  2. 2.
    Kapteijn F, Rodriguez-Mirasol J, Moulijn JA (1996) Appl Catal B 9:25–64Google Scholar
  3. 3.
    Lykaki M, Papista E, Sónia ACC, Tavares PB, Konsolakis M (2018) Catal Sci Technol 8:2312–2322Google Scholar
  4. 4.
    Centi G, Galli A, Montanari B, Perathoner S, Vaccari A (1997) Catal Today 35:113–120Google Scholar
  5. 5.
    Sadovska G, Tabor E, Bernauer M, Sazama P, Fila V, Kmječ T, Kohout J, Zaveta K, Tokarova V, Sobalík Z (2018) Catal Sci Technol 8:2841–2852Google Scholar
  6. 6.
    Jirátová K, Balabánová J, Kovanda F, Klegová A, Obalová L, Fajgar R (2017) Catal Lett 147:1–13Google Scholar
  7. 7.
    Ma Z, Ren Y, Lu Y, Bruce PG (2013) J Nanosci Nanotechnol 13:5093–5103Google Scholar
  8. 8.
    Komvokis VG, Marti M, Delimitis A, Vasalos LA, Triantafyllidis KS (2011) Appl Catal B 103:62–71Google Scholar
  9. 9.
    Kim SS, Choi SH, Lee SM, Hong SC (2012) J Ind Eng Chem 18:1263–1266Google Scholar
  10. 10.
    Ren Y, Ma Z, Bruce PG (2011) Cryst Eng Commun 13:6955–6959Google Scholar
  11. 11.
    Xue L, He H, Liu C, Zhang C, Zhang B (2009) Environ Sci Technol 43:890–895Google Scholar
  12. 12.
    Chromčáková Z, Obalová L, Kovanda F, Legut D, Titov A, Ritz M, Fridrichová D, Michalik S, Kuśtrowski P, Jirátová K (2015) Catal Today 257:18–25Google Scholar
  13. 13.
    Zou W, Xie PF, Hua WM, Wang YD, Kong DJ, Yue YH, Ma Z, Yang WM, Gao Z (2014) J Mol Catal A 394:83–88Google Scholar
  14. 14.
    Zhang X, Shen Q, He C, Ma C, Cheng J, Liu Z, Hao Z (2012) Catal Sci Technol 2:1249–1258Google Scholar
  15. 15.
    Konsolakis M (2015) ACS Catal 5:6397–6421Google Scholar
  16. 16.
    Asano K, Ohnishi C, Iwamoto S, Shioya Y, Inoue M (2008) Appl Catal B 78:242–249Google Scholar
  17. 17.
    Ohnishi C, Asano K, Iwamoto S, Chikama K, Inoue M (2007) Catal Today 120:145–150Google Scholar
  18. 18.
    Yu HB, Wang XP, Wu XX, Chen Y (2018) Chem Eng J 334:800–806Google Scholar
  19. 19.
    Yu HB, Tursun M, Wang XP, Wu XX (2016) Appl Catal B 185:110–118Google Scholar
  20. 20.
    You YC, Chang HZ, Ma L, Guo L, Qin X, Li JY, Li JH (2018) Chem Eng J 347:184–192Google Scholar
  21. 21.
    Wang YZ, Hu XB, Zheng K, Wei XH, Zhao YX (2018) Catal Commun 111:70–74Google Scholar
  22. 22.
    Stelmachowski P, Ciura K, Grzybek G (2016) Catal Sci Technol 6:14Google Scholar
  23. 23.
    Wang YZ, Hu XB, Zheng K, Zhang H, Zhao YX (2018) React Kinet Mech Cat 123:707–721Google Scholar
  24. 24.
    Zhang QL, Tang XS, Ning P, Duan YK, Song ZX, Shi YZ (2015) RSC Adv 5:51263–51270Google Scholar
  25. 25.
    Hadjiev VG, Iliev MN, Vergilov IV (1988) J Phys C 21:199–201Google Scholar
  26. 26.
    Zuo J, Xu C, Liu Y, Qian Y (1998) Nanostruct Mater 10:1331–1335Google Scholar
  27. 27.
    Lorite I, Romero JJ, Fernández JF (2012) J Raman Spectrosc 43:1443–1448Google Scholar
  28. 28.
    Lopes I, Hassan NE, Guerba H, Wallez G, Davidson A (2006) Chem Mater 18:5826–5828Google Scholar
  29. 29.
    Petersen AP, Forbes RP, Govender S, Kooyman PJ, Steen EV (2018) Catal Lett 148:1215–1227Google Scholar
  30. 30.
    Pritchard J, Morris L, Walsh D, Sadasivan S, Ménard H (2017) Catal Lett 23:1–11Google Scholar
  31. 31.
    Zhang C, Zhang ZP, Sui C, Yuan FL, Niu XY, Zhu YJ (2016) ChemCatChem 8:2155–2164Google Scholar
  32. 32.
    Słoczyński J, Janas J, Machej T, Rynkowski J, Stoch J (2000) Appl Catal B 24:45–60Google Scholar
  33. 33.
    Chen JH, Shi WB, Li JH (2011) Catal Today 175:216–222Google Scholar
  34. 34.
    Liu Q, Wang LC, Chen M, Cao Y, He HY, Fan KN (2009) J Catal 263:104–113Google Scholar
  35. 35.
    Zhang L, Shi L, Huang L, Zhang J, Gao R, Zhang D (2014) ACS Catal 4:1753–1763Google Scholar
  36. 36.
    Shang D, Zhong Q, Cai W (2015) Appl Surf Sci 325:211–216Google Scholar
  37. 37.
    Ovari L, Krick CS, Lykhach Y, Libuda J, Erdohelyi A, Papp C, Kiss J, Steinruck H-P (2013) J Catal 307:132–139Google Scholar
  38. 38.
    JeanCharles D, Danielle G, Philippe V, Alain L (2000) Phys Chem Chem Phys 2:1319–1324Google Scholar
  39. 39.
    Abu-Zied BM, Soliman SA (2009) Catal Lett 132:299Google Scholar
  40. 40.
    Grzybek G, Stelmachowski P, Gudyka S, Indyka P, Sojka Z, Guillén-Hurtado N, Rico-Pérez V, Bueno-López A, Kotarba A (2016) Appl Catal B 180:622–629Google Scholar
  41. 41.
    Zhou HB, Hu PL, Huang Z, Qin F, Shen W, Xu HL (2013) Ind Eng Chem Res 52:4504–4509Google Scholar
  42. 42.
    Shen YS, Li CL, Tang YL, Zhu SM (2014) RSC Adv 4:29107–29119Google Scholar
  43. 43.
    Xue L, Zhang CB, He H, Teraoka Y (2007) Catal Today 126:449–455Google Scholar
  44. 44.
    Stelmachowski P, Maniak G, Kaczmarczyk J, Zasada F, Piskorz W, Kotarba A, Sojka Z (2014) Appl Catal B 146:105–111Google Scholar
  45. 45.
    Maniak G, Stelmachowski P, Stanek JJ, Kotarba A, Sojka Z (2011) Catal Commun 15:127–131Google Scholar
  46. 46.
    Maniak G, Stelmachowski P, Kotarba A, Sojka Z, Rico-Pérez V, Bueno-López A (2013) Appl Catal B 136:302–307Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Engineering Research Center of Ministry of Education for Fine ChemicalsTaiyuanChina
  2. 2.School of Chemistry and Chemical EngineeringShanxi UniversityTaiyuanChina

Personalised recommendations