Synthesis of a Novel NiMnTi Mixed Metal Oxides from LDH Precursor and Its Catalytic Application for Selective Catalytic Reduction of NOx with NH3

  • XiaoJian Li
  • Yali Du
  • XingMei Guo
  • RuoNan Wang
  • BenHui Hou
  • Xu WuEmail author


NiMnTi mixed metal oxide (NiMnTi-LDO) was novelly fabricated via calcining NiMnTi layered double hydroxide. The structure and property of as-prepared sample were investigated by multiple characterizations and the results revealed that NiMnTi-LDO possessed high surface area, fine dispersion, strong reducibility and abundant surface acidic sites. The catalytic performance of NiMnTi-LDO catalyst was evaluated in selective catalytic reduction of NOx with NH3 (NH3-SCR). The catalyst displayed preferable NOx conversion of above 90% and N2 selectivity in a broad temperature range of 180–360 °C. Moreover, the resistance to SO2 and stability were favorably attained at 210 °C over NiMnTi-LDO catalyst.

Graphical Abstract

NiMnTi-LDO derived from LDH precursor was novelly prepared and evaluated in NH3-SCR


Layered double hydroxide (LDH) Mixed metal oxides NiMnTi-LDO NH3-SCR 



The project was supported by National Natural Science Foundation of the China (No. 21073131), Shanxi Provincial (No. 201601D10207).


  1. 1.
    Boningari T, Smirniotis PG (2016) Curr Opin Chem Eng 13:133–141CrossRefGoogle Scholar
  2. 2.
    Ren Z, Fan H, Wang R (2017) Catal Commun 100:71–75CrossRefGoogle Scholar
  3. 3.
    Gao F, Tang X, Yi H, Zhao S, Li C, Li J, Shi Y, Meng X (2017) Catalysts 7:199CrossRefGoogle Scholar
  4. 4.
    Mu W, Zhu J, Zhang S, Guo Y, Su L, Li X, Li Z (2016) Catal Sci Technol 6:7532–7548CrossRefGoogle Scholar
  5. 5.
    Wu R, Zhang N, Liu X. Li L, Song L, Qiu W, He H (2018) Catal Lett 148:1228–1235CrossRefGoogle Scholar
  6. 6.
    Tian W, Sheng Y, Fan X, Zhang X (2011) J Hazard Mater 188:105–109CrossRefGoogle Scholar
  7. 7.
    Chen Z, Yang Q, Li H, Li X, Wang L, Tsang S (2010) J Catal 276:56–65CrossRefGoogle Scholar
  8. 8.
    Li S, Huang B, Yu C (2017) Catal Commun 98:47–51CrossRefGoogle Scholar
  9. 9.
    Meng B, Zhao Z, Chen Y, Wang X, Li Y, Qiu J (2014) Chem Commun 50:12396–12399CrossRefGoogle Scholar
  10. 10.
    Sun W, Li X, Zhao Q, Mu J, Chen J (2018) Catal Lett 148:227–234CrossRefGoogle Scholar
  11. 11.
    Wan Y, Zhao W, Tang Y, Li L, Wang H, Cui Y, Gu J, Li Y, Shi J (2014) Appl Catal B 148–149:114–122CrossRefGoogle Scholar
  12. 12.
    Cai S, Zhang D, Shi L, Xu J, Zhang L, Huang L, Li H, Zhang J (2014) Nanoscale 6:7346–7354CrossRefGoogle Scholar
  13. 13.
    Jiang Y, Wang X, Lai C, Shi W, Liang G, Bao C, Ma S (2018) Catal Lett 148:2911–2917CrossRefGoogle Scholar
  14. 14.
    Wu G, Li J, Fang Z, Lan L, Wang R, Gong M, Chen Y (2015) Catal Commun 64:75–79CrossRefGoogle Scholar
  15. 15.
    Boningari T, Smirniotis PG (2012) J Catal 288:74–83CrossRefGoogle Scholar
  16. 16.
    Chen L, Li R, Li Z, Yuan F, Niu X, Zhu Y (2017) Catal Sci Technol 7:3243–3257CrossRefGoogle Scholar
  17. 17.
    Nie Y, Yan Q, Chen S, O’Hare D, Wang Q (2017) Catal Commun 97:47–50CrossRefGoogle Scholar
  18. 18.
    Sarkarat M, Komarneni S, Rezvani Z, Wu X, Yin S, Tsugio S, Yan Z (2013) Appl Clay Sci 80–81:390–397CrossRefGoogle Scholar
  19. 19.
    Chang Z, Zhao N, Liu J, Li F, Evans D, Duan X, Forano C, Roy M (2011) J Solid State Chem 184:3232–3239CrossRefGoogle Scholar
  20. 20.
    Jabłońska M, Palkovits R (2016) Catal Sci Technol 6:49–72CrossRefGoogle Scholar
  21. 21.
    Yan Q, Chen S, Qiu L, Gao Y, O’Hare D, Wang Q (2018) Dalton Trans 47:2992–3004CrossRefGoogle Scholar
  22. 22.
    Yan Q, Nie Y, Yang R, Cui Y, O’Hare D, Wang Q (2017) Appl Catal A 538:37–50CrossRefGoogle Scholar
  23. 23.
    Li H, Zhang D, Maitarad P, Shi L, Gao R, Zhang J, Cao W (2012) Chem Commun 48:10645–10647CrossRefGoogle Scholar
  24. 24.
    Lee Y, Choi J, Jeon H, Choi K, Lee J, Kang J (2011) Energy Environ Sci 4:914–920CrossRefGoogle Scholar
  25. 25.
    Zhao Y, Li B, Wang Q, Gao W, Wang C, Wei M, Evans D, Duan X, O’Hare D (2014) Chem Sci 5:951–958CrossRefGoogle Scholar
  26. 26.
    Basag S, Piwowarska Z, Kowalczyk A, Wegrzyn A, Baran R, Gil B, Michalik M, Chmielarz L (2016) Appl Clay Sci 129:122–130CrossRefGoogle Scholar
  27. 27.
    Xu X, Li L, Huang J, Jin H, Fang X, Liu W, Zhang N, Wang H, Wang X (2018) ACS Catal 8:8033–8045CrossRefGoogle Scholar
  28. 28.
    Boningari T, Smirniotis PG (2011) Catal Lett 141:1399–1404CrossRefGoogle Scholar
  29. 29.
    Li H, Deng L, Zhu G, Kang L, Liu Z (2012) Mater Sci Eng B 177:8–13CrossRefGoogle Scholar
  30. 30.
    Zhang W, Shi Y, Li C, Zhao Q, Li X (2016) Catal Lett 146:1956–1964CrossRefGoogle Scholar
  31. 31.
    Chen L, Niu X, Li Z, Dong Y, Zhang Z, Yuan F, Zhu Y (2016) Catal Commun 85:48–51CrossRefGoogle Scholar
  32. 32.
    Chen Z, Wang F, Li H, Yang Q, Wang L, Li X (2012) Ind Eng Chem Res 51:202–212CrossRefGoogle Scholar
  33. 33.
    Deshmane V, Owen S, Abrokwah R, Kuila D (2015) J Mol Catal A 408:202–213CrossRefGoogle Scholar
  34. 34.
    Boningari T, Smirniotis PG (2011) Appl Catal B 110:195–206CrossRefGoogle Scholar
  35. 35.
    Yuan D, Li X, Zhao Q, Zhao J, Tadé M, Liu S (2014) J Catal 309:268–279CrossRefGoogle Scholar
  36. 36.
    Hu H, Cai S, Li H, Huang L, Shi L, Zhang D (2015) ACS Catal 5:6069–6077CrossRefGoogle Scholar
  37. 37.
    Ali S, Chen L, Yuan F, Li R, Zhang T (2017) Appl Catal B 210:223–234CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  • XiaoJian Li
    • 1
  • Yali Du
    • 2
  • XingMei Guo
    • 1
  • RuoNan Wang
    • 1
  • BenHui Hou
    • 1
  • Xu Wu
    • 1
    Email author
  1. 1.College of Chemistry and Chemical EngineeringTaiyuan University of TechnologyTaiyuanPeople’s Republic of China
  2. 2.College of Chemistry and Chemical EngineeringJinzhong UniversityJinzhongPeople’s Republic of China

Personalised recommendations