Solidification of Spent Ion-Exchange Resin Pulps with Aid of Polymer Binders
- 4 Downloads
The results of studies of the physical and chemical properties of samples obtained during solidification of simulators of spent ion-exchange resin pulps with the use of polymer binders are presented. Investigations were conducted for pulps simulating heterogeneous radioactive wastes from the Kursk NPP. It is shown that the physical and chemical properties of the final compounds and the technological processes used to obtain them correspond to the requirements of solidified radioactive waste sent to storage or disposal. The surface of the samples is uniform and the components are distributed uniformly. Water resistance and radiation resistance tests showed that the mechanical strength of the tested samples is almost identical to the initial strength. It is shown that the mechanical load at which plastic deformation of the polymer compound occurs is a factor of two larger than and the leach rate does not exceed the established value.
Unable to display preview. Download preview PDF.
- 1.C. Miller, P. Werner, and C. Jensen, “In situ solidification and encapsulation of commercial nuclear power plant, DOE and DOD wastes,” in: WM’06 Conf., Feb. 26 – March 2, 2006, 09-WM-06151.Google Scholar
- 2.NP-019–15, Collection, Reprocessing, Storage, and Conditioning of Liquid Radwastes. Safety Requirements, NTTs YaRB, Moscow (2015).Google Scholar
- 3.NP-093–14, Acceptability Criteria for Disposal of Radwaste, NTTs YaRB, Moscow (2015).Google Scholar
- 4.RB-023-02, Recommendations for Establishing Acceptability Criteria for Conditioned Radwaste for Storage and Disposal, NTTs YaRV, Moscow (2001).Google Scholar
- 5.GOST R 52126–2003, Radioactive Waste. Determination of the Chemical Stability of Solidified High-Level Waste by the Long-Time Leaching Method, Izd. Standartov, Moscow (2003).Google Scholar
- 6.GOST 10180–12, Concretes. Methods of Determining Strength Using Control Samples, Standartinform, Moscow (2013).Google Scholar
- 7.OI 001.725–2011, Cement Compounds Based on Radwaste. Determination of Ultimate Strength in Compression Using a Testing Brand Machine. Industry Instructions, GKhK, Zheleznogorsk (2011).Google Scholar