Testing the self-cleaning properties of a coordination polymer surface
- 359 Downloads
It is well established that self-cleaning can be related to the hydrophobic or hydrophilic nature of a surface. Using adsorption chromatography, molecular simulations and wetting dynamics measurements, the self-cleaning properties of a new, strongly water resistant and hydrophilic cystine-containing coordination polymer (CP) were tested. Adsorption isotherms of n-octane and methanol were determined in the range of 313–343 K. Next the isosteric enthalpy of adsorption and the change in adsorption entropy were calculated to explain higher adsorption of methanol than n-butane. Performed chromatographic tests, molecular dynamics simulations and wetting dynamics experiments additionally prove that the Zn(Cys)2 CP is a promising material for the application in the preperation of self-cleaning surfaces or coatings.
It is well established that the self-cleaning technologies are among the most important achievements of biomimetics. As it was pointed out by Ganesh et al. self-cleaning has many important applications (cleaning of glass, textiles, solar batteries etc.) (Ganesh et al. 2011). Self-cleaning can be the native property of a surface and/or can be introduced using different coatings. There are two major categories of self-cleaning surfaces: hydrophobic (Varshney and Mohapatra 2018; Yu et al. 2018; He et al. 2018) and hydrophilic (Prince et al. 2014). In the case of hydrophobic self-cleaning surfaces the repelling of water from a substrate causes the rolling of a droplet across a surface and the dirt is carried away with the droplet. This effect is observed for example for the Lotus leaves (Crick and Parkin 2010; Yu et al. 2014). In the case of hydrophilic surfaces the self-cleaning is due to the spreading of water on a surface.
Recently some new self-cleaning systems have been proposed utilizing the photocatalytic effect for the degradation of organic pollutants adsorbed on a surface (Yusof et al. 2018). Moreover some “smart” surfaces have been also developed and the self-cleaning effect can be UV (Kaner et al. 2017; Pifferi et al. 2015) or laser-induced (Zheng et al. 2016).
In this study we present the experimental data and give an insight into the molecular mechanism of the self-cleaning process. A hydrophilic, cysteine (Cys) containing coordination polymer (CP) Zn(C3H5NO2S)2 is applied for this purpose (Ferrer et al. 2014). This CP is strongly water-resistant and, as it is shown in our study, the adsorbed hydrocarbon molecules are easily removed from its surface by polar molecules i.e. methanol and/or water. The experimental results are supported by molecular simulations. To the best of our knowledge, this is the first study reporting the self-cleaning properties of CP surfaces.
2.1 Coordination polymer
A Zn(Cys)2 CP was obtained using the procedure reported by Ferrer et al. (2014). The structure was confirmed by the XRD, FTIR thermal and elemental analysis. This CP is nonporous (the BET surface area is equal to 96 m2/g). The crystallographic data and the structure of this CP were reported previously (Ferrer et al. 2014).
2.2 Chromatographic measurements
The chromatographic investigations were carried out using a Chrom 4 gas chromatograph with a flame ionization detector (FID). A computer was connected to the gas chromatograph to control, acquire and process the chromatographic data. The adsorbent was placed in glass column (30 cm × 2 mm I.D.) with an absorbent bed length of 22 cm, which corresponded to 0.37 g of Zn(Cys)2 used. Before adsorption experiments, the column with the adsorbent was conditioned at 403 K for 8 h under a flow of helium.
Methanol and n-octane (A.R. grade) were used as adsorbates. The adsorbates were injected into the column by means of a Hamilton microsyringe. The size of the injected samples was 0.5 µl. The temperature of the injection device was set at 373 K and 433 K for methanol and n-octane, respectively. Additionally in some experiments, to investigated the effect of water on n-octane adsorption, dosed different amounts of water (1, 2, 4 µl) before as well after n-octane injection.
2.3 Molecular simulation of wetting and self-cleaning
All molecular dynamics (MD) simulations were performed using the OpenMM molecular simulation toolkit (Eastman et al. 2013). As in our previous studies (Włoch et al. 2017a, b, 2018) the TIP4P/2005 (Abascal and Vega 2005) water model was applied. The OPLSAA force field parameters were taken from the TINKER package (Robertson et al. 2015; Lagardère et al. 2018), while the parameters for Zn were taken from the study of Li et al. (2013). First the wetting of the bare CP surface was determined. Next, to study the self-cleaning effect, the monolayer adsorption of hydrocarbons was simulated (C10H22, C24H50 and C55H112). Lastly, the water drop was placed on top of the equilibrated alkane monolayer, and the wetting properties were determined again. The hydrocarbon molecules could freely move on a surface (see Electronic Supplementary Material for further simulation details and results).
2.4 Dynamics of wetting
To check the dynamics of wetting six Zn(Cys)2 samples were prepared following the procedure described in Electronic Supplementary Material. Three of them were thermally desorbed (T = 393 K) and the remaining three were equilibrated with the saturated C10H22 vapour at the T = 300 K. Next the wetting process was performed using the system described in the Electronic Supplementary Material, and the movies were recorded.
3 Results and discussion
3.1 Chromatographic data
From the data collected in Figures S1 and S2 (Electronic Supplementary Material) one can observe that the carrier gas flow-rate (VHe = 30 and 60 cm3/min) has small influence on the n-octane adsorption isotherms determined in the range of T = 313–343 K. In contrast, we observe the influence of this gas flow-rate on methanol adsorption. This is why for our calculations we used the data determined at the flow 30 cm3/min. As it can be seen from the data collected in Figures S2c and S2d the reproducibility of measurements is very good.
Figure 1 shows the comparison of methanol and n-octane adsorption isotherms on Zn(Cys)2 determined for the studied temperatures. In the case of both adsorbates one can observe the linear parts of adsorption isotherms at low coverages, and the decrease of adsorption with the rise in temperature (due to the exothermic nature of the process).
Moreover, for all studied temperatures the adsorption of n-octane is smaller than the adsorption of the methyl alcohol (the same sequence of adsorption isotherms is observed at the flow-rate of 60 cm3/min—see Figure S3 in the Electronic Supplementary Material).
Figure 2 shows the comparison of the isosteric enthalpy of adsorption (calculated using Eq. 1) and the change in the entropy of the process (Eq. 2). One can conclude that the qst values are more negative for n-octane than for methanol. Moreover, the absolute value of methanol adsorption enthalpy progressively decreases due to heterogeneity of the studied CP surface. The rise in the absolute enthalpy value (starting at adsorption ca. 20 µmole/g) is caused by adsorption of subsequent methanol molecule forming surface associates, because it is well known that the adsorption mechanism of polar molecules is usually dominated by clustering around the adsorption sites (Furmaniak et al. 2008). It has been well established that the metal nodes serve as the CP adsorption centers for hydrogen and polar molecules (Rosi et al. 2003). Thus one can expect, that in the case of methanol we observe donor–acceptor interactions with exposed zinc surface cations. As it can be observed in Fig. 2b the absolute value of the n-octane adsorption enthalpy slightly increases at small coverages and next remains almost constant. The enthalpy steadiness is caused by the decrease of the solid–fluid interactions with the concomitant increase of the fluid–fluid interactions, upon rising the surface coverage (Vernov and Steele 1991). It is well proved that the non-polar molecules (like alkanes) during adsorption may form different ordered structures due to adsorbate–adsorbate interactions (Gilbert et al. 1998). Since the n-octane molecule does not possess the dipole moment, the adsorption in this case is not very sensitive to the presence of the surface polar sites. Thus, the observed in Fig. 1 (and Figure S3) better methanol than n-octane adsorption causes more positive entropy change, in comparison to the liquid state (Fig. 2c, d). We conclude that the n-octane molecules due to the strong affinity for the CP surface, as well as due to the fluid–fluid interactions are less mobile than the adsorbed methanol molecules.
The fact that the adsorption of methanol is stronger than the adsorption of n-octane has been also corroborated by the results collected in Fig. 3. In this figure we show the chromatograms of dosed n-octane followed by injection of different volumes of methanol (Fig. 3a) and water (Fig. 3b) into the column. We note that the addition of polar molecules decreases the n-octane retention time. Thus it can be concluded that n-octane is expelled from the adsorbed phase by polar methanol and/or water molecules.
3.2 Molecular simulation and wetting dynamics results
Figure 4 collects the results of MD simulation for water nanodroplet sitting on the considered CP surface. One can observe that the complete wetting occurs, and the resulting water contact angle is equal to zero. It means, that the studied CP surface is strongly hydrophilic, and completely wetted by water at the room temperature. However, more interesting are the results showing the behavior of water nanodroplet on the studied CP surface covered by an n-alkane monolayer. Collected in Fig. 5 results for n-decane show that the equilibrated hydrocarbon monolayer (see Fig. 5 for t = 0.5 ns) is completely expelled by water molecules forming the nanodroplet (see Fig. 5 for t = 2.5, 5 and 10.5 ns). The same situation is observed for other n-alkane molecules (see Figure S4 in the Electronic Supplementary Material), leading to conclusion about the self-cleaning properties of the studied CP surface. It is interesting to note, that even C55H112 molecules (being solid at the normal conditions) are successfully expelled by the nanodroplet of water sitting on the studied CP surface (Figure S4). This indicates that the self-cleaning behaviour is robust.
Figure 6 collects the results of wetting dynamics measurements. As one can observe, macroscopic water droplet wets the dry Zn(Cys)2 surface very fast (around 1 s) however, the wetting of Zn(Cys)2 equilibrated with C10H22 vapour is around 5 times longer. This is the confirmation of the chromatography and simulation results presented above.
Zn(Cys)2 CP adsorbs better polar molecules than n-alkanes. The mechanism of low-coverage adsorption in the case of CH3OH is controlled by adsorption on polar surface sites and clusterisation. For n-octane adsorption process is dominated by adsorbate–adsorbate interactions. Higher affinity of Zn(Cys)2 surface to polar than to nonpolar molecules is confirmed by the MD simulation results showing that even C55H112 molecules are expelled from the CP surface by water nanodroplet. This finally leads in the macroscale to the faster wetting of a bare Zn(Cys)2 surface than a surface covered by hydrocarbons. Thus studied CP, being strongly water resistant is a promising material for the formation of self-cleaning surfaces and/or coatings. To get a deeper insight into the mechanism of the self-cleaning process further data are necessary and the results will be reported by us in near future.
This manuscript is dedicated to the memory of our friend and coworker dr hab. Jerzy Włoch who passed away on 12.06.2018. We gratefully acknowledge financial support by the Polish National Science Centre (NCN) Grant OPUS 9 no. 2015/17/B/ST5/01446, and Grant OPUS 13 UMO-2017/25/B/ST5/00975.
- Eastman, P., Friedrichs, M.S., Chodera, J.D., Radmer, R.J., Bruns, C.M., Ku, J.P., Beauchamp, K.A., Lane, T.J., Wang, L.-P., Shukla, D., Tye, T., Houston, M., Stich, T., Klein, C., Shirts, M.R., Pande, V.S.: OpenMM 4: a reusable, extensible, hardware independent library for high performance molecular simulation. J. Chem. Theory Comput. 9, 461–469 (2013)CrossRefGoogle Scholar
- Grob, R.L.: Physicochemical measurements by gas chromatography. In: Eugene F. Barry, Thomas A. Brettell (eds.) Modern Practice of Gas Chromatography, 3rd edn. Wiley, New York (1995)Google Scholar
- Lagardère, L., Jolly, L.H., Lipparini, F., Aviat, F., Stamm, B., Jing, Z.F., Harger, M., Torabifard, H., Cisneros, G.A., Schnieders, M.J., Gresh, N., Maday, Y., Ren, P.Y., Ponder, J.W., Piquemal, J.P.: Tinker-HP: a massively parallel molecular dynamics package for multiscale simulations of large complex systems with advanced point dipole polarizable force fields. Chem. Sci. 9, 956–972 (2018)CrossRefGoogle Scholar
- Majer, V., Svoboda, V.: Enthalpies of Vaporization of Organic Compounds: A Critical Review and Data Compilation. Blackwell Scientific Publications, Oxford (1985)Google Scholar
- Paryjczak, T.: Gas Chromatography in Adsorption and Catalysis. Ellis Horwood, Chichester (1987)Google Scholar
- Prince, J.A., Bhuvana, S., Anbharasi, V., Ayyanar, N., Boodhoo, K.V.K., Singh, G.: Self-cleaning metal organic framework (MOF) based ultra filtration membranes—a solution to bio-fouling in membrane separation processes. Sci. Rep. 4, 6555 (2014). https://doi.org/10.1038/srep06555 CrossRefGoogle Scholar
- Yaws, C.L.: Yaws’ Handbook of Thermodynamic and Physical Properties of Chemical Compounds: Physical, Thermodynamic and Transport Properties for 5,000 Organic Chemical Compounds. McGraw-Hill, New York (2003)Google Scholar
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.