Quantitative phase analysis of fly ash of municipal solid waste by X-ray powder diffractometry/Rietveld refinement

  • Atsushi OhbuchiEmail author
  • Yuya Koike
  • Toshihiro Nakamura
ORIGINAL ARTICLE
  • 17 Downloads

Abstract

Six crystalline phases (anhydrite, calcite, gehlenite, halite, quartz, and sylvite) and the amorphous phase in fly ash of municipal solid waste (MSW) were quantified using Rietveld refinement of X-ray diffraction data. Corundum was used as an internal standard for the determination of amorphous phase. Gehlenite was synthesized by the solid-phase method to obtain the pure material for calibration standard. Quantitative values of 4.8, 5.1, 12.3, 9.3, 1.3, and 7.1 mass% for anhydrite, calcite, gehlenite, halite, quartz, and sylvite, respectively, were obtained by Rietveld refinement, in agreement with those obtained using the external standard and standard addition methods. Relative standard deviations (n = 5) of each crystalline phase were 1.6–63%. Monthly variations of crystalline phases of MSW fly ash were observed over a year (2008–2009). High correlation (R = 0.8068) was observed between the concentrations of halite and sylvite, which were derived from kitchen wastes such as vegetables and seasonings. Conspicuous concentrations of calcite and quartz were each observed once at June and December, respectively. Rietveld refinement was applicable as a quantitative method for the determination of MSW fly ash composition profile.

Keywords

MSW fly ash X-ray diffractometry Rietveld refinement Determination of crystalline phase Seasonal variation 

Notes

References

  1. 1.
    Sakai S, Urano S, Takatsuki H (2000) Leaching behavior of PCBs and PCDDs/DFs from some waste materials. Waste Manag 20:241–247.  https://doi.org/10.1016/S0956-053X(99)00316-5 CrossRefGoogle Scholar
  2. 2.
    Verhulst D, Buekens A, Spencer PJ, Eriksson G (1996) Thermodynamic behavior of metal chlorides and sulfates under the conditions of incineration furnaces. Environ Sci Technol 30:50–56.  https://doi.org/10.1021/es940780&%23x002B; CrossRefGoogle Scholar
  3. 3.
    Saikia N, Kato S, Kojima T (2007) Production of cement clinkers from municipal solid waste incineration (MSWI) fly ash. Waste Manag 27:1178–1189.  https://doi.org/10.1016/j.wasman.2006.06.004 CrossRefGoogle Scholar
  4. 4.
    Aubert JE, Husson B, Sarramone N (2006) Utilization of municipal solid waste incineration (MSWI) fly ash in blended cement Part 1: processing and characterization of MSWI fly ash. J Hazard Mater B136:624–631.  https://doi.org/10.1016/j.jhazmat.2005.12.041 CrossRefGoogle Scholar
  5. 5.
    Qian G, Song Y, Zhang C, Xia Y, Zhang H, Chui P (2006) Diopside-based glass-ceramics MSW fly ash and bottom ash. Waste Manag 26:1462–1467.  https://doi.org/10.1016/j.wasman.2005.12.009 CrossRefGoogle Scholar
  6. 6.
    Nishida K, Nagayoshi Y, Ota H, Nagasawa H (2001) Melting and stone production using MSW incinerated ash. Waste Manag 21:443–449.  https://doi.org/10.1016/S0956-053X(00)00136-7 CrossRefGoogle Scholar
  7. 7.
    Fan Y, Zhang FS, Zhu J, Liu Z (2008) Effective utilization of waste ash from MSW and coal co-combustion power plant-zeolite synthesis. J Hazard Mater 153:382–388.  https://doi.org/10.1016/j.jhazmat.2007.08.061 CrossRefGoogle Scholar
  8. 8.
    Takaoka M, Nakatsuka D, Takeda N, Fujiwara T (2000) Application of X-ray fluorescence analysis to determination of elements in fly ash (in Japanese). J Jpn Soc Waste Manag Exp 11:333–342.  https://doi.org/10.3985/jswme.11.333 CrossRefGoogle Scholar
  9. 9.
    Ohbuchi A, Kitano M, Nakamura T (2008) Powder briquette/X-ray fluorescence analysis of major and minor elements in alkali-washed fly ash of municipal solid waste. X-ray Spectrom 37:237–244.  https://doi.org/10.1002/xrs.1046 CrossRefGoogle Scholar
  10. 10.
    Ferreira C, Ribeiro A, Ottosen L (2005) Effect of major constituents of MSW fly ash during electrodialytic remediation of heavy metals. Sep Sci Technol 40:2007–2019.  https://doi.org/10.1081/SS-200068412 CrossRefGoogle Scholar
  11. 11.
    Torigai M, Ouyang T, Iwashima K, Osako M, Tanaka M (1997) Studies on microwave digestion procedure for the simultaneous multielement determination of arsenic, antimony, chromium, cadmium, nickel, and lead in municipal waste incineration fly ash by ICP-AES (in Japanese). Bunseki Kagaku 46:401–406.  https://doi.org/10.2116/bunsekikagaku.46.401 CrossRefGoogle Scholar
  12. 12.
    Mester Z, Angelone M, Brunori C, Cremisini C, Muntau H, Morabito R (1999) Digestion methods for analysis of fly ash samples by atomic absorption spectrometry. Anal Chim Acta 395:157–163.  https://doi.org/10.1016/S0003-2670(99)00342-6 CrossRefGoogle Scholar
  13. 13.
    Lima AT, Ottosen LM, Pedersen AJ, Riberio AB (2008) Characterization of fly ash bio and municipal waste. Biomass Bioenergy 32:277–282.  https://doi.org/10.1016/j.biombioe.2007.09.005 CrossRefGoogle Scholar
  14. 14.
    Fujii K, Ochi K, Ohbuchi A, Koike Y (2018) Evaluation of physicochemical properties of radioactive cesium in municipal solid waste incineration fly ash by particle size classification and leaching tests. J Environ Manag 217:157–163.  https://doi.org/10.1016/j.jenvman.2018.03.028 CrossRefGoogle Scholar
  15. 15.
    Zheng L, Wang C, Wang W, Shi Y, Gao X (2011) Immobilization of MSW fly ash through geopolymerization: effects of water-wash. Waste Manag 31:311–317.  https://doi.org/10.1016/j.wasman.2010.05.015 CrossRefGoogle Scholar
  16. 16.
    Polyak K, Bodog I, Hlavay J (1994) Determination of chemical species of selected trace elements in fly ash. Talanta 41:1151–1159.  https://doi.org/10.1016/0039-9140(94)80086-3 CrossRefGoogle Scholar
  17. 17.
    Chang FY, Wey MY (2006) Comparison of the characteristics of bottom and fly ashes generated from various incineration processes. J Hazard Mater 138:594–603.  https://doi.org/10.1016/j.jhazmat.2006.05.099 CrossRefGoogle Scholar
  18. 18.
    Rietveld HM (1969) A profile refinement method for nuclear and magnetic structures. J Appl Cryst 2:65–71.  https://doi.org/10.1107/S0021889869006558 CrossRefGoogle Scholar
  19. 19.
    Chung FH, Scott RW (1973) A new approach to the determination of crystallinity of polymers by X-ray diffraction. J Appl Cryst 6:225–230.  https://doi.org/10.1107/S0021889873008514 CrossRefGoogle Scholar
  20. 20.
    Bish DL, Howard CJ (1988) Quantitative phase analysis using the Rietveld method. J Appl Cryst 21:86–91.  https://doi.org/10.1107/S0021889887009415 CrossRefGoogle Scholar
  21. 21.
    Taylor JC, Aldridge LP (1993) Full-profile Rietveld quantitative XRD analysis of Portland cement: standard XRD profiles for the major phase tricalcium silicate (C3S: 3CaO·SiO2). Powder Diffr 8:138–144.  https://doi.org/10.1017/S0885715600018054 CrossRefGoogle Scholar
  22. 22.
    Taylor JC, Hinczak I, Matulis CE (2000) Rietveld full-profile quantification of Portland cement clinker: the importance of including a full crystallography of the major phase polymorphs. Powder Diffr 15:7–18.  https://doi.org/10.1017/S0885715600010769 CrossRefGoogle Scholar
  23. 23.
    Guirado F, Gali S, Chinchon S (2000) Quantitative Rietveld analysis of aluminous cement clinker phases. Cem Concr Res 30:1023–1029.  https://doi.org/10.1016/S0008-8846(00)00289-1 CrossRefGoogle Scholar
  24. 24.
    Kocklmann W, Kirfel A (2001) Non-destructive phase analysis of archaeological ceramics using TOF neutron diffraction. J Archaeol Sci 28:213–222.  https://doi.org/10.1006/jasc.2000.0651 CrossRefGoogle Scholar
  25. 25.
    Pajares I, de la Torre AG, Martinez-Ramirez S, Puertas F, Blanco-Varela MT, Aranda MAG (2002) Quantitative analysis of mineralized white Portland clinkers: the structure of fluorellestadite. Powder Diffr 17:281–286.  https://doi.org/10.1154/1.1505045 CrossRefGoogle Scholar
  26. 26.
    Schmidt R, Pollmann H (2000) Quantitative of calcium sulpho-aluminate cement by Rietveld analysis. Mater Sci Forum 321–324:1022–1027.  https://doi.org/10.4028/www.scientific.net/MSF.321-324.1022 CrossRefGoogle Scholar
  27. 27.
    Suherman PM, van Riessen A, O’Connor B, Bolton D, Fairhurst H (2002) Determination of amorphous phase levels in Portland cement clinker. Powder Diffr 17:178–185.  https://doi.org/10.1154/1.1471518 CrossRefGoogle Scholar
  28. 28.
    Izumi F, Ikeda T (2000) A Rietveld-analysis program RIETAN-98 and its application to zeolites. Mater Sci Forum 321–324:198–203.  https://doi.org/10.4028/www.scientific.net/MSF.321-324.198 CrossRefGoogle Scholar
  29. 29.
    Nakamura T (1988) Quantitative determination by X-ray diffractometry of calcium sulfate and calcium carbonate in airborne dusts. Powder Diffr 3:86–90.  https://doi.org/10.1017/S0885715600013294 CrossRefGoogle Scholar
  30. 30.
    Ohbuchi A, Kitano M, Nakamua T (2009) XRF analysis for major and minor elements in fly ash of municipal solid waste incineration using powder briquette method (in Japanese). Bunseki Kagaku 58:249–256.  https://doi.org/10.2116/bunsekikagaku.58.249 CrossRefGoogle Scholar
  31. 31.
    Toraya H (1990) Array-type universal profile function for powder pattern fitting. J Appl Cryst 23:485–491.  https://doi.org/10.1107/S002188989000704X CrossRefGoogle Scholar
  32. 32.
    Cheng GCH, Zussman J (1963) The crystal structure of anhydrite (CaSO4). Acta Cryst 16:767–769.  https://doi.org/10.1107/S0365110X63001997 CrossRefGoogle Scholar
  33. 33.
    Sass RL, Vidale R, Donohue J (1957) Interatomic distances and thermal anisotropy in sodium nitrate and calcite. Acta Cryst 10:567–570.  https://doi.org/10.1107/S0365110X57002029 CrossRefGoogle Scholar
  34. 34.
    Ishizawa N, Miyata T, Minota I, Marumo F, Iwai S (1980) A structure investigation of α-Al2O3 at 2170 K. Acta Cryst B36:228–230.  https://doi.org/10.1107/S0567740880002981 CrossRefGoogle Scholar
  35. 35.
    Swainson IP, Dove MT, Schemahl WW (1992) Neutron powder diffraction study of the åkermanite–gehlenite solid solution series. Phys Chem Miner 19:185–195.  https://doi.org/10.1007/BF00202107 CrossRefGoogle Scholar
  36. 36.
    Barrett WT, Wallace WE (1954) Studies of NaCl-KCl solid solutions. I. Heats of formation, lattice spacings, densities, Schottky defects and mutual solubilities. J Am Chem Soc 76:366–369.  https://doi.org/10.1021/ja01631a014 CrossRefGoogle Scholar
  37. 37.
    Young RA, Mackie PE, von Dreele RB (1977) Application of the pattern-fitting structure-refinement method of X-ray powder diffractometer. J Appl Cryst 10:262–269.  https://doi.org/10.1107/S0021889877013466 CrossRefGoogle Scholar
  38. 38.
    Dollase WA (1986) Correction of intensities for preferred orientation in powder diffractometry: application of the March model. J Appl Cryst 19:267–272.  https://doi.org/10.1107/S0021889886089458 CrossRefGoogle Scholar
  39. 39.
    Charlu TV, Newton RC, Kleppa OJ (1981) Thermochemistry of synthetic Ca2Al2SiO7 (gehlenite)–Ca2MgSi2O7 (åkermanite) melilites. Geo Cos Acta 45:1609–1617.  https://doi.org/10.1016/0016-7037(81)90289-1 CrossRefGoogle Scholar
  40. 40.
    Yoshioka T (1969) Some observations on the synthetic gehlenites. J Jpn Assoc Mineral Petrol Econ Geol 61:106–111.  https://doi.org/10.2465/ganko1941.61.106 CrossRefGoogle Scholar
  41. 41.
    Asahi T, Matsudaira T, Kobayashi S, Nakayama K, Nakamura T (2010) Estimation of purity of chrysotile asbestos by X-ray diffractometry/Rietveld refinement. Anal Sci 26:1295–1300.  https://doi.org/10.2116/analsci.26.1295 CrossRefGoogle Scholar
  42. 42.
    Ohbuchi A. Nakamura T (2018) Sample preparation and quantitative analysis for powder. Encyclopedia of analytical chemistry. Wiley, New York.  https://doi.org/10.1002/9780470027318.a9561 Google Scholar
  43. 43.
    Ohbuchi A, Kitano M, Nakamura T (2008) X-ray fluorescence analysis of sludge ash from sewage disposal plant. X-ray Spectrom 37:544–550.  https://doi.org/10.1002/xrs.1085 CrossRefGoogle Scholar
  44. 44.
    Kasina M, Kowalski PR, Michalik M (2017) Seasonal changes in chemical and mineralogical composition of sewage sludge incineration residues and their potential for metallic elements and valuable components recovery. Energy Procedia 125:34–40.  https://doi.org/10.1016/j.egypro.2017.08.049 CrossRefGoogle Scholar
  45. 45.
    Grubbs FE (1950) Sample criteria for testing outlying observations. Ann Math Stat 21:27–58.  https://doi.org/10.1214/aoms/1177729885 MathSciNetCrossRefzbMATHGoogle Scholar

Copyright information

© Springer Japan KK, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Research and Development DepartmentApplied Rigaku Technologies, Inc.AustinUSA
  2. 2.X-ray Instrumental DivisionRigaku CorporationAkishimaJapan
  3. 3.Department of Applied Chemistry, School of Science and TechnologyMeiji UniversityKawasakiJapan

Personalised recommendations