, Volume 64, Issue 4, pp 398–405 | Cite as

Effect of alkali treatment on wettability and thermal stability of individual bamboo fibers

  • Hong Chen
  • Wenfu Zhang
  • Xuehua Wang
  • Hankun Wang
  • Yan Wu
  • Tuhua ZhongEmail author
  • Benhua FeiEmail author
Original Article

Abstract

The aim of this study is to examine the wettability and thermal properties of individual bamboo fibers after alkali treatment. The individual bamboo fibers were treated by sodium hydroxide (NaOH) solution with varying concentrations (6, 8, 10, 15 and 25%) followed by freeze-drying treatment. The surface analysis of alkali-treated individual bamboo fibers was characterized by atomic force microscope. Water droplet on the individual fiber surface was observed with drop shaper analyzer and the contact angles on fiber surface were also measured. Thermal properties were further studied by thermogravimetric analysis. The results indicated that alkali treatment resulted in the increase in surface roughness of individual bamboo fibers. Alkali treatment with low NaOH concentration could enhance the wettability of treated individual bamboo fibers, and while the wettability was reduced with alkali treatment at high concentration (25%). Thermal analysis revealed that the onset of decomposition and the maximum decomposition were moved to higher temperature after alkali treatment at low NaOH concentrations (6, 8, and 10%), suggesting the improvement in the thermal stability of treated individual bamboo fibers, while the thermal stability was compromised after alkali treatment at higher concentrations (15 and 25%).

Keywords

Bamboo fiber Alkali treatment Surface analysis Wettability Thermal stability 

Notes

Acknowledgements

We would like to appreciate the Basic Scientific Research Funds of International Center for Bamboo and Rattan (1632016007), and National Natural Science Foundation of China (31500474, 31370563).

Supplementary material

10086_2018_1713_MOESM1_ESM.docx (1013 kb)
Supplementary material 1 (DOCX 1013 KB)

References

  1. 1.
    Yu Y, Tian GL, Wang HK, Fei BH, Wang G (2011) Mechanical characterization of single bamboo fibers with nanoindentation and microtensile technique. Holzforschung 65:113–119Google Scholar
  2. 2.
    Liese W, Köhl M (eds) (2015) Bamboo: the plant and its uses. Springer, ChamGoogle Scholar
  3. 3.
    Ren D, Yu ZX, Zhang XX, Wang HK, Wang H, Yu Y (2017) Quantitative characterization of the interface between bamboo fiber and polypropylene with pull-out test and nanomechanical imaging. J Mater Sci 52(3):1296–1307CrossRefGoogle Scholar
  4. 4.
    Fei P, Fei BH, Yan Y, Xiong HG, Tan J (2014) Thermal properties and crystallization behavior of bamboo fiber/high-density polyethylene composites: nano-TiO2 effects. J Appl Poly Sci 131(3).  https://doi.org/10.1002/APP.39846
  5. 5.
    Alix S, Philippe E, Bessadok A, Lebrun L, Morvan C, Marais S (2009) Effect of chemical treatments on water sorption and mechanical properties of flax fibres. Bioresour Technol 100(20):4742–4749CrossRefGoogle Scholar
  6. 6.
    Narendar R, Dasan KP (2014) Chemical treatments of coir pith: morphology, chemical composition, thermal and water retention behavior. Compos Part B Eng 56:770–779CrossRefGoogle Scholar
  7. 7.
    Das M, Chakraborty D (2006) Influence of alkali treatment on the fine structure and morphology of bamboo fibers. J Appl Polym Sci 102(5):5050–5056CrossRefGoogle Scholar
  8. 8.
    Das M, Chakraborty D (2008) Evaluation of improvement of physical and mechanical properties of bamboo fibers due to alkali treatment. J Appl Polym Sci 107(1):522–527CrossRefGoogle Scholar
  9. 9.
    Liu Y, Hu H (2008) X-ray diffraction study of bamboo fibers treated with NaOH. Fibers Polym 9(6):735–739CrossRefGoogle Scholar
  10. 10.
    Ray D, Sarkar BK (2001) Characterization of alkali-treated jute fibers for physical and mechanical properties. J Appl Polym Sci 80(7):1013–1020CrossRefGoogle Scholar
  11. 11.
    Liu DG, Song JW, Anderson DP, Chang PR, Hua Y (2012) Bamboo fiber and its reinforced composites: structure and properties. Cellulose 19:1449–1480CrossRefGoogle Scholar
  12. 12.
    Chen H, Wang G, Cheng HT (2011) Properties of single bamboo fibers isolated by different chemical methods. Wood Fiber Sci 43(2):1–10Google Scholar
  13. 13.
    Amel BA, Paridah MT, Sudin R, Anwar UMK, Hussein AS (2013) Effect of fiber extraction methods on some properties of kenaf bast fiber. Ind Crops Prod 46:117–123CrossRefGoogle Scholar
  14. 14.
    Nakagaito AN, Yano H (2008) Toughness enhancement of cellulose nanocomposites by alkali treatment of the reinforcing cellulose nanofibers. Cellulose 15:323–331CrossRefGoogle Scholar
  15. 15.
    Reddy KO, Maheswari CU, Shukla M, Song JI, Rajulu AV (2013) Tensile and structural characterization of alkali treated Borassus fruit fine fibers. Compos Part B Eng 44(1):433–438CrossRefGoogle Scholar
  16. 16.
    Xu YJ, Xu Y, Yue XP (2017) Changes of hydrogen bonding and aggregation structure of cellulose fiber due to microwave-assisted alkali treatment and its impacts on the application as fluff pulp. Cellulose 24:967–976CrossRefGoogle Scholar
  17. 17.
    Sinha E, Rout SK (2008) Influence of fibre-surface treatment on structural, thermal and mechanical properties of jute. J Mater Sci 43:2590–2601CrossRefGoogle Scholar
  18. 18.
    Ariawan D, Mohd Ishak ZA, Salim MS, Mat Taib R, Ahmad Thirmizir MZ (2017) Wettability and interfacial characterization of alkaline treated kenaf fiber-unsaturated polyester composites fabricated by resin transfer molding. Polym Compos 38(3):507–515CrossRefGoogle Scholar
  19. 19.
    Balaji AN, Nagarajan KJ (2017) Characterization of alkali treated and untreated new cellulosic fiber from Saharan aloe vera cactus leaves. Carbohydr Polym 174:200–2008CrossRefGoogle Scholar
  20. 20.
    Norul Izani M, Paridah MT, Anwar UMK, Mohd Nor MY, H’ng PS (2013) Effects of fiber treatment on morphology, tensile and thermogravimetric analysis of oil palm empty fruit bunches fibers. Compos Part B Eng 45(1):1251–1257CrossRefGoogle Scholar
  21. 21.
    Rashid B, Leman Z, Jawaid M, Ghazali MJ, Ishak MR (2016) Physiochemical and thermal properties of lignocellulosic fiber from sugar palm fiber: effect of treatment. Cellulose 23:2905–2916CrossRefGoogle Scholar
  22. 22.
    Wang F, Zhou SJ, Li L, Zhang XP (2017) Changes in the morphological-mechanical properties and thermal stability of bamboo fibers during the processing of alkali treatment. Polym Compos.  https://doi.org/10.1002/pc.24332 CrossRefGoogle Scholar
  23. 23.
    Yang ZP, Xu SW, Ma XL, Wang SY (2008) Characterization and acetylation behavior of bamboo pulp. Wood Sci Technol 42:621–632CrossRefGoogle Scholar
  24. 24.
    Chen H, Yu Y, Zhong T, Wu Y, Li Y, Wu Z, Fei B (2017) Effect of alkali treatment on microstructure and mechanical properties of individual bamboo fibers. Cellulose 24(1):333–347CrossRefGoogle Scholar
  25. 25.
    Wang G, Shi S, Wang JW, Yu Y, Cao SP, Cheng HT (2011) Tensile properties of four types of individual cellulosic fibers. Wood Fiber Sci 43(4):353–364Google Scholar
  26. 26.
    Eronen P, Österberg M, Jääskeläinen AS (2009) Effect of alkaline treatment on cellulose supramolecular structure studied with combined confocal Raman spectroscopy and atomic force microscopy. Cellulose 16(2):167–178CrossRefGoogle Scholar
  27. 27.
    Chandrasekar M, Ishak MR, Sapuan SM, Leman Z, Jawaid M (2017) A review on the characterisation of natural fibres and their composites after alkali treatment and water absorption. Plast Rubber Compos 46(3):119–136CrossRefGoogle Scholar
  28. 28.
    Chen CJ, Chen G, Li X, Guo H, Wang G (2017) The influence of chemical treatment on the mechanical properties of windmill palm fiber. Cellulose 24(4):1611–1620CrossRefGoogle Scholar
  29. 29.
    Tian G, Chen B, Qi S, Niu H, Han E, Wu D (2016) Enhanced surface free energy of polyimide fibers by alkali treatment and its interfacial adhesion behavior to epoxy resins. Compos Interface 23(2):145–155CrossRefGoogle Scholar
  30. 30.
    Chowdhury MNK, Beg MDH, Khan MR, Mina MF (2013) Modification of oil palm empty fruit bunch fibers by nanoparticle impregnation and alkali treatment. Cellulose 20(3):1477–149CrossRefGoogle Scholar
  31. 31.
    Parameswaran N, Liese W (1976) On the fine structure of bamboo fibres. Wood Sci Technol 10(4):231–246Google Scholar
  32. 32.
    Young RA (1976) Wettability of wood pulp fibers: applicability of methodology. Wood Fiber Sci 8(2):120–128Google Scholar
  33. 33.
    Ouajai S, Shanks RA (2005) Composition, structure and thermal degradation of hemp cellulose after chemical treatments. Polym Degrad Stabil 89(2):327–335CrossRefGoogle Scholar
  34. 34.
    Ishikawa A, Okano T, Sugiyam J (1997) Fine structure and tensile properties of ramie fibres in the crystalline form of cellulose I, II, IIII and IVI. Polymer 38(2):463–468CrossRefGoogle Scholar
  35. 35.
    Kabir MM, Wang H, Lau KT, Cardona F (2013) Effects of chemical treatments on hemp fibre structure. Appl Surf Sci 276:13–23CrossRefGoogle Scholar
  36. 36.
    Zhong T, Oporto SG, Jaczynski J, Jiang C (2015) Nanofibrillated cellulose and copper nanoparticles embedded in polyvinyl alcohol films for antimicrobial applications. BioMed Res Int 2015:1–8Google Scholar
  37. 37.
    Wang H, Li D, Yano H, Abe K (2014) Preparation of tough cellulose II nanofibers with high thermal stability from wood. Cellulose 21(3):1505–1515CrossRefGoogle Scholar

Copyright information

© The Japan Wood Research Society 2018

Authors and Affiliations

  1. 1.College of Furnishings and Industrial Design, Nanjing Forestry UniversityNanjingChina
  2. 2.Zhejiang Forestry AcademyHangzhouChina
  3. 3.International Center for Bamboo and RattanBeijingChina
  4. 4.Composite Materials and Engineering CenterWashington State UniversityPullmanUSA

Personalised recommendations