Solute diffusion into cell walls in solution-impregnated wood under conditioning process II: effect of solution concentration on solute diffusion
- 206 Downloads
- 2 Citations
Abstract
This study focused on solute diffusing into cell walls in solution-impregnated wood during conditioning, process of moderate drying of solvent. To clarify the effect of solution concentration on the diffusion during the conditioning, weight percent gain (WPG) and relative swelling of the wood sample impregnated with an aqueous solution of polyethylene glycol (PEG) polymers at a concentration of 10, 20, 30, 40, or 50 mass% were examined during the conditioning and subsequent drying processes. The relation between the concentration and the relative swelling after all processes, an indicator of the amount of the polymers in cell walls, exhibited a concave-downward curve with a maximum value at 20 mass%. The estimated mass of the polymers in cell walls just before conditioning increased with the concentration. This indicates that the distribution of the polymers changed during conditioning. The estimated mass just before conditioning and the relative swelling after all processes were normalized to the packing ratios of the polymers in cell walls. The ratio after all processes subtracted by that just before conditioning was larger than the ratio just before conditioning, and increased with the concentration up to 20 mass%; after which it decreased. This indicates that the majority of the polymers in cell walls increased during conditioning, and that the amount of the polymers that diffused into cell walls was at the maximum at concentration of 20 mass%. This was explained by two factors: the decrease in the diffusivity into cell walls and in the concentration difference of the polymers between cell walls and cell cavity with the concentration, based on the behavior of WPG during conditioning; and the estimated minimum concentration at which the solution contains the least amount of polymers to fill the cell walls.
Keywords
Impregnated wood Conditioning Relative humidity Solute diffusion Solution concentrationReferences
- 1.Stamm AJ (1964) Dimensional stabilization. Wood and cellulose science. Ronald Press, New York, pp 312–342Google Scholar
- 2.Norimoto M, Grill J (1993) Structure and properties of chemically treated wood. In: Shiraishi N, Kajita H, Norimoto M (eds) Recent research on wood and wood-based materials, current Japanese materials research, vol 11. Elsevier Applied Science, London and New York, pp 135–154CrossRefGoogle Scholar
- 3.Stamm AJ (1956) Dimensional stabilization of wood with carbonwaxes. For Prod J 6:201–204Google Scholar
- 4.Ishimaru Y (1993) PEG To Mokuzai No Hanashi (in Japanese). Mokuzaihozon 19:204–218Google Scholar
- 5.Jeremic D, Cooper P, Heyd D (2007) PEG bulking of wood cell walls as affected by moisture content and nature of solvent. Wood Sci Technol 41:597–606CrossRefGoogle Scholar
- 6.Jeremic D, Cooper P (2009) PEG quantification and examination of molecular weight distribution in wood cell walls. Wood Sci Technol 43:317–329CrossRefGoogle Scholar
- 7.Jeremic D, Quijano-Solis C, Cooper P (2009) Diffusion rate of polyethylene glycol into cell walls of red pine following vacuum impregnation. Cellulose 16:339–348CrossRefGoogle Scholar
- 8.Kitani Y, Ohsawa J, Nakato K (1970) Adsorption of polyethylene glycol on water-swollen wood versus molecular weight (in Japanese). Mokuzai Gakkaishi 16:326–333Google Scholar
- 9.Sadoh T, Hashihira M (1973) A note on the swelling of wood with polyethylene glycols (in Japanese). Bull Kyoto Univ For 45:227–237Google Scholar
- 10.Schneider VA (1969) Contribution on the dimensional stabilization of wood with polyethylene glycol. Part 1: Basic investigation on the dimensional stabilization of wood with polyethylene glycol (in German). Holz Roh Werkst 27:209–224CrossRefGoogle Scholar
- 11.Schneider VA (1970) Contribution on the dimensional stabilization of wood with polyethylene glycol. Part 2: Investigation of changes of wood properties by PEG impregnation and on the effectiveness of various impregnation processes (in German). Holz Roh Werkst 28:20–34CrossRefGoogle Scholar
- 12.Stamm AJ (1959) The dimensional stability of wood. For Prod J 9:375–381Google Scholar
- 13.Stamm AJ (1964) Factors affecting the bulking and dimensional stabilization of wood with polyethylene glycols. For Prod J 14:403–408Google Scholar
- 14.Tarkow H, Feist WC, Southerland CF (1966) Interaction of wood with polymeric materials penetration versus molecular size. For Prod J 16:61–65Google Scholar
- 15.Tanaka S, Seki M, Miki T, Shigematsu I, Kanayama K (2015) Solute diffusion into cell walls in solution-impregnated wood under conditioning process I: effect of relative humidity on solute diffusivity. J Wood Sci 61:543–551CrossRefGoogle Scholar
- 16.Tanaka S, Miki T, Seki M, Shigematsu I, Kanayama K (2015) Mechanism verification of solute diffusion into cell walls in solution impregnated wood under conditioning process: effect of relative humidity on swelling and shrinkage behavior of wood impregnated with an aqueous solution of polyethylene glycol (in Japanese). J Soc Mater Sci Japan 64:369–374CrossRefGoogle Scholar
- 17.Sadoh T (1967) The dimensional changes of wood during polyethylene glycol treatment and some elastic properties of the treated wood. Mokuzai Gakkaishi 13:41–45Google Scholar
- 18.Greenspan L (1977) Humidity fixed points of binary saturated aqueous solutions. J Res Natl Bur Stand Sec A Phys Chem 81A:89–96CrossRefGoogle Scholar
- 19.Society Japan Wood Research (ed) (2010) Mokuzai No Sosei To Seisei, Mokushitsu No Kagaku (in Japanese). Buneido, Tokyo, pp 3–4Google Scholar
- 20.Kollmann F (1951) Physik des Holzes, Technologie des Holzes und der Holzwerkstoffe I (in German). Springer, Berlin, pp 331–333Google Scholar