Fabrication and the electrochemical activation of network-like MnO2 nanoflakes as a flexible and large-area supercapacitor electrode
- 164 Downloads
Porous network-like MnO2 thick films are successfully synthesized on a flexible stainless steel (SS) mesh using a simple and low-cost electrodeposition method followed by an electrochemical activation process. Morphology, chemical composition, and crystal structure of the prepared electrodes before and after the activation process are determined and compared by scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR), and X-ray diffraction (XRD) analyses. The results show that the implementation of the electrochemical activation process does not change the chemical composition and crystal structure of the films, but it influences the surface morphology of the MnO2 thick layer to a flaky nanostructure. Based on the electrochemical data analysis, the maximum specific capacitance of 1400 mF (381 F g−1) and 3700 mF (352 F g−1) are measured for small (2.6 cm2) and large (10 cm2) surface area electrodes, respectively. In addition, a flexible symmetric MnO2//MnO2 solid-state supercapacitor shows a capacitance of 0.3 F with about 98% retention at different bending angles from 0 to 360°.
KeywordsSupercapacitor MnO2 Electrochemical activation Nanostructure Flexible
The authors would like to thank Dr. M. Qorbani for valuable and useful discussions. Financial assistance of Research and Technology Council of Sharif University of Technology and partial support from Iran National Science Foundation through project number 940009 is greatly acknowledged.
- 16.Qorbani M, Chou TC, Lee YH, Samireddi S, Naseri N, Ganguly A, Esfandiar A, Wang CH, Chen LC, Chen KH, Moshfegh AZ (2017) Multi-porous Co3O4 nanoflakes@sponge-like few-layer partially reduced graphene oxide hybrids: towards highly stable asymmetric supercapacitors. J Mater Chem A 5(24):12569–12577CrossRefGoogle Scholar