Influence of accelerated ageing on the physical properties of CAD/CAM restorative materials

  • Thomas NiemEmail author
  • Nivin Youssef
  • Bernd Wöstmann
Original Article
  • 28 Downloads

Abstract

Objectives

This study aims to investigate the influence of thermocycling on the physical properties of different CAD/CAM restorative materials and assess their ability to maintain energy dissipation capacities and damping effects.

Materials and methods

The results of a 3-point bending test were used to calculate flexural strength (FS), modulus of elasticity (ME), modulus of toughness (MT) and elastic recovery (ER) for three ceramic, twelve composite and five polymer-based materials. Specimens (n = 10, 4.0 × 1.5 × 17.0 mm3) were loaded until rupture after water storage (24 h; 37.0 ± 1.0 °C) or thermocycling (5000 cycles; 5–55 °C). Statistical data analysis was performed using parametric statistics (p = 0.05).

Results

Thermocycling had no significant influence on any investigated properties of ceramic materials (p > 0.05). Hybrid composites showed significant differences between water storage and thermocycling (p < 0.05), with the exception of FS of Tetric CAD. Similarly, ME with AMBARINO High-Class, CERASMART, Tetric CAD and Vita Enamic and MT and ER with Paradigm and Tetric CAD were not affected. For polymer-based materials, significant differences were found with the exceptions of FS (PEEK-OPTIMA, Telio CAD), ME (M-PM Disc, PEEK-OPTIMA, Telio CAD, Vita CAD-Temp), MT (Telio CAD) and ER (Telio CAD).

Conclusions

The material properties of composite and polymer-based CAD/CAM materials were susceptible to degradation processes induced by thermocycling. Only Telio CAD and Tetric CAD showed no significant effects like all ceramic materials, thus preserving their inherent ability to elastically and plastically dissipate energy.

Clinical relevance

A careful material selection is advisable when planning CAD/CAM restorations as remarkable differences may exist in the durability of physical characteristics through the impact of water.

Keywords

CAD/CAM material Thermocycling Modulus of toughness Elastic recovery Resiliency Energy dissipation 

Notes

Acknowledgements

The authors thank Antje Hübner for her technical assistance in sample preparation and data acquisition. We also thank Juvora Ltd. for donating PEEK-Optima. In addition, we gratefully acknowledge the support of our biostatistician Dr. Johannes Herrmann.

Funding information

This research did not receive any specific grant from funding agencies in the public, commercial or not-for-profit sectors. No external funding; the study is solely based on the department budgets of the authors.

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

Ethical approval

This article does not contain any studies with human participants or animals performed by any of the authors.

Informed consent

For this type of study, formal consent is not required.

References

  1. 1.
    Zaytsev D, Panfilov P (2014) Deformation behavior of human enamel and dentin-enamel junction under compression. Mater Sci Eng C Mater Biol Appl 34:15–21.  https://doi.org/10.1016/j.msec.2013.10.009/S0928-4931(13)00577-8 CrossRefPubMedGoogle Scholar
  2. 2.
    Kahler B, Swain MV, Moule A (2003) Fracture-toughening mechanisms responsible for differences in work to fracture of hydrated and dehydrated dentine. J Biomech 36:229–237CrossRefGoogle Scholar
  3. 3.
    Jameson MW, Hood JA, Tidmarsh BG (1993) The effects of dehydration and rehydration on some mechanical properties of human dentine. J Biomech 26:1055–1065CrossRefGoogle Scholar
  4. 4.
    Currey JD, Landete-Castillejos T, Estevez J, Ceacero F, Olguin A, Garcia A, Gallego L (2009) The mechanical properties of red deer antler bone when used in fighting. J Exp Biol 212:3985–3993.  https://doi.org/10.1242/jeb.032292 CrossRefPubMedGoogle Scholar
  5. 5.
    Yan J, Daga A, Kumar R, Mecholsky JJ (2008) Fracture toughness and work of fracture of hydrated, dehydrated, and ashed bovine bone. J Biomech 41:1929–1936.  https://doi.org/10.1016/j.jbiomech.2008.03.037 CrossRefPubMedGoogle Scholar
  6. 6.
    Nyman JS, Roy A, Shen X, Acuna RL, Tyler JH, Wang X (2006) The influence of water removal on the strength and toughness of cortical bone. J Biomech 39:931–938CrossRefGoogle Scholar
  7. 7.
    Kruzic JJ, Nalla RK, Kinney JH, Ritchie RO (2003) Crack blunting, crack bridging and resistance-curve fracture mechanics in dentin: effect of hydration. Biomaterials 24:5209–5221CrossRefGoogle Scholar
  8. 8.
    Ferracane JL (2006) Hygroscopic and hydrolytic effects in dental polymer networks. Dent Mater 22:211–222CrossRefGoogle Scholar
  9. 9.
    Ferracane JL, Marker VA (1992) Solvent degradation and reduced fracture toughness in aged composites. J Dent Res 71:13–19CrossRefGoogle Scholar
  10. 10.
    van Groeningen G, Jongebloed W, Arends J (1986) Composite degradation in vivo. Dent Mater 2:225–227CrossRefGoogle Scholar
  11. 11.
    Lohbauer U, Frankenberger R, Kramer N, Petschelt A (2003) Time-dependent strength and fatigue resistance of dental direct restorative materials. J Mater Sci Mater Med 14:1047–1053CrossRefGoogle Scholar
  12. 12.
    Lohbauer U, Belli R, Ferracane JL (2013) Factors involved in mechanical fatigue degradation of dental resin composites. J Dent Res 92:584–591CrossRefGoogle Scholar
  13. 13.
    Hampe R, Lumkemann N, Sener B, Stawarczyk B (2018) The effect of artificial aging on Martens hardness and indentation modulus of different dental CAD/CAM restorative materials. J Mech Behav Biomed Mater 86:191–198CrossRefGoogle Scholar
  14. 14.
    Al-Harbi FA, Ayad NM, ArRejaie AS, Bahgat HA, Baba NZ (2017) Effect of aging regimens on resin nanoceramic chairside CAD/CAM material. J Prosthodont 26:432–439CrossRefGoogle Scholar
  15. 15.
    Sonmez N, Gultekin P, Turp V, Akgungor G, Sen D, Mijiritsky E (2018) Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: a comparative in vitro study. BMC Oral Health 18:5CrossRefGoogle Scholar
  16. 16.
    Egilmez F, Ergun G, Cekic-Nagas I, Vallittu PK, Lassila LVJ (2018) Does artificial aging affect mechanical properties of CAD/CAM composite materials. J Prosthodont Res 62:65–74CrossRefGoogle Scholar
  17. 17.
    Tsujimoto A, Barkmeier WW, Takamizawa T, Latta MA, Miyazaki M (2017) Influence of thermal cycling on flexural properties and simulated wear of computer-aided design/computer-aided manufacturing resin composites. Oper Dent 42:101–110CrossRefGoogle Scholar
  18. 18.
    Lauvahutanon S, Takahashi H, Shiozawa M, Iwasaki N, Asakawa Y, Oki M, Finger WJ, Arksornnukit M (2014) Mechanical properties of composite resin blocks for CAD/CAM. Dent Mater J 33:705–710CrossRefGoogle Scholar
  19. 19.
    Blackburn C, Rask H, Awada A (2018) Mechanical properties of resin-ceramic CAD-CAM materials after accelerated aging. J Prosthet Dent 119:954–958CrossRefGoogle Scholar
  20. 20.
    Porto T, Roperto R, Campos E, Porto-Neto S, Teich S (2016) Behavior of CAD/CAM materials after long thermocycling process. Dent Mater 32S:e33CrossRefGoogle Scholar
  21. 21.
    Porto TS, Roperto RC, Akkus A, Akkus O, Teich S, Faddoul FF, Porto-Neto ST, Campos EA (2018) Effect of thermal cycling on fracture toughness of CAD/CAM materials. Am J Dent 31:205–210PubMedGoogle Scholar
  22. 22.
    Okada R, Asakura M, Ando A, Kumano H, Ban S, Kawai T, Takebe J (2018) Fracture strength testing of crowns made of CAD/CAM composite resins. J Prosthodont Res 62:287–292CrossRefGoogle Scholar
  23. 23.
    Beer FP, Johnston ER, DeWolf JT, Mazurek DF (2015) Mechanics of materials. McGraw-Hill Inc., New York, p 759Google Scholar
  24. 24.
    Dyer SR, Lassila LV, Jokinen M, Vallittu PK (2005) Effect of cross-sectional design on the modulus of elasticity and toughness of fiber-reinforced composite materials. J Prosthet Dent 94:219–226CrossRefGoogle Scholar
  25. 25.
    Smith ER, Allen MR (2013) Bisphosphonate-induced reductions in rat femoral bone energy absorption and toughness are testing rate-dependent. J Orthop Res 31:1317–1322CrossRefGoogle Scholar
  26. 26.
    Niem T, Youssef N, Wostmann B (2019) Energy dissipation capacities of CAD-CAM restorative materials: a comparative evaluation of resilience and toughness. J Prosthet Dent 121:101–109CrossRefGoogle Scholar
  27. 27.
    Shackelford JF (2015) Introduction to materials science for engineers. Pearson Education Inc., New York, p 168Google Scholar
  28. 28.
    Anusavice KJ (2003) Mechanical properties of dental materials. In: Anusavice KJ (ed) Phillips’ science of dental materials. WB Saunders Company, St. Louis, pp 73–101Google Scholar
  29. 29.
    Williams JG (2001) Fracture mechanics testing methods for polymers, adhesives and composites. Elsevier Science Ltd., AmsterdamGoogle Scholar
  30. 30.
    Grellmann W (2001) New developments in toughness evaluation of polymers and compounds by fracture machanics. In: Grellmann W, Seidler S (eds) Deformation and fracture behaviour of polymers. Springer, New York, pp 3–26CrossRefGoogle Scholar
  31. 31.
    Cesar PF, Della Bona A, Scherrer SS, Tholey M, van Noort R, Vichi A, Kelly R, Lohbauer U (2017) ADM guidance-ceramics: fracture toughness testing and method selection. Dent Mater 33:575–584CrossRefGoogle Scholar
  32. 32.
    Smith RL, Mecholsky JJ, Freiman SW (2009) Estimation of fracture energy from the work of fracture and fracture surface area: I. Stable crack growth. Int J Fract 156:97–102.  https://doi.org/10.1007/s10704-009-9350-7 CrossRefGoogle Scholar
  33. 33.
    ISO (2015) ISO 6872, Dentistry—ceramic materials. International Organization for Standardization, GenevaGoogle Scholar
  34. 34.
    ASTM (2017) D790-17:2017, Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials. West Conshohocken, PAGoogle Scholar
  35. 35.
    ISO (2013) ISO 9513, Metallic materials—calibration of extensometer systems used in uniaxial testing. International Organization for Standardization, GenevaGoogle Scholar
  36. 36.
    Daemi H, Rajabi-Zeleti S, Sardon H, Barikani M, Khademhosseini A, Baharvand H (2016) A robust super-tough biodegradable elastomer engineered by supramolecular ionic interactions. Biomaterials 84:54–63.  https://doi.org/10.1016/j.biomaterials.2016.01.025/S0142-9612(16)00033-8 [pii]CrossRefPubMedGoogle Scholar
  37. 37.
    Kaizer MR, Almeida JR, Goncalves APR, Zhang Y, Cava SS, Moraes RR (2016) Silica coating of nonsilicate nanoparticles for resin-based composite materials. J Dent Res 95:1394–1400.  https://doi.org/10.1177/0022034516662022 CrossRefPubMedPubMedCentralGoogle Scholar
  38. 38.
    Lopez-Suevos F, Dickens SH (2008) Degree of cure and fracture properties of experimental acid-resin modified composites under wet and dry conditions. Dent Mater 24:778–785.  https://doi.org/10.1016/j.dental.2007.09.006 CrossRefPubMedGoogle Scholar
  39. 39.
    Awada A, Nathanson D (2015) Mechanical properties of resin-ceramic CAD/CAM restorative materials. J Prosthet Dent 114:587–593.  https://doi.org/10.1016/j.prosdent.2015.04.016/S0022-3913(15)00255-3 CrossRefPubMedGoogle Scholar
  40. 40.
    Tjandrawinata R, Irie M, Suzuki K (2005) Flexural properties of eight flowable light-cured restorative materials, in immediate vs 24-hour water storage. Oper Dent 30:239–249PubMedGoogle Scholar
  41. 41.
    Prakki A, Pereira PN, Kalachandra S (2009) Effect of propionaldehyde or 2,3-butanedione additives on the mechanical properties of Bis-GMA analog-based composites. Dent Mater 25:26–32.  https://doi.org/10.1016/j.dental.2008.05.002 CrossRefPubMedGoogle Scholar
  42. 42.
    Peutzfeldt A, Asmussen E (1992) Modulus of resilience as predictor for clinical wear of restorative resins. Dent Mater 8:146–148CrossRefGoogle Scholar
  43. 43.
    Lakens D (2013) Calculating and reporting effect sizes to facilitate cumulative science: a practical primer for t-tests and ANOVAs. Front Psychol 4Google Scholar
  44. 44.
    Kausch HH, Gensler R, Grein C, Plummer CJG, Scaramuzzino P (1999) Crazing in semicrystalline thermoplastics. J Macromol Sci Phys B 38:803–815.  https://doi.org/10.1080/00222349908248140 CrossRefGoogle Scholar
  45. 45.
    Cohen J (1988) Statistical power analysis for the behavioral sciences. Lawrence Erlbaum Associates, New YorkGoogle Scholar
  46. 46.
    Chen PY, Lin AY, Lin YS, Seki Y, Stokes AG, Peyras J, Olevsky EA, Meyers MA, McKittrick J (2008) Structure and mechanical properties of selected biological materials. J Mech Behav Biomed Mater 1:208–226.  https://doi.org/10.1016/j.jmbbm.2008.02.003 CrossRefPubMedGoogle Scholar
  47. 47.
    Winwood K, Zioupos P, Currey JD, Cotton JR, Taylor M (2006) The importance of the elastic and plastic components of strain in tensile and compressive fatigue of human cortical bone in relation to orthopaedic biomechanics. J Musculoskelet Neuronal Interact 6:134–141PubMedGoogle Scholar
  48. 48.
    Bijjargi S, Chowdhary R (2013) Stress dissipation in the bone through various crown materials of dental implant restoration: a 2-D finite element analysis. J Investig Clin Dent 4:172–177.  https://doi.org/10.1111/j.2041-1626.2012.00149.x CrossRefPubMedGoogle Scholar
  49. 49.
    Lauvahutanon S, Shiozawa M, Takahashi H, Iwasaki N, Oki M, Finger WJ, Arksornnukit M (2017) Discoloration of various CAD/CAM blocks after immersion in coffee. Restor Dent Endod 42:9–18CrossRefGoogle Scholar
  50. 50.
    Ferracane JL, Berge HX, Condon JR (1998) In vitro aging of dental composites in water—effect of degree of conversion, filler volume, and filler/matrix coupling. J Biomed Mater Res 42:465–472CrossRefGoogle Scholar
  51. 51.
    Ferracane JL, Condon JR (1991) Degradation of composites caused by accelerated aging. J Dent Res 70(Spec Iss 1):480. www.iadr.org Google Scholar
  52. 52.
    Stawarczyk B, Ender A, Trottmann A, Ozcan M, Fischer J, Hammerle CH (2012) Load-bearing capacity of CAD/CAM milled polymeric three-unit fixed dental prostheses: effect of aging regimens. Clin Oral Investig 16:1669–1677.  https://doi.org/10.1007/s00784-011-0670-4 CrossRefPubMedGoogle Scholar
  53. 53.
    Edelhoff D, Schraml D, Eichberger M, Stawarczyk B (2016) Comparison of fracture loads of CAD/CAM and conventionally fabricated temporary fixed dental prostheses after different aging regimens. Int J Comput Dent 19:101–112PubMedGoogle Scholar
  54. 54.
    Wimmer T, Ender A, Roos M, Stawarczyk B (2013) Fracture load of milled polymeric fixed dental prostheses as a function of connector cross-sectional areas. J Prosthet Dent 110:288–295CrossRefGoogle Scholar
  55. 55.
    Mohsen NM, Craig RG, Filisko FE (2001) The effects of moisture on the dielectric relaxation of urethane dimethacrylate polymer and composites. J Oral Rehabil 28:376–392CrossRefGoogle Scholar
  56. 56.
    Soderholm KJ (1981) Degradation of glass filler in experimental composites. J Dent Res 60:1867–1875CrossRefGoogle Scholar
  57. 57.
    Schrader ME, Block A (1971) Tracer study of kinetics and mechanism of hydrolytically induced interfacial failure. J Polym Sci Part C Polymer Symposium:281–291Google Scholar
  58. 58.
    Ishida H, Miller JD (1984) Substrate effects on the chemisorbed and physisorbed layers of methacryl silane modified particulate minerals. Macromolecules 17:1659–1666.  https://doi.org/10.1021/ma00139a004 CrossRefGoogle Scholar
  59. 59.
    Plueddemann EP (1970) Adhesion through silane coupling agents. J Adhes 2:184–201.  https://doi.org/10.1080/0021846708544592 CrossRefGoogle Scholar
  60. 60.
    Ivoclar Vivadent (2018) Tetric CAD: scientific documentation. Ivoclar Vivadent AG, Schaan. http://www.ivoclarvivadent.com/en/download-center/scientific-documentations. Accessed Jul 2018
  61. 61.
    Ivoclar Vivadent (2010) Telio CAD: scientific documentation. Ivoclar Vivadent AG, Schaan. http://www.ivoclarvivadent.com/en/download-center/scientific-documentations. Accessed 2010
  62. 62.
    VITA Zahnfabrik (2019) VITA ENAMIC: technical and scientific documentation. VITA Zahnfabrik H. Rauter GmbH & Co. KG, Bad Säckingen. https://mam.vita-zahnfabrik.com/portal/ecms_mdb_download.php?id=82333&sprache=en&fallback=&rechtsraum=&cls_session_id=&neuste_version=1. Accessed Feb 2019

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Dental Clinic - Department of ProsthodonticsJustus-Liebig-UniversityGiessenGermany

Personalised recommendations