A Study On Energy Absorption of Aluminium Foam

  • Krešimir Grilec
  • Gojko Marić
  • Suzana Jakovljević
Originalarbeit
  • 173 Downloads

Summary

Foamed materials in general, and aluminium foams in particular, demonstrate a number of interesting properties due to their porous structure, which makes them usable in a wide range of applications. The capability of absorbing the impact energy is one of the most interesting properties of foams. This paper studies the influence of chemical composition, density and shape of aluminium foams on energy absorption. Samples of aluminium foam were produced from an "Alulight" precursor. The ability of samples to absorb mechanical energy was estimated from the results of compression tests. Tests were carried out by a universal test machine. During tests, the sample "force–elongation" diagram was written down. Test results showed that aluminium foams have good energy absorption and the capability of absorption decreases with the density of foam. Alulight AlMgSi 0.6 TiH2-0.4 foam can absorb more energy than Alulight AlSi 10 TiH2-0.8 foam.

Summary

Schaumstoffe im Allgemeinen und Aluminiumschäume im Besonderen zeigen zahlreiche interessante Eigenschaften wegen ihrer porösen Struktur und haben breite Anwendungen. Das Energieabsorptionsvermögen gehört zu den interessantesten Eigenschaften des Schaumes. In der vorliegenden Arbeit wurde der Einfluss der chemischen Zusammensetzung, der Dichte und der Form von Aluminiumschaum auf die Energieabsorption untersucht. Die Probestücke wurden durch das "Alulight"-Verfahren hergestellt. Das Energieabsorptionsvermögen der Probestücke wurde durch die Ergebnisse der Druckfestigkeitsprüfung abgeschätzt. Die Prüfungen wurden mit Hilfe der universellen Prüfmaschine durchgeführt. Bei der Druckfestigkeitsprüfung wurde das Spannungs-Dehnungs-Diagramm erhalten. Die Ergebnisse zeigten, dass die Aluminiumschäume ein gutes Energieabsorptionsvermögen haben. Das Energieabsorptionsvermögen nimmt mit der Schaumdichte ab. Der Alulight AlMgSi 0.6 TiH2-0.4-Schaum kann mehr Energie als der Alulight AlSi 10 TiH2-0.8-Schaum absorbieren.

Keywords

Foam Energy Absorption Impact Energy Aluminium Foam Foam Material 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Untersuchung der Energieabsorption von Aluminiumschaum

This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. Simancik, F., H.P. Degischer and H. Wörz: Foamed Aluminium - Light Structural and Insulation Material. Euromat '95, Venice/Padua, Italy, 25.– 28.09.1995., Associazione Italiana di Metallurgia, Milan, 1995Google Scholar
  3. Degischer, H.P., and B. Kriszt: Handbook of Cellular Metals: Productions, Processing, Applications. Wiley-VCH, 2002Google Scholar
  4. Yu, C.J., H.H. Eifert, J. Banhart and J. Baumeister: Metal Foaming by a Powder Metallurgy Method: Production, Properties and Applications. Materials Research Innovations (1998) 2: 181–188CrossRefGoogle Scholar
  5. Baumeister, J., J. Banhart and M. Weber: Aluminium Foams for Transport Industry. Materials & Design (1997) 18(4/6), 217–220Google Scholar

Copyright information

© Springer-Verlag 2010

Authors and Affiliations

  • Krešimir Grilec
    • 1
  • Gojko Marić
    • 1
  • Suzana Jakovljević
    • 1
  1. 1.Faculty of Mechanical Engineering and Naval ArchitectureZagrebCroatia

Personalised recommendations