Rheological properties of polyethylene/metaboric acid thermoplastic blends
- 229 Downloads
The rheological properties of molten low-density polyethylene/metaboric acid blends were studied. It was found that the blend behavior can be rather different, depending on volume fraction of the inorganic component. Specifically, at some concentration of metaboric acid, the dynamic moduli and the Newtonian viscosity of the blends demonstrate a jump-like change. The concentration threshold depends on temperature and equals to 21.9 and 14.1 vol %, at 150 and 180 ∘C, respectively. In the concentration range below the threshold, the gain in the content of inorganic component results in an enhancement of the blend dynamic moduli and viscosity, without changing the general character of the rheological behavior of composition in the region of linear response. On the other hand, at higher concentrations of metaboric acid, the yield stress is observed, and the elastic modulus in the linear region of mechanical behavior becomes virtually independent of frequency. It was suggested that the rheological behavior of blends is related to a spontaneous change in their structure as well as planar molecular structure of the inorganic component.
KeywordsPolymer blend Viscoelasticity Shear viscosity Yielding Percolation
The authors thank T.N. Filippova for measurement of swell degree of the melt jets of the blends. This work was supported by the Russian Foundation for Basic Research (grants no. 13–03–00725 A and 14–03–00538 A).
- Adalja BSB, Otaigbe JU, Thalacker J (2007) Glass-polymer melt hybrids. I: viscoelastic properties of novel affordable organic-inorganic polymer hybrids. Polym Eng Sci 47:1055–1067Google Scholar
- Barnes HA (2003) A review of the rheology of filled viscoelastic systems. Rheol Rev: 1–36Google Scholar
- Brazhkin VV, Katayama Y, Inamura Y, Kondrin MV, Lyapin AG, Popova SV, Voloshin RN (2003) Structural transformations in liquid, crystalline and glassy B 2 O 3 under high pressure. JETP Lett 78:845–849Google Scholar
- Hodge IM (1994) Enthalpy relaxation and recovery in amorphous materials. J Non-Cryst Solids 169:211–266Google Scholar
- Kracek FC, Morey GW, Merwin HE (1938) The system, water-boron oxide. Am J Sci A 35:143–171Google Scholar
- Landolt-Börnstein (1999) Thermodynamic properties of inorganic materials: pure substances. Part 1. Springer, Berlin HeidelbergGoogle Scholar
- Malkin A, Isayev AI (2012) Rheology: concepts, methods, and applications, 2nd ed. ChemTec Publ, TorontoGoogle Scholar
- Otaigbe JU (1996) Relationship of polymer engineering with glass technology. Trends Polym Sci 4:70–74Google Scholar
- Otaigbe JU, Beall GH (1997) Inorganic phosphate glasses as polymers: a review. Trends in Polym Sci 5:369–379Google Scholar
- Shaulov AYu, Berlin AA (2012) Low-softening inorganic polyoxides as polymer components of materials. Recent Res Devel Polym Sci Ser A 11:21–76Google Scholar