Dependence of an electric capacitance on the constant voltage C = f(U) in pure bentonite, composites and semiconductors
- 76 Downloads
Abstract
The present paper is devoted to studying the effect of dc voltage on the amount of electrical capacitance in pure bentonite, composites and semiconductors with different conductivity, as well as the dependence of electrical conductivity on the external field. The reason for the dependence of the capacitance on the DC voltage may be the presence of potential barriers in them and the dependence of the electrical conductivity (σ) on the applied voltage. In those samples where there is a large range of variation of σ, there are also large changes in electrical capacitance. The principle of a change in electrical conductivity, a change in the electrical capacitance is observed, can be successfully used in microelectronics, electrical engineering, etc. Created capacities parameters can changed in a wide range of voltage and temperature.
1 Introduction
The effect of “negative capacitance” is observed in different semiconductors: in diodes with a Schottky barrier NiSi2 ~ n-Si [1], NiSi2—n-Si, Pd-n-Si, Pd-n-GaAs [2], WNx-n-GaAs [3], and Al-n-GaAs [4]. In the structure of the metal–dielectric–metal type, “negative capacitance” is observed at relatively high electric fields. The mechanism of the “negative capacity” of various composites is different and, in general, not well understood. However, in [4, 5], it is noted that the emergence of a “negative capacitance” is associated with a change in current when a step of constant or alternating voltage is applied. Studies of the dependence C = f(U) are also not proposed in the literature in the proposed scale. The dependence of electric capacity on a constant voltage C = f(U) is noted in [6, 7, 8]. Capacity growth with an increase in the constant voltage is associated with an increase in the number of domains moments, which are oriented in the direction of the electric field. At large values of the electric field, the domains “heal” (as the authors put it) for this reason, the capacitance decreases with increasing field strength. Islet metal films have a high low-frequency effective dielectric constant (ε = 107 ÷ 108) [7], and it is a positive value. The conductivity of island metal films increases under the influence of an external electric field (anomalous conductivity effect) [5]. Since the dielectric constant of conducting systems is largely determined by their conductivity, the dielectric constant of island films must change with the change of the electric field. At the same time, with an increase in conductivity (with an increase in the electric field), the positive part of the effective dielectric constant of metallic films should decrease, and the negative part should increase in absolute value.
2 Materials and methods
To identify the mechanisms of the influence of constant voltage on the electrical capacity of materials, pure polymer films (polyethylene, propylene, polyvinylidene fluoride), composites based on polyethylene and silicon, composites based on bentonite and magnetic microparticles (refined siderite) and montmorillonite clay (bentonite), semiconductors with various thickness and conductivity, n-Ge, n-İnAs, n-Si, p-Si were investigated. The bentonite of the Dash-Salakhlinskoye field (Azerbaijan) was modified in a certain amount at turnover, 6000 rpm for 30 min, and the ferrite particles were modified in two modes: 6000 rpm (M1) and 3000 rpm (M2) for 10 min in a planetary mill type FRITSCH. Then, by mixing the powders of the components, discs of a size were compressed: length 16 mm, diameter 7 mm. Composites consist of 50% M1 + 50% (unmodified bentonite, NB) and 50% M1 + 50% (modified bentonite, MB). The thickness of the composites was equal to 180 mm. Samples were in the form of discs (washers) with a thickness of 1.5 mm and a diameter of 7 mm. The disks were pressed without heating at room temperature under a pressure of 1 GPa. To study the electrophysical characteristics, measuring electrodes made of silver paste were applied to both ends of the pressed discs.
The dependences of capacitance and electrical conductivity on constant voltage for all samples at room temperature (T = 293 K) were investigated.
3 Results and discussion
It can be seen from formula (2) that the C/C_{0} ratio depends on the U/U_{0} ratio, namely, at U ≤ 4U_{0}, capacity begins to increase, and at U > 4U_{0}, capacity decreases. Using formula (1), we carried out a theoretical calculation of the dependence of the capacitance on the magnitude of the external field. In this case, the ratio U/U_{0} at U ≤ 4U_{0} and U > 4U_{0} is considered.
The presence of potential wells in them (U/U_{0} ratio), as well as the dependence of electrical conductivity on a constant voltage, plays an important role in changing the electrical capacitance of media.
Change of an electric capacitance and electrical conductivity of the samples (in percent)
Name of sample | Changing of C и σ | |
---|---|---|
C, pF (%) | σ, Oм^{−1}cм^{−1} (%) | |
Pure dielectric film | 0.14 | 0.17 |
Pure bentonite | 5.5 | 6 |
Composite based on 60% unmodified bentonite and 40% magnetic particles (6000 rpm) M1 | 4.5 | 6 |
Composite based on 60% modified bentonite and 40% magnetic particles (6000 rpm) M1 | 33 | 38 |
Composite based on 60% unmodified bentonite and 40% magnetic particles (3000 rpm) M2 | 50 | 55 |
p-Si | 17 | 20 |
n-Ge | 60 | 65 |
A decrease in the capacitance in the same samples with an increase in the constant voltage also qualitatively agrees with the theoretical calculations of the capacitance using formula (1) (Fig. 8a, region 2). In other words, the condition U ≥ 4U_{0} is satisfied in this area.
It should be emphasized that a change in the electric field can strongly influence the magnitude and sign of the electric capacitance. With an increase in the electric field, the height of the potential barrier decreases, as a result of which the number of charge carriers increases and thereby increases the value of electrical conductivity (σ ~ n) [9, 10]. Since the electric capacitance is directly proportional to the dielectric constant (C ~ ε), the electric field indirectly affects the magnitude and sign of the electric capacitance. In those samples (structures) where there is a large range of variation of σ, there are also large changes in electrical capacitance (see Table 1). Regardless of the nature and production in the samples studied, the dependence of the electric capacitance on the magnitude of the constant voltage was found. The reason for the dependence of the capacitance on the DC voltage may be the presence of potential barriers in them and the dependence of the electrical conductivity (σ) on the applied voltage.
4 Conclusions
The data obtained allow us to conclude that the electric capacitance is indirectly dependent on the electrical conductivity, with a large change in electrical conductivity, a change in the electrical capacitance is observed. This principle can be successfully used in microelectronics, electrical engineering, etc. Capacities can be created, resistance parameters, which can be changed in a wide range of voltage and temperature.
Notes
References
- 1.V.B. Bondarenko, Y.A. Kudinov, S.E. Ershov, V.V. Korablev, Natural heterogeneity of Schottky barrier height. FTP 32(5), 554 (1998)Google Scholar
- 2.O.P. Sinha, Effect of 100 MeV Si7+ ions’ irradiation on Pd/n-GaAs Schottky diodes. Radiat. Eff. Defects Solids 172, 975 (2017)ADSCrossRefGoogle Scholar
- 3.K. Steiner, H. Mikami, K. Nishihori, M. Nagaoka, N. Uchitomi, WNX–Schottky diodes on semiconductor–insulator–semiconductor-like n-GaAs/undoped-AlGaAs/n-GaAs heterostructures. J. Vac. Sci. Technol. B Microelectron. Nanometer Struct. Process. Meas. Phenom. 9, 1601 (1998)ADSCrossRefGoogle Scholar
- 4.J.S. Lee, C.S. Park, J.W. Yang, J.Y. Kang, D.S. Ma, Properties of WNx films and WNx/GaAs Schottky diodes prepared by ion beam assisted deposition technique. J. Appl. Phys. 67, 1134 (1998)ADSCrossRefGoogle Scholar
- 5.M. Krasilshchikov, B. Smirnov, A. Shalaeva, The effect of DC voltage on the parameters of ceramic capacitors. Electronics 2, 76 (2012)Google Scholar
- 6.M. Krasilshchikov, B. Smirnov, A. Shalaeva, Ceramic low-pass low-pass filter. Electronics 8, 22 (2009)Google Scholar
- 7.M. Krasilshchikov, B. Smirnov, A. Shalaeva, New ceramic noise canceling capacitors. Compon. Technol. 7, 60 (2010)Google Scholar
- 8.I.G. Pashayev, Studying the properties of silicon contacts with a Schottky barrier made on the basis of amorphous and polycrystalline various metal alloys. Uspekhi Fiz. Met. 13, 397–416 (2012)CrossRefGoogle Scholar
- 9.I. Pashayev, T.V. Creetskaia, Preparation of multilayer metallic coatings on silicon surfaces, their properties and applications. Metallurgia 2, 127 (2014)Google Scholar
- 10.P.T. Oreshkin, in Physics of semiconductors and dielectrics/M (Higher School, 1977), p. 444Google Scholar
- 11.I.G. Pashaev, T.V. Kritskaya, Obtaining multilayer metal coatings on a silicon surface, their properties and application. Metallurgiya 2(32), 127–134 (2014)Google Scholar
Copyright information
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.