Biotransformation of lanthanum by Aspergillus niger
- 249 Downloads
Lanthanum is an important rare earth element and has many applications in modern electronics and catalyst manufacturing. However, there exist several obstacles in the recovery and cycling of this element due to a low average grade in exploitable deposits and low recovery rates by energy-intensive extraction procedures. In this work, a novel method to transform and recover La has been proposed using the geoactive properties of Aspergillus niger. La-containing crystals were formed and collected after A. niger was grown on Czapek-Dox agar medium amended with LaCl3. Energy-dispersive X-ray analysis (EDXA) showed the crystals contained C, O, and La; scanning electron microscopy revealed that the crystals were of a tabular structure with terraced surfaces. X-ray diffraction identified the mineral phase of the sample as La2(C2O4)3·10H2O. Thermogravimetric analysis transformed the oxalate crystals into La2O3 with the kinetics of thermal decomposition corresponding well with theoretical calculations. Geochemical modelling further confirmed that the crystals were lanthanum decahydrate and identified optimal conditions for their precipitation. To quantify crystal production, biomass-free fungal culture supernatants were used to precipitate La. The results showed that the precipitated lanthanum decahydrate achieved optimal yields when the concentration of La was above 15 mM and that 100% La was removed from the system at 5 mM La. Our findings provide a new aspect in the biotransformation and biorecovery of rare earth elements from solution using biomass-free fungal culture systems.
KeywordsRare earth elements Lanthanum Aspergillus niger Biotransformation Biorecovery
Rare earth elements (REE) are vital to the world’s fastest growing markets including renewable energy, electric vehicles, telecommunication and defence technologies and the demand for them has risen year on year (Goodenough et al. 2018). Lanthanum is moderately abundant in the Earth’s crust and represents a group of REE that include 14 lanthanides that have multiple industrial applications such as additives in the production of high-performance alloys and as catalysts in glass and ceramics manufacturing and in the refinement of crude oil (Kilbourn 1987; Tyler 2004; Massari and Ruberti 2013). Lanthanum oxide (La2O3) is an important material in microelectronics as it exhibits the best electrical properties in metal oxide semiconductor field effect transistors and could be the ideal substitute for SiO2 in CMOS integrated circuits (Leskelä and Ritala 2003; Kakushima et al. 2007). Another potential application in environmental technology is that it can be used as a highly efficient absorbent for the removal of phosphorus from polluted water (Zhang et al. 2011; Xie et al. 2015). REE primarily occur in associated minerals that are scattered among other mineral-containing ores, meaning that mining can be costly and ineffective due to a lack of economically exploitable deposits worldwide, with the average grade of REE-containing ores being usually less than 10% (Humphries 2010). Traditional physico-chemical methods involve multiple steps of leaching with a combination of hazardous chemicals, e.g. nitric acid and butyl phosphonate, with a huge amount of energy consumption only achieving a recovery rate of approximately 1% (Preston et al. 1996). This is very low when compared with other industrially important elements such as platinum group metals (PGMs) where average recovery rates can amount to 96% or even higher (Patel and Dawson 2015). Therefore, new approaches for the recovery of REE from mines, leachates and waste materials need to be proposed, which could, if adopted for commercial use, greatly alleviate the shortage of supplies of these metals.
Through the mechanism of biologically induced mineralization (BIM) (Gadd 2010), whereby organisms create favourable conditions for extracellular chemical precipitation of mineral phases by modifying their extracellular microenvironment, metal-containing compounds can be formed. Aspergillus niger is a common soil fungus and an important industrial microorganism for the production of citric acid (Currie 1917; Kubicek and Rohr 1985; Mattey 1992; Papagianni 2007). It is also noted for producing various other organic acids including gluconic and oxalic acids, and all these can have a huge role in geomicrobial transformations of minerals and metal speciation (Gadd 1999; Gadd et al. 2014). The application of oxalic acid is an effective means by which certain metals can be precipitated in the form of insoluble metal oxalates of general formula Mx(C2O4)y·zH2O. Bioprecipitation of metals mediated by oxalic acid-producing fungi, such as A. niger, can provide a potentially useful mechanism for metal biorecovery from solution (Ilyas et al. 2017; Liang and Gadd 2017). The recovery of elements is an indispensable step in the bioleaching process for both REE-bearing ores and waste materials (Ilyas et al. 2017). Some approaches to recovering REE from La-containing ores and electronic wastes by involving microbial participation have also been reported, e.g. bioleaching, bioaccumulation and biosorption (Ismail et al. 2015; Ayora et al. 2016; Park et al. 2016). Some previous studies have shown that REE can be mobilized from solid materials such as spent catalysts and luminescent powder from cathode ray tubes by sulphur-oxidizing bacteria, such as Acidithiobacillus ferrooxidans, A. thiooxidans and Leptospirillum ferrooxidans (Barmettler et al. 2016). In a separate study, 50% of the total REE was released from spent fluid catalytic cracking catalyst by 4-day-old cell-free supernatant of Gluconobacter oxydans, indicating that organic acid-producing microorganisms can effectively induce bioleaching and improve the recovery of REE from waste materials (Reed et al. 2016). Hopfe et al. (2017) discovered that significant amounts of REE were leached from lanthanide-containing fluorescent phosphor material using both a biomass-free supernatant and living culture of a mixture of yeasts and acetic acid bacteria. Some preliminary research has reported the dissolution of commercial lanthanide oxides (Schwartz and Näveke 1980), by different strains of A. niger, which confirmed the accessibility of lanthanides to Aspergillus species. Supernatants of cultures of A. niger, A. ficuum and A. terreus have been used by some researchers to study bioleaching of REE from natural sources, such as carbonaceous shales, monazite sand, red mud and Th–U concentrate (Hassanien et al. 2013; Amin et al. 2014; Qu et al. 2015; Brisson et al. 2016; Desouky et al. 2016; Keekan and Jalondhara 2017). REE in ores can be recovered as oxides through several steps including acid leaching, filtration, precipitation using oxalic acid and calcination, and this has been in practice as a part of the recovery process for some minerals such as bastnasite and monazite (Sinha et al. 2016). Despite fungi exhibiting a significant role in biogeochemical cycles for metals and metalloids (Gadd 2007), few studies have clarified interactions of fungal species with REE. Therefore, more information on the mechanisms and conditions effecting the biotransformation of REE is clearly needed. The present study examines the bioprecipitation of lanthanum oxalate by A. niger and adds new knowledge about the microbial biotransformation of lanthanides.
Materials and methods
Microorganism and media
The fungal strain used in this study was Aspergillus niger (ATCC 1015), which was routinely maintained in Petri dishes containing commercial malt extract agar (MEA) (Lab M Limited, Bury, Lancashire, UK) at 25 °C in the dark. Modified Czapek-Dox medium (MCD) contained the following substances (l−1 Milli-Q H2O): glucose 30 g, NaNO3 3 g, Na2HPO4 1 g, MgSO4·7H2O 0.5 g, KCl 0.5 g and FeSO4·7H2O 0.01 g. Where required, 15 g of agar no. 1 (Lab M, Bury, UK) was added to make solid agar medium. The final pH of MCD medium was adjusted to pH 5.5 using 1 M HCl/NaOH prior to autoclaving for 15 min at 115 °C. To achieve higher oxalate precipitation yields, nitrate (NO3−) was used as the nitrogen source in modified AP1 medium, composed of the following (l−1 Milli-Q H2O): NaNO3 3 g, KH2PO4 0.5 g, MgSO4·7H2O 0.2 g, CaCl2·6H2O 0.05 g, NaCl 0.1 g, FeCl3·6H2O 0.0025 g, trace metals (ZnSO4·7H2O 0.004 g, MnSO4·4H2O 0.004 g and CuSO4·5H2O 0.0004 g) and glucose 20 g. The medium was adjusted to pH 5.5 using 1 M HCl/NaOH prior to sterilization at 115 °C for 15 min. For preparation of solid plates, 15 g of agar no. 1 was applied to 1000 ml of medium.
Lanthanum chloride heptahydrate (99.9%) (Sigma-Aldrich, St Louis, MO, USA) was used as the La source in experiments using solid agar plates. A 500-mM LaCl3 stock solution was prepared and sterilized through a Minisart Syringe Filter (pore size 0.2 μm) (Sartorius Lab Instruments GmbH & Co., Goettingen, Germany) before use. Each Petri dish contained 25-ml La-spiked medium, which was prepared by pipetting appropriate amounts of the La stock solution into the nutrient agar when cooled to 55 °C after autoclaving at 115 °C. The surface pH of the plates was measured using a flat-tipped pH probe (VWR International, Lutterworth, England, UK). A 90-mm-diameter cellophane membrane (Focus Packaging and Design Ltd., Louth, UK), which was treated by washing with Milli-Q water and autoclaving at least three times in Milli-Q water at 121 °C for 15 min, was placed on top of the agar surface to separate the fungal biomass from the medium. Plugs (6 mm diameter) were cut from the leading edge of a vigorously growing A. niger colony using a sterile cork borer and transferred to La-containing plates and incubated in the dark at 25 °C until the colony reached the edge of the plate. Colony diameter was measured daily in two directions across the colony. To recover the biomass, the fungal colony growing on the membrane was removed from the surface, washed three times with Milli-Q water and oven-dried at 105 °C until constant weight. Biomass yield was determined by measuring the dry weight; the surface pH after fungal growth was measured as described previously. A tolerance index (TI) was calculated according to the following formula: TI = (dry weight of La-exposed biomass/dry weight of control biomass × 100%) (Sayer et al. 1995; Wei et al. 2013). Growth was presented as colony expansion rates, growth rates being defined as millimetres per day, calculated according to a linear regression equation. Each treatment was conducted at least in triplicate.
Crystals that were formed in the agar were recovered by gently homogenizing the agar in 50 ml Milli-Q water at 80 °C in a crystallizing dish (Sayer and Gadd 1997; Li et al. 2015). After sedimentation and washing at least three times with cool Milli-Q water, the extracted crystals were stored in a desiccator until constant weight, and accurately measured using an HR-150A analytical balance (A&D Instruments Ltd., Abingdon, Oxfordshire, UK).
For lanthanum biotransformation experiments in liquid medium, A. niger was inoculated on MEA slants and grown for a few days until profuse growth resulted. To obtain a spore suspension, 20 ml of sterile 0.1% (v/vaq) Tween 80 was added to the slants and mixed well by vortexing. The resulting suspension was then filtered through sterile muslin cloth to remove mycelia from the suspension. The spores were washed three times using sterile Milli-Q water to remove remaining Tween 80 by centrifugation at 2553×g for 30 min. Serial dilution was carried out to obtain a spore concentration of 1 × 108 ml−1; 1 ml of this inoculum was transferred to 99 ml liquid medium in a 250-ml Erlenmeyer flask, which was maintained in a shaking incubator (Infors Multitron Standard, Rittergasse, Switzerland) at 125 rpm in the dark at 25 °C for 7 days. For harvesting, the culture was aseptically filtered through sterile 63-μm nylon mesh (John Staniar & Co. Ltd., Manchester, UK) to obtain a biomass-free supernatant which was stored at 4 °C prior to experiments. Supernatant pH was measured as described previously.
La biotransformations by fungal supernatants were performed in 15 ml centrifuge tubes, incubated on a roller mixer (Stuart Equipment, Stone, Staffordshire, UK) at room temperature for 24 h, prepared by adding 1 ml sterile LaCl3 of the desired concentration into 9 ml fungal supernatant to achieve a final volume of 10 ml and La concentrations of 0, 1, 3, 5, 7, 11, 15, 20, 30, 40 and 50 mM. After precipitation, minerals produced were collected by sedimentation and removal of the supernatant and then washed three times with Milli-Q water before being dried in a desiccator at room temperature until constant weight, in order to calculate crystal yield. Each treatment was performed at least in triplicate.
Crystal yield and La assay
To accurately estimate precipitation yield and removal of La from the supernatant after precipitation, dried crystal samples were accurately weighed as previously described. After fungal supernatant reactions with LaCl3, resulting supernatants were collected by centrifugation (2553×g, 30 min) prior to measurement of lanthanum concentrations using the Arsenazo III colorimetric method (White and Gadd 1990; Rohwer et al. 1995; Ivanov and Ermakova 2001) and an Ultrospec 2100 pro spectrophotometer (Biochrom Ltd., Holliston, MA, USA) at an optical density of 658 nm. This was achieved by pipetting 1-ml sample into a test tube with 1 ml 0.02% (w/v) Arsenazo III (Sigma-Aldrich, St. Louis, USA) in pH 2.8 potassium hydrogen phthalate buffer with a final volume of 10 ml made up by adding Milli-Q water. The concentration of lanthanum in the solution was calculated based on a calibration curve created using a series of standard solutions at 0, 1.44, 3.60, 7.20, 10.80 and 14.40 μmol l−1 La. The La removal rate was defined as RLa = (m1 − m2) × 100%, where m1 is the amount of La added to the reaction system and m2 that of the remaining La in the supernatant after reaction.
Geochemical modelling was carried out to analyse interactions of lanthanum with oxalate and pH in the aqueous state using Geochemist’s Workbench (GWB) edition 12.0 (Aqueous Solutions LLC, Urbana-Champaign, USA), which is mainly comprised of two subprograms, i.e. SpecE8 for calculating species activities and Act2 for creating stability diagrams (Ceci et al. 2015a, b; Li and Gadd 2017). The stability diagrams of both (C2O4)2− and La3+ activities as a function of pH were constructed using Act2 to simulate changes in the mineral species under ideal conditions; all ion activities were calculated using SpecE8 according to their concentrations in the liquid medium. As A. niger was found to secrete ~ 25 mM oxalic acid after 12-day growth in a previous study (Ceci et al. 2015b), the activity of oxalate was calculated based on 25 mM (C2O4)2− in the equilibrium system, while that of lanthanum was set at 1 mM La3+, which was found to be an effective concentration to precipitate La as oxalate. Activities for other chemicals in simulated spent AP1 medium were calculated using the following concentrations: 35.3 mM NaNO3, 3.7 mM KH2PO4, 1.7 mM NaCl, 0.8 mM MgSO4·7H2O, 0.2 mM CaCl2·6H2O, 17.9 μM MnSO4·4H2O, 13.9 μM ZnSO4·7H2O, 9.3 μM FeCl3·6H2O and 1.6 μM CuSO4·5H2O. For MCD fungal supernatant, the concentrations used were the following: 35.3 mM NaNO3, 7.0 mM Na2HPO4, 6.7 mM KCl, 2.0 mM MgSO4·7H2O and 36.0 μM FeSO4·7H2O. All simulated equilibrium conditions were set at 25 °C under 1.013 bars atmospheric pressure.
EDXA and SEM
Dried La-containing crystals were mounted on adhesive carbon tape stuck to aluminium electron microscopy specimen stubs (JEOL, 25 mm × 8 mm) for determination of elemental composition using an energy-dispersive X-ray spectroscopy system (Oxford Instruments Inca, Abingdon, Oxfordshire, UK) embedded within a JEOL JSM 7400F field emission scanning electron microscope (JEOL Ltd., Tokyo, Japan) operating at an accelerating voltage of 15 kV for 100 s. Samples on the stub were plated with a layer of 10-nm gold and platinum using a Cressington 208HR sputter coater (Cressington Scientific Instruments Ltd., Watford, England, UK) prior to examination using the emission scanning electron microscope (JEOL JSM7400F) running at an accelerating voltage of 5 kV.
XRD and TGA
Crystal samples were ground to a fine powder using a clean ceramic mortar and pestle and compacted tightly on the reverse side of an aluminium specimen holder (15 × 20 × 2 mm3), which was held against a glass side and detached after the back cover was snapped into place. The mineral phase of the crystals was identified using a Hiltonbrooks X-ray diffractometer (HiltonBrooks Ltd., Crewe, UK) equipped with a single graphite crystal monochromatic CuKα chronometer (30 mA, 40 kV). Duplicate samples were analysed over the range of 3–60° 2θ angle at a scan rate of one degree per min in 0.1° increments.
TGA of the crystal samples was carried out using a NETZSCH STA 409PC TG/DTG/DTA analyser fitted with a SiC furnace (NETZSCH Group, Selb, Germany). Small amounts (< 100 mg) of crystals were heated to 1000 °C at a heating rate of 10 K min−1 using dry N2 as a purge gas at a flow rate of 100 cm3 min−1. The samples were maintained at 1000 °C until constant weight. A curve of mass loss as a function of temperature was created as the result. After thermal treatment, all samples were collected for XRD analysis to identify the presence of possible mineral phases.
One-way ANOVA was applied using Tukey’s test to compare means of growth rate, biomass yield, and surface pH at a significance level of 0.05 between samples from the same medium treated with different concentrations of lanthanum.
Fungal growth and crystal formation
Growth rate, biomass yield, agar surface pH and tolerance index (TI) of A. niger after 14-day growth at 25 °C in the dark in solid Czapek-Dox medium supplemented with lanthanum chloride
La concentration (mM)
Growth rate (mm day−1)
Biomass (g dry wt)
14.21 ± 0.46a
0.19 ± 0.01a
1.86 ± 0.04b
14.12 ± 0.11a
0.18 ± 0.05a
2.00 ± 0.04a
14.31 ± 0.21a
0.16 ± 0.01a
1.87 ± 0.03b
10.67 ± 0.33b
0.17 ± 0.01a
1.71 ± 0.04c
SEM and EDXA
Thermal decomposition analysis
Biomass-free culture supernatant experiments
Control experiments were carried out using 25 mM oxalic acid solution reacted with solutions of LaCl3. It was found that the precipitation yield in the control group also showed an increase with rising La concentrations until 15 mM La where the maximum yield of 53.3 mg dry wt was reached. A similar trend of pH change was found for the control which declined from pH 1.77 at 1 mM La to pH 1.43 at 15 mM La (Fig. 7b). The amount of removed La, which reached 146.5 mg dry wt, was only slightly lower than the maximum of 149.7 mg dry wt occurring at 20 mM and showed almost a linear relationship to the lanthanum concentration over the range 1 to 15 mM La. The removal rate was maintained at 100% until 11 mM La and slightly dropped to 97.7% at 15 mM La before a marked decline at 20 mM La and above (Fig. 7d).
Despite the chemical properties and characteristics of lanthanum and its compounds being well-studied in a chemical context, its interactions with microorganisms have received scant attention. Our work, for the first time, has demonstrated the formation of insoluble biogenic lanthanum oxalate by fungi and has therefore offered an insight into possible future biotechnological applications for the biorecovery of lanthanides and other rare earths and metals (Liang and Gadd 2017). Growth of A. niger in solid medium was only slightly affected by even high concentrations (> 10 mM) of lanthanum and the formation of large amounts of crystals was achieved, demonstrating the high efficiency of the process. This work has therefore laid a foundation for the biorecovery of REE using mycogenic oxalic acid. Crystals of lanthanum oxalate precipitated under chemical conditions usually carry 10.2 molecules of water and have a well-formed monoclinic crystal habit with clinopinacoid (0,1,0) (where the crystal plane is parallel to the vertical and the inclined lateral axes), orthopinacoid (1,0,0) (with crystal planes parallel to the orthodiagonal and vertical axes) and clinodome (0,1,1) (a dome in which the planes are parallel to the inclined axis) structures (Gilphin and McCrone 1952), which is in agreement with the morphological features of our samples produced at high La concentrations (Fig. 8c, d). The morphology of abiotic REE oxalates can also vary according to the methods and conditions applied to the precipitation reaction. Flower-like hierarchical microparticles, which showed similarity to those obtained in our work, were formed when La2(C2O4)3·10H2O was precipitated at room temperature in the presence of sodium citrate, and nanotubes were produced using a mixed solvent of water and ethanol in a 1:1 ratio (Zhang et al. 2014).
The temperature range and decomposition course generally corresponded with a previous study where La2(C2O4)3·10H2O was heated to 900 °C and a weight loss of 58.1% was recorded (Zhan et al. 2012). However, a step of 4.9% mass loss occurred at 226 °C, which was caused by the transformation of hexahydate to dihydrate, was not prominent here and a total loss of 22.6% upon reaching 250 °C was recorded. This work has therefore not only demonstrated a means to recover La as lanthanum oxalate but also that mycogenic lanthanum oxalate can serve as a precursor for the preparation of La2O3 which has significant catalytic properties and is of use in several industrial fields including biodiesel production, manufacture of optical glass, phosphate removal and antimicrobial substances (Johnson et al. 2005; Liu et al. 2017; Fang et al. 2018; Salinas et al. 2018).
As regards geomicrobial transformations of minerals, fungal-produced oxalic acid can play a role in the solubilization of several minerals including calcite and dolomite (Gadd 2017). Minerals containing, e.g. Ca, Cd, Co, Cu, Mg, Mn, Sr, Zn, Ni and Pb can be transformed into oxalates by interaction with oxalate-secreting fungi (Gadd 2007; Sullivan et al. 2012; Gadd et al. 2014). Many preceding studies involving the transformation of minerals by oxalic acid-producing fungi have focused on the bioprecipitation of calcium oxalate as whewellite and weddellite (Punja and Jenkins 1984; Gadd et al. 2014; Gadd 2017). One of our preliminary experiments using La-containing malt extract agar as a growth medium for A. niger also developed pyramid-shaped crystals with typical morphological characteristics of calcium oxalate amid lanthanum oxalate crystals (data not shown). Oxalic acid could be useful in the final steps of metallurgical processes to recovery REE from leachates or other solutions (Sinha et al. 2016). Chi et al. (2004) applied oxalic acid to precipitate total rare earth elements, including Ce and La, from a leachate from bastnasite processing, and the produced oxalates were transformed into oxides after being roasted at 900 °C for 2 h. A similar process was also reported in another study where oxalic acid was utilized to recover lanthanides from REE-bearing phosphate rocks after being treated with strong acid (Aly and Mohammed 1999). Moreover, an appropriate amount of (NH4)2C2O4 was successfully used to separate lanthanum from a leachate consisting of a mixture of elements extracted from spent Ni-Mn batteries (Fernandes et al. 2013). Our XRD results showed uniformity for all biogenic and control samples from both agar plates and liquid media reactions at 1 mM La, confirming that the biominerals were well-formed crystalline structures of high purity as indicated by the sharp characteristic peaks matching impeccably with standard patterns for lanthanum oxalate in the database and a flat noise base.
In solid media experiments, only lanthanum oxalate crystals occurred even at high La concentrations. However, at higher La concentrations in the biomass-free liquid culture supernatant experiments, phosphorus was found in high amounts, associated with micro-sized spheres, indicating that P-containing compounds were also precipitated. This coincided well with the results of pH changes shown in the mass balance analysis at pH 3.40 and 1 mM La and with the geochemical modelling which showed lanthanum oxalate speciation when below pH 3.63. The plateau occurring above 15 mM La, as shown in the mass balance analysis, indicated that oxalic acid was depleted by excessive amounts of La3+, and any remaining La could participate in the precipitation of phosphates in the liquid media. It was reported that lanthanum phosphate, usually in the form of micro- or nano-sized particles and having a number of different mineral phases, could be produced by mixing La(NO3)3 and H3PO4 in a continuous precipitation reactor (Kawase et al. 2007). This could also account for the phosphates obtained at high La concentrations in our work. It is well known that fungi can release P from inorganic and organic sources which can therefore interact with other metals such as cadmium, cobalt, copper, lead, zinc and uranium, leading to the precipitation of secondary metal phosphates as microscale or nanoscale structures (Rhee et al. 2012, 2014; Gadd et al. 2014; Liang et al. 2015, 2016). In the present study, phosphates precipitated in the supernatant reaction system probably arose from chemical moieties in the growth medium according to the geochemical modelling where LaPO4 is formed if the system is pH > ~ 3.5 in the presence of excessive amounts of La3+ (Fig. 10b). Therefore, the precipitation of P-containing biominerals could be caused by the presence of phosphates in the supernatant: by adjusting the pH and the volume of the lanthanum solution, the formation of lanthanum phosphates could be avoided.
In conclusion, the fungal transformation of lanthanum chloride into La2(C2O4)3·10H2O, which can be subsequently converted into lanthanum oxide, is achievable by bioprecipitation in both La-containing solid media and biomass-free culture supernatants. Our study suggests a new biotechnological aspect for the biorecovery of rare earth elements.
The authors thank Mr. Martin Kierans (Central Imaging Facility, School of Life Sciences, University of Dundee) and Dr. Yongchang Fan (Division of Physics, University of Dundee) for their assistance with scanning electron microscopy and Dr. Laszlo Csetenyi (Concrete Technology Group, Department of Civil Engineering, University of Dundee) for assistance with X-ray diffraction and thermogravimetric experiments.
Financial support of the Geomicrobiology Group is received from the Natural Environment Research Council [NE/M010910/1 (TeaSe); NE/M011275/1 (COG3)], which is gratefully acknowledged. Xia Kang acknowledges receipt of a School of Life Sciences PhD scholarship and sponsorship from the China Scholarship Council (No. 201606910077).
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
This article does not contain any studies with human participants or animals performed by any of the authors.
- Amin MM, El-Aassy IE, El-Feky MG, Sallam AM, El-Sayed EM, Nada AA, Harpy NM (2014) Fungal leaching of rare earth elements from lower carboniferous carbonaceous shales, southwestern Sinai, Egypt. Rom J Biophys 24:25–41Google Scholar
- Currie JN (1917) The citric acid fermentation of Aspergillus niger. J Biol Chem 31:15–37Google Scholar
- Hassanien WAG, Desouky OAN, Hussien SSE (2013) Bioleaching of some rare earth elements from Egyptian monazite using Aspergillus ficuum and Pseudomonas aeruginosa. Walailak J Sci Technol 11:809–823Google Scholar
- Humphries M (2010) Rare earth elements: the global supply chain. Congressional Research Service. The Library of Congress, Washington, DCGoogle Scholar
- Ismail Z, Abu Elgoud E, Gasser M, Aly H, Abdel Hai F, Ali I (2015) Leaching of some lanthanides from phosphogypsum fertilizers by mineral acids. Arab J Nucl Sci Appl 48:37–50Google Scholar
- Kakushima K, Tsutsui K, Ohmi S-I, Ahmet P, Rao VR, Iwai H (2007) Rare earth oxides in microelectronics, p 345-365. In: Fanciulli M, Scarel G (eds) Rare earth oxide thin films: topics in applied physics, vol 106. Springer, Berlin, HeidelbergGoogle Scholar
- Schwartz W, Näveke R (1980) Biotechnische laugung armer erze mit heterotrophen mikroorganismen. Metall Jahrg 34:847–850Google Scholar
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.