Analysis of 410NiMo coating deposited by thermal spray in CA6NM martensitic stainless steel against erosion by cavitation

  • Émillyn Ferreira Trevisani OlivioEmail author
  • Paulo Sergio Olivio Filho
  • Lucas Alan de Aguiar
  • João Roberto Sartori Moreno
  • Ramón Sigifredo Cortés Paredes
ORIGINAL ARTICLE
  • 70 Downloads

Abstract

For most applications, martensitic stainless steels are subject to operating conditions where good mechanical properties and wear resistance are required. Soldering soft martensitic stainless steels features decreased tenacity of the welded joint which, along with the residual stresses, can shorten the life of component and accelerate the cavitation process. In order to increase the strength of the martensitic structures, thermal spraying is used to produce coatings, laid without resulting in thermal cycles that influence the structural integrity of the coated steels. This work was deposited by the electric arc and wire flame, the 410NiMo martensitic stainless steel, in wire and rod form, respectively, on the substrate of the martensitic stainless steel CA6NM. The samples were sent to Vickers microhardness tests and accelerated cavitation, according to ASTM G32-10. The results were obtained through optical microscopy, X-ray diffraction, SEM, and dispersive energy spectroscopy (DES); the samples featured high adhesion, low porosity, and cavitation erosion–resistant coatings. The thermal spray is suitable for the application of this type of coating.

Keywords

Thermal spraying Cavitation erosion CA6NM steel 410NiMo 

Notes

Acknowledgments

The authors thank the laboratories LEME (UTFPR), CMCM (UTFPR), LABATS (UFPR), LEME (UFPR), LORXI (UFPR), LAMATS (UFPR), LACTEC, and PGMEC.

References

  1. 1.
    Cunha MAR (2013) Modelagem De Cavitação Bifásica em um Rotor de Bomba Centrífuga. Dissertação de mestrado. Universidade Federal do ABC, Santo AndréGoogle Scholar
  2. 2.
    Ferreira RB, Ventrella VA (2005) Influência Da Camada De Revestimento Na Recuperação Por Soldagem De Turbinas Hidráulicas Danificadas Por Erosão Cavitacional. XII Congresso Nacional de Estudantes de Engenharia Mecânica. Ilha Solteira, SP. 22 a 26 de agosto de 2005Google Scholar
  3. 3.
    Allenstein AN (2007) Estudo da Resistência à Cavitação do Aço Inoxidável Martensítico CA6-NM Nitretado por Plasma: 2007. 113p. Dissertação (mestrado) - Universidade Federal do Paraná, CuritibaGoogle Scholar
  4. 4.
    Henke SL, Niño CE, Buschinelli AJA, Corrêa JA (1998) Especificação de procedimentos de reparo por soldagem de aços inoxidáveis martensíticos macios sem TTPS. XXIV ENTS, FortalezaGoogle Scholar
  5. 5.
    Henke SL (1998) Desenvolvimento de Procedimento de Soldagem de Aço Inoxidável Martensítico Macio tipo CA 6NM Sem tratamento Térmico Posterior. Dissertação de Mestrado, Universidade Federal de Santa Catarina, FlorianópolisGoogle Scholar
  6. 6.
    GonÇalves BHB (2007) Estudo comparativo da resistência à erosão por cavitação do metal de solda depositado por um arame tubular tipo 13%Cr - 4%Ni −0,4%Mo e do aço fundido ASTM A 743 CA-6NM. Dissertação de Mestrado, Belo Horizonte, Universidade Federal de Minas GeraisGoogle Scholar
  7. 7.
    Novicki N, Casas WJP, Henke SL (2008) Tenacidade à Fratura do Aço CA6NM Temperado e Revenido e de sua Junta Soldada sem TTPS. Rev Soldagem Insp 13:25–31.  https://doi.org/10.1590/S0104-92242013000200006 CrossRefGoogle Scholar
  8. 8.
    ASTM A743 / A743M-98ae1, Standard Specification for Castings, Iron- Chromium, Iron-Chromium-Nickel, Corrosion Resistant, for General Application, ASTM International, West Conshohocken, PA, 1999, http://www.astm.org
  9. 9.
    Prado EM (2004) DO; Influência das variáveis do processo MIG/MAG Convencional e MIG Pulsado nas propriedades mecânicas de juntas soldadas com arame ER410NiMo. Dissertação de Mestrado, Universidade Federal do Paraná, CuritibaGoogle Scholar
  10. 10.
    Pukasiewicz AGM Desenvolvimento de revestimentos Fe-Mn-Cr-Si-Ni resistentes à cavitação depositadas por aspersão ASP. 2008. 192p. Tese (doutorado) - Universidade Federal do Paraná, CuritibaGoogle Scholar
  11. 11.
    Marques PV (2003) Aspersão Térmica, Infosolda. Available in: < https://www.infosolda.com.br/artigos/processos-de-soldagem/231-aspersao-termica>. Access in 03 may 2016
  12. 12.
    Gartner F, Voyer J, Qi X Kreye H (2006) New challenges for wire and rod flame spraying. Institute Of Materials TechnologyGoogle Scholar
  13. 13.
    Lima CC, Trevisan R (2007) Aspersão Térmica Fundamentos e Aplicações, 2ª edn ed, 152p. Artliber Editora Ltda, São PauloGoogle Scholar
  14. 14.
    ASTM G32-10, Standard Test Method for Cavitation Erosion Using Vibratory Apparatus, ASTM International, West Conshohocken, PA, 2010, http://www.astm.org
  15. 15.
    Terres CJF (2006) 126p. Avaliação De Revestimentos de Aços Inoxidáveis Depositados por Aspersão Térmica. Dissertação (mestrado) - Universidade Federal do Paraná, CuritibaGoogle Scholar
  16. 16.
    Thorpe ML (1993) Thermal Spray. Industry in transition. Adv Mater Process 143(5):50–61 (ISSN 0026-0665)Google Scholar
  17. 17.
    Fauchais PL, Heberlein JVR, Boulos M (2014) Thermal spray fundamentals: from powder to part, 2nd edn. © Springer Science+Business, New York 1566 pCrossRefGoogle Scholar
  18. 18.
    Capra AR et al. (2007) Desenvolvimento de procedimentos de reparo de trincas e recuperação de cavitação em turbinas hidráulicas fundidas em Aço Inoxidável Martensítico Macio CA6NM. Available in: < http://www.cgti.org.br/publicacoes/wp-content/uploads/2016/03/Desenvolvimento-de-procedimentos-de-reparo.pdf>. Access in 02.maio.2016
  19. 19.
    Almeida LFCB de (2015) 133p. Avaliação da influência de aplicação de vibração mecânica na microestrutura e em características mecânicas de juntas do aço inoxidável martensítico CA6NM soldadas pelo processo FCAW. Dissertação (mestrado) - Escola de Engenharia da Universidade de São Paulo, LorenaGoogle Scholar
  20. 20.
    Boccanera LF (1999) 149p. Resistência a Erosão por Cavitação de Revestimentos Depositados por Soldagem e Aspersão Térmica. Tese (doutorado) - Universidade Federal de Santa Catarina, FlorianópolisGoogle Scholar
  21. 21.
    Pereira SA (2000) 136p. Desenvolvimento de Procedimento de Reparo por Soldagem em Aços Inoxidáveis Martensíticos com Metal de Adição Similar sem TTP. Dissertação (mestrado) - Universidade Federal de Santa Catarina, FlorianópolisGoogle Scholar

Copyright information

© Springer-Verlag London Ltd., part of Springer Nature 2019

Authors and Affiliations

  • Émillyn Ferreira Trevisani Olivio
    • 1
    Email author
  • Paulo Sergio Olivio Filho
    • 2
  • Lucas Alan de Aguiar
    • 2
  • João Roberto Sartori Moreno
    • 1
  • Ramón Sigifredo Cortés Paredes
    • 2
  1. 1.Federal Technological University of ParanáCuritibaBrazil
  2. 2.Federal University of ParanáCuritibaBrazil

Personalised recommendations