Tensile property and micro-texture evolution of the charge weld in a billet-to-billet extrusion of AA6061 aluminum profile

  • Shumei LouEmail author
  • Anning Wang
  • Shuai Lu
  • Guangxin Guo
  • Chuandong Qu
  • Chunjian Su
ORIGINAL ARTICLE
  • 11 Downloads

Abstract

Charge welds occur in profiles during billet-to-billet extrusion of hollow aluminum profiles. To investigate the effects of charge welds on the tensile property of the profile, a tensile test and a fracture scanning test using the scanning electron microscope (SEM) are conducted. The results showed that charge weld plays bad roles in the tensile property of the profile. The tensile samples derived from the charge weld distribution zone are always fractured near the charge welds. In addition, the tensile strengths of the early-stage charge welds are the poorest. To validate the property variations in the charge weld zone along the extrusion directions in a microscale, the evolution of microstructure characteristics and texture in the charge weld distribution zone are discussed with the help of the electron back scattering diffraction (EBSD). The grain morphologies, misorientation, and micro-textures are not uniform along the charge weld in the extrusion direction or on different sides of itself. Incomplete dynamic recrystallization with lower distortion energy and dislocation density due to lack of frictions with dies at the beginning and middle stages of the charge weld results in strip-shaped coarse grains and lower-angle grain boundaries, further revealing the essence of the low tensile strength at the beginning and in the middle of the charge weld. The intensity of shear texture {111}<112> on the charge weld is the largest compared with those on both sides of it, verifying the large plane strain status on the charge weld plane.

Keywords

Hollow aluminum profiles Charge welds Tensile properties Micro-texture 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Notes

Acknowledgements

This work was financially supported by the National Natural Science Foundation of China (51705295), the Shandong Provincial Natural Science Foundation, China (ZR2014JL040, ZR2018MEE022), the Science and Technology Project for the Universities of Shandong Province (J16LA58), and the SDUST Research Fund.

References

  1. 1.
    Kim KJ, Lee CH, Yang DY (2002) Investigation into the improvement of welding strength in three-dimensional extrusion of tubes using porthole dies. J Mater Process Technol 130–131:426–431CrossRefGoogle Scholar
  2. 2.
    Kim YT, Ikeda K, Murakami T (2002) Metal flow in porthole die extrusion of aluminium. J Mater Process Technol 121:107–115CrossRefGoogle Scholar
  3. 3.
    Donati L, Tomesani L, Minak G (2007) Characterization of seam weld quality in AA6082 extruded profiles. J Mater Process Technol 191:127–131CrossRefGoogle Scholar
  4. 4.
    Ceretti E, Mazzoni L, Giardini C (2009) Simulation of metal flow and welding prediction in porthole die extrusion: the influence of the geometrical parameters. Int J Mater Form 2(Suppl 1):101–104CrossRefGoogle Scholar
  5. 5.
    Khan YA, Valberg HS (2010) Metal flow in idealised A-symmetric 2D extrusion welding. Int J Mater Form 3(Suppl 1):383–386CrossRefGoogle Scholar
  6. 6.
    Den Bakker AJ, Werkhoven RJ, Sillekens WH, Katgerman L (2014) The origin of weld seam defects related to metal flow in the hot extrusion of aluminium alloys EN AW-6060 and EN AW-6082. J Mater Process Technol 214:2349–2358CrossRefGoogle Scholar
  7. 7.
    Gagliardi F, Citrea T, Ambrogio G, Filice L (2014) Influence of the process setup on the microstructure and mechanical properties evolution in porthole die extrusion. Mater Des 60:274–281CrossRefGoogle Scholar
  8. 8.
    Bai SW, Fang G, Zhou J (2017) Analysis of the bonding strength and microstructure of AA6082 extrusion weld seams formed during physical simulation. J Mater Process Technol 250:109–120CrossRefGoogle Scholar
  9. 9.
    Yu JQ, Zhao GQ, Chen L (2016) Investigation of interface evolution, microstructure and mechanical properties of solid-state bonding seams in hot extrusion process of aluminum alloy profiles. J Mater Process Technol 230:153–166CrossRefGoogle Scholar
  10. 10.
    Plata M, Piwnik J (2000) Theoretical and experimental analysis of seam weld formation in hot extrusion of aluminum alloys. Proceedings of the Seventh International Aluminum Extrusion Technology Seminar. Chicago, ET: 205–211Google Scholar
  11. 11.
    Donati L, Tomesani L (2004) The prediction of seam welds quality in aluminum extrusion. J Mater Process Technol 153–154:366–373Google Scholar
  12. 12.
    Li Q, Harris C, Jolly MR (2003) Finite element modelling simulation of charge welding phenomenon in aluminium extrusion process. Mater Des 24:493–496CrossRefGoogle Scholar
  13. 13.
    Mahmoodkhani Y, Wells M, Parson N, Jowett C, Poole W (2014) Modeling the formation of charge weld during billet-on-billet extrusion. Materials 7:3470–3480CrossRefGoogle Scholar
  14. 14.
    Zhou J, Li L, Duszczyk J (2003) 3D FEM simulation of the whole cycle of aluminium extrusion throughout the transient state and the steady state using the updated Lagrangian approach. J Mater Process Technol 134:383–397CrossRefGoogle Scholar
  15. 15.
    Pinter T, Reggiani B, Donati L, Tomesani L (2015) Numerical assessment of the influence of process and geometric parameters on extrusion welds and die deformation after multiple-cycles. Mate Today Proc 2:4856–4865CrossRefGoogle Scholar
  16. 16.
    Nanninga N, White C, Dickson R (2011) Charge weld effects on high cycle fatigue behavior of a hollow extruded AA6082 profile. J Mater Eng Perform 20:1235–1241Google Scholar
  17. 17.
    Engelhardt M, Behne D, Grittner N, Neumann A, Reimche W, Klose C (2015) Non-destructive testing of longitudinal and charge weld seams in extruded aluminum and magnesium profiles. Mater Today Proc 2:4866–4873Google Scholar
  18. 18.
    Reggiani B, Segatori A, Donati L, Tomesani L (2013) Prediction of charge welds in hollow profiles extrusion by FEM simulations and experimental validation. Int J Adv Manuf Technol 69:1855–1872CrossRefGoogle Scholar
  19. 19.
    Zhang XM, Feng D, Shi XK, Liu SD (2013) Oxide distribution and microstructure in welding zones from porthole die extrusion. Trans Nonferrous Metal Soc China 23:765–772CrossRefGoogle Scholar
  20. 20.
    Lou SM, Wang YX, Liu CX, Lu S, Liu SJ, Su CJ (2017) Analysis and prediction for the evolution of billet butt and charge weld in the continuous extrusion process of a hollow aluminum profile. J Mater Eng Perform 26:4121–4130Google Scholar
  21. 21.
    Zhang CS, Yang S, Wang CX, Zhao GQ, Gao AJ, Wang LJ (2016) Numerical and experimental investigation on thermo-mechanical behavior during transient extrusion process of high-strength 7××× aluminum alloy profile. Int J Adv Manuf Technol 85:1915–1926CrossRefGoogle Scholar
  22. 22.
    Mahmoodkhani Y, Wells MA, Poole WJ, Grajales L, Parson N (2015) The development of grain structure during axisymmetric extrusion of AA3003 aluminum alloys. Metall Mater Trans A 46:5920–5932CrossRefGoogle Scholar
  23. 23.
    Zhang K, Marthinsen K, Holmedal B, Aukrust T, Segatori A (2018) Through thickness variations of deformation texture in round profile extrusions of 6063-type aluminium alloy: experiments, FEM and crystal plasticity modelling. Mater Sci Eng A 722:20–29CrossRefGoogle Scholar
  24. 24.
    Kayser T, Klusemann B, Lambers HG, Maier HJ, Svendsen B (2010) Characterization of grain microstructure development in the aluminum alloy EN AW-6060 during extrusion. Mater Sci Eng A 527:6568–6573CrossRefGoogle Scholar
  25. 25.
    Yang XH, Wang DG, Wu ZG, Yi JH, Ni S, Du Y, Song M (2016) A coupled EBSD/TEM study of the microstructural evolution of multi-axial compressed pure Al and Al–Mg alloy. Mater Sci Eng A 658:16–27CrossRefGoogle Scholar
  26. 26.
    Chen L, Zhang JX, Zhao GQ, Wang ZS, Zhang CS (2018) Microstructure and mechanical properties of Mg-Al-Zn alloy extruded by porthole die with different initial billets. Mater Sci Eng A 718:390–397CrossRefGoogle Scholar
  27. 27.
    Chen GJ, Chen L, Zhao GQ, Zhang CS, Cui WC (2017) Microstructure analysis of an Al-Zn-Mg alloy during porthole die extrusion based on modeling of constitutive equation and dynamic recrystallization. J Alloy Compd 710:80–91CrossRefGoogle Scholar
  28. 28.
    Yu JQ, Zhao GQ, Zhang CS, Chen L (2016) Dynamic evolution of grain structure and micro-texture along a welding path of aluminum alloy profiles extruded by porthole dies. Mater Sci Eng A 682:679–690CrossRefGoogle Scholar
  29. 29.
    Yu JQ, Zhao GQ, Cui WC, Zhang CS, Chen L (2017) Microstructural evolution and mechanical properties of welding seams in aluminum alloy profiles extruded by a porthole die under different billet heating temperatures and extrusion speeds. J Mater Process Technol 247:214–222CrossRefGoogle Scholar
  30. 30.
    Fan XH, Tang D, Fang WL, Li DY, Peng YH (2016) Microstructure development and texture evolution of aluminum multi-port extrusion tube during the porthole die extrusion. Mater Charact 118:468–480CrossRefGoogle Scholar
  31. 31.
    den Bakker AJ, Katgerman L, van der Zwaag S (2016) Analysis of the structure and resulting mechanical properties of aluminium extrusions containing a charge weld interface. J Mater Process Technol 229:9–21CrossRefGoogle Scholar

Copyright information

© Springer-Verlag London Ltd., part of Springer Nature 2019

Authors and Affiliations

  • Shumei Lou
    • 1
    Email author
  • Anning Wang
    • 1
  • Shuai Lu
    • 2
  • Guangxin Guo
    • 1
  • Chuandong Qu
    • 1
  • Chunjian Su
    • 1
  1. 1.Department of Mechanical and Electrical EngineeringShandong University of Science and TechnologyQingdaoChina
  2. 2.Shandong Yancon Light Alloy Co., LtdJiningChina

Personalised recommendations