Optimization of parameters for micro friction stir welding of aluminum 5052 using Taguchi technique
- 14 Downloads
The study investigates the effect of basic parameters in friction stir welding of thin sheet. Using Aluminum Al 5052 as the base material and Taguchi L9 orthogonal array for optimization, three vital process parameters namely rotational speed, probe shape, and transverse speed were studied with the aim to maximize the tensile strength. Alongside the process, the effect on micro hardness and grain structure of the material was also investigated and metallographic properties were studied using Scanning Electron Microscopy (SEM). Fixtures made from Bakelite and mild steel were used in the process. Experiments performed on Bakelite fixture produced defective joint for all tool shapes. The results designate square-shaped tool as the one producing sound, defect-free, and high-strength joints. Hardness increases with increase in rotational speed and decreases with increase in transverse speed. Optimal parameters found were transverse speed 200 mm/min, rotational speed 3250 rpm, and square shaped tool.
KeywordsFriction stir welding Al-5052 Taguchi ANOVA Tool shape
Unable to display preview. Download preview PDF.
- 1.Scialpi A, De Giorgi M, De Filippis LAC, Nobile R, Panella FW (2009) Mechanical analysis of ultra-thin friction stir welding joined sheets with dissimilar and similar mate-rials. Mater Des 29:124–132Google Scholar
- 2.Sattari S, Bisadi H, Sajed M (2012) Mechanical properties and temperature distributions of thin friction stir welded sheets of AA5083. Int J Mech Appl 2(1):1–6Google Scholar
- 4.Sithole K, Rao VV (2016) Recent developments in micro friction stir welding: a review. In: IOP conference series: materials science and engineering, vol 114, no. 1. IOP Publishing, Bristol, p 012036Google Scholar
- 6.Sivashanmugam M, Kumar T, Ravikumar S, Seshagiri Rao V, Muruganandam D (2010) A review on friction stir welding for aluminium alloys. In Frontiers in Automobile and Mechanical Engineering (FAME), pp. 216–221Google Scholar
- 8.Meilinger Á, Török I (2013) The importance of friction stir welding tool. Prod Process Syst 6(1):25–34Google Scholar
- 13.Brinckmann S, Strombeck AV, Schilling C, Dos Santos JF, Lohwasser D, Kocak M (1998) Mechanical and toughness properties of robotic-FSW repair welds in 6061-T6 aluminium alloys. GKSS FORSCHUNGSZENTRUM GEESTHACHT GMBH-PUBLICATIONS-E 1, no. 41: ALL-ALLGoogle Scholar
- 14.Attallah MM, Salem HG (2004) Effect of Friction Stir Welding Process Parameters on the Mechanical Properties of the As-Welded and Post-Weld Heat Treated AA2095. In Proceedings of the Fifth International Symposium on Friction Stir Welding, Metz, France, pp. 14–16Google Scholar
- 15.Sato YS, Kurihara Y, Park SHC, Kokawa H, Tsuji N (2004) Friction stir welding of ultrafine grained Al alloy 1100 produced by accumulative roll-bonding. Scripta Materialia 50, no. 1: 57–60Google Scholar
- 16.ASTM American Society for Testing and Materials (2009) Standard test methods for tension testing of metallic materials. ASTM internationalGoogle Scholar