Densification, microstructure and mechanical properties of spark plasma sintered Ni-17%Cr binary alloys
- 20 Downloads
Spark plasma sintering (SPS) system was used to develop Ni-17%Cr alloys using nickel and chromium as the raw elemental materials. The powders were fabricated at different sintering temperatures ranging between 800 and 1100 °C, at constant pressure of 50 MPa, heating rate of 150 °C/min and holding time of 10 min. Scanning electron microscopy (SEM), X-ray diffraction (XRD), Vickers microhardness tester and Archimedes’ method were used to investigate the effect of sintering temperature on its microstructure, phases, mechanical properties, densification and fracture mode. The results showed that the relative density, microhardness and fracture morphology of the alloy were affected by sintering temperature, which also affects the microstructure. The maximum relative density of 98.2% and hardness value of 296.33 HV1.0 were obtained at sintering temperature of 1100 °C. The fractography results revealed that the sintered alloys were characterized by transgranular fracture from 900 to 1100 °C.
KeywordsSpark plasma sintering Densification Fracture Porosity Nickel-based alloy
Unable to display preview. Download preview PDF.
This work is based on the research supported by the National Research Foundation (NRF) of South Africa for the grant, Unique Grant No. 99348.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 2.Oguma H, Tsukimoto K, Goya S, Okajima Y, Ishizaka K, Ito E (2015) Development of advanced materials and manufacturing technologies for high-efficiency gas turbines. MHI Technical Review 52(4):106-15Google Scholar
- 5.Tin S and Pollock TM (2010) Nickel-based superalloys for blade application: production, performance and application. Encyclopedia of aerospace engineeringGoogle Scholar
- 7.Donachie MJ, Donachie SJ (2002) Superalloys: a technical guide. ASM international, RussellGoogle Scholar
- 25.García JMJ, Li Z, Vahlas C, de La Torre SD, López FJ (2010) Spark plasma sintering and characterization of NiCoCrAlY-Ta superalloy powder. J Mater Sci Eng 4:57–63Google Scholar
- 27.Tokita M (1999) Mechanism of spark plasma sintering. in Proceeding of NEDO international symposium on functionally graded materials, p. 22Google Scholar
- 39.Shi K, Huang B, He B, Xiao Y, Yang X, Lian Y, Liu X, Tang J (2018) Room-temperature tensile strength and thermal shock behavior of spark plasma sintered W-K-TiC alloys. Nucl Eng TechnolGoogle Scholar