High-strength steel S960QC welded with rare earth nanoparticle coated filler wire
- 148 Downloads
High-strength steel S960 is one of a number of advanced steels able to meet the demands of the shipbuilding, offshore, and construction industries for a favorable good high strength/weight ratio. Gas metal arc welding (GMAW) is commonly used in all structural steel fabrication, and developments in GMAW have removed previous limitations regarding high heat input and have reduced flaws. One solution for controlled heat input while ensuring a stable arc is alloying the welding wire. Usage of nanoparticles as an alloying element in welding wire have shown significant improvements in weld properties. This study investigates an S960QC joint welded with a welding wire having Lanthanum (La) nanoparticles as a coating and examines the influence of La on the welding parameters, arc stability, microstructure formation, and mechanical properties. The results are compared with a weld formed with conventional Union X96 welding wire. The microstructures observed in the weld region were martensite and tempered martensite for both wires. In the heat-affected zone, microstructures of upper bainite, martensite, tempered martensite, and globular bainite were found. The La nanoparticle-coated wire provided a stable arc during welding. However, due to the increase in wire thickness, manual wire feeding was required. The impact toughness was lower in the joint formed with the nanoparticle-coated wire. Additionally, the hardness at the fusion region was higher in the joint welded with the nanoparticle-coated wire.
KeywordsHigh strength steel S960QC LaB6 nanoparticle coated filler wire Robotic GMAW SEM Impact toughness
Open access funding provided by Lappeenranta University of Technology (LUT). This work was supported by the Lappeenranta University of Technology, Finland and Peter the Great St. Petersburg Polytechnic University, Russia. The authors are grateful to Antti Kähkönen, Antti Heikkinen, Alexey Maystro, and Vitaly Dmitriev for providing the test materials. The research work was completed during ENI CBC project Energy-efficient systems based on renewable energy for Arctic conditions “EFREA” financed by the European Union, the Russian Federation, and the Republic of Finland.
All the authors read, analyzed, approved, and wrote the final manuscript.
Compliance with ethical standards
Conflict of interests
The authors declare that they have no conflict of interest.
- 1.Suzuki S, Muraoka R, Obinata T, Endo S, Horita T, Omata K (2004) Steel products for shipbuilding. JFE pp 41–48. Available: http://www.jfe-steel.co.jp/en/research/report/002/pdf/002-05.pdf. Accessed on: 2 April 2018
- 4.Protopopov EV, Feyler SV (2016) Analysis of current state and prospects of steel production development. In: IOP Conference Series: Materials Science and EngineeringGoogle Scholar
- 5.Hulka K, Kern A, Schriever U (2005) Application of niobium in quenched and tempered high-strength steels. Mater Sci Forum:500–501Google Scholar
- 8.Schillo N, Feldmann M (2016) Experiments on the rotational capacity of beams made of high strength steel. In: Proceedings of the international colloquium on stability and ductility of steel structures, SDSS 2016, pp 533–540Google Scholar
- 17.Mirjavadi SS, Alipour M, Hamouda AMS, Matin A, Kord S, Afshari BM, Koppad PG (2017) Effect of multi-pass friction stir processing on the microstructure, mechanical and wear properties of AA5083/ZrO2 nanocomposites. J Alloys Compd 726:1262–1273. https://doi.org/10.1016/j.jallcom.2017.08.084 CrossRefGoogle Scholar
- 18.Mirjavadi SS, Alipour M, Emamian S, Kord S, Hamouda AMS, Koppad PG, Keshavamurthy R (2017) Influence of TiO2 nanoparticles incorporation to friction stir welded 5083 aluminum alloy on the microstructure, mechanical properties and wear resistance. J Alloys Compd 712:795–803. https://doi.org/10.1016/j.jallcom.2017.04.114 CrossRefGoogle Scholar
- 23.Oi K, Murayama M (2015) Recent trend of welding technology development and applications. JFE Tech Rep 20:1–7Google Scholar
- 24.(2014) MEKA steel UHS960QC. Available: http://www.meka-steel.nl/files/products/34/MK%20UHS%20960QC.pdf. Accessed on: 30 Mar 2018
- 25.Rautaruukii Corporate (2014) Optim QC structural steels. Rautaruukki Corporation pp 1–6. Available: https://www.oxycoupage.com/FichiersPDF/Ruukki_Pdf/English/Optim-QC-structural-steels.pdf. Accessed on: 28 March 2018
- 28.Zhang Y, Hou M (2012) The development of construction steel structure welding technology in China. In: Chinese Academic of EngineeringGoogle Scholar
- 32.Fattahi M, Noei Aghaei V, Dabiri AR, Amirkhanlou S, Akhavan S, Fattahi Y (2015) Novel manufacturing process of nanoparticle/Al composite filler metals of tungsten inert gas welding by accumulative roll bonding. Mater Sci Eng A 648:47–50. https://doi.org/10.1016/j.msea.2015.09.053 CrossRefGoogle Scholar
- 34.Makarov SV, Sapozhkov SB (2013) Use of complex nanopowder (Al2O3, Si, Ni, Ti, W) in production of electrodes for manual arc welding. World Appl Sci J 22(SPL.ISSUE2):87–90. https://doi.org/10.5829/idosi.wasj.2013.22.tt.22145 CrossRefGoogle Scholar
- 41.Layus P, Kah P, Parshin S, Dmitriev V, Belinga EM (2018) Study of welding wire nanocoated with lanthanum boride for S960 high-strength steel welding. In: The 28th Int Ocean and Polar Eng ConfGoogle Scholar
- 42.Yang X, Hiltunen E, Kah P ( 2017) New nano-coated welding wire for ultra-high-strength steel (S960QC) and MAG robotized welding in arctic offshore construction. In Proceedings of the International Offshore and Polar Engineering Conference, pp 86–91Google Scholar
- 43.Koo JY, Luton MJ, Bangaru NV, Petkovic RA, Fairchild DP, Petersen CW, Asahi H et al (2004) Metallurgical design of ultra high-strength steels for gas pipelines. Int J Offshore Polar Eng 14(1):2–10Google Scholar
- 44.Asahi H, Hara T, Sugiyama M, Maruyama N, Terada Y, Tamehiro H, Koyama K et al (2004) Development of plate and seam welding technology for X120 linepipe. Int J Offshore Polar Eng 14(1):11–17Google Scholar
- 46.Keehan E (2004) Effect of microstructure on mechanical properties of high strength steel weld metals. Doktorsavh Chalmers Tek Hogsk (2205)Google Scholar
- 47.Keehan E, Karlsson L, Andrén H, Bhadeshia HKDH (2006) Influence of carbon, manganese and nickel on microstructure and properties of strong steel weld metals: part 3—increased strength resulting from carbon additions. Sci Technol Weld Join 11(1):19–24. https://doi.org/10.1179/174329306X77858 CrossRefGoogle Scholar
- 48.Bhadeshia HKDH (2001) Bainite in steels: transformations, microstructure and properties, 2nd edn. IOM Communications, LondonGoogle Scholar
- 50.Bhadeshia HKDH (2007) Strong ferritic-steel welds. Mater Sci Forum 539-543:6–11. https://doi.org/10.4028/www.scientific.net/MSF.539-543.6 CrossRefGoogle Scholar
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.