Evaluation of component repair using direct metal deposition from scanned data
- 113 Downloads
In this work, the repair volume of AISI H13 tool steel samples with hemisphere-shaped defects was reconstructed through reverse engineering and the samples were repaired by laser-aided direct metal deposition (DMD) using Co-based alloys powder as the filler material. Microstructure characterization and elemental distribution of deposits were analyzed using optical microscope (OM), scanning electron microscope (SEM), and energy dispersive spectrometry (EDS). Mechanical properties of repaired samples were evaluated via tensile test and microhardness measurement. The experiment showed that a gap between deposits and substrate exists if only employing the tool path generated from the reconstructed repair volume but the gap can be removed by depositing an extra layer covering that region. Microstructure and tensile test confirmed strong metallurgical bond in the interface. Defect-free columnar structure dominated the deposits near the interface while other regions of deposits consisted of dendrite structure with interdendritic eutectics. The tensile test showed that the repaired samples have a higher ultimate tensile strength (UTS) and lower ductility compared with those of base metal. Fractography from tensile test showed repaired samples fractured brittlely at the deposits section with cracking propagating along the grain boundaries. The hardness measurement showed that the deposited layers have a much higher hardness in comparison to the substrate.
KeywordsDirect metal deposition Repair Reverse engineering Additive manufacturing Tool steel
Unable to display preview. Download preview PDF.
This project was supported by National Science Foundation Grants CMMI-1547042 and CMMI 1625736, and the Intelligent Systems Center, Center for Aerospace Manufacturing Technologies, and Material Research Center at Missouri S&T. Their financial support is greatly appreciated.
- 9.Bartkowski D, Młynarczak A, Piasecki A, Dudziak B, Gościański M, Bartkowska A (2015) Microstructure, microhardness and corrosion resistance of Stellite-6 coatings reinforced with WC particles using laser cladding. Opt Laser Technol 68:191–201. https://doi.org/10.1016/j.optlastec.2014.12.005 CrossRefGoogle Scholar
- 17.Childs THC, Akhtar SP, Hauser C, et al (2006) Selective laser melting of prealloyed high alloy steel powder beds. In: Adv. Mater. Forum III. Trans Tech Publications, pp 516–523Google Scholar
- 26.Liu R, Wang Z, Zhang Y, Sparks T, Liou F (2016) A smooth toolpath generation method for laser metal deposition. Proceedings of the 27th Annual International Solid Freeform Fabrication Symposium, Austin, Texas, USA: 1038-1046Google Scholar