Significant and reversible dimensional changes in hydrothermally compressed cedar wood and its potential as humidity-sensitive actuator

European Journal of Wood and Wood Products volume 77, pages1021–1028(2019)Cite this article

Abstract

Japanese cedar wood samples were radially compressed by 52% using saturated water vapor at 160 °C. The steam-compressed (SC) samples were boiled in water to recover their compressed shapes, and the shape recovery was evaluated on the basis of the dimensional changes under completely dry condition. The compressed shape of the wood was memorized by steaming for 90 min. After the recovery treatment, the radial and tangential swelling of the wood samples were measured during the moistening and subsequent drying. The SC wood exhibited anomalously large and reversible swelling in the radial direction, whereas its tangential swelling was almost the same as that of the uncompressed wood. The significant and reversible swelling of the SC wood was due to the swimming ring-like expansion and collapse of the folded earlywood cell wall. To evaluate the potential of SC wood as a humidity-sensitive actuator, a wooden bilayer was made by combining SC wood with a cedar wooden veneer. The flexural deformation of the SC wooden bilayer due to humidity change was significantly greater than that of the conventional bilayer, which consists of beech wood and cedar wooden veneer.

This is a preview of subscription content, access via your institution.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

References

  1. Chen S, Obataya E, Matsuo-Ueda M (2018) Shape fixation of compressed wood by steaming: a mechanism of shape fixation by rearrangement of crystalline cellulose. Wood Sci Technol 52(5):1229–1241

    CAS  Article  Google Scholar 

  2. Dwianto W, Norimoto M, Morooka T, Tanaka F, Inoue M, Liu Y (1998) Radial compression of Sugi wood (Cryptomeria japonica D. Don). Holz Roh Werkst 56:403–411

    Article  Google Scholar 

  3. Fang CH, Mariotti N, Cloutier A, Koubaa A, Blanchet P (2012) Densification of wood veneers by compression combined with heat and steam. Eur J Wood Prod 70:155–163

    CAS  Article  Google Scholar 

  4. Guo J, Songa K, Salmén L, Yin Y (2015) Changes of wood cell walls in response to hygro-mechanical steam treatment. Carbohydr Polym 115:207–214

    CAS  Article  Google Scholar 

  5. Guo J, Rennhofer H, Yin Y, Lichtenegger HC (2016) The influence of thermo-hygro-mechanical treatment on the micro- and nanoscale architecture of wood cell walls using small- and wide-angle X-ray scattering. Cellulose 23:2325–2340

    CAS  Article  Google Scholar 

  6. Guo J, Yin J, Zhang Y, Salmén L, Yin Y (2017) Effects of thermo-hygro-mechanical (THM) treatment on the viscoelasticity of in situ lignin. Holzforschung 71(6):455–460

    CAS  Article  Google Scholar 

  7. Hirano A, Obataya E, Adachi K (2016) Potential of moderately compressed wood as an elastic component of wooden composites. Eur J Wood Prod 74:685–691

    CAS  Article  Google Scholar 

  8. Inagaki T, Siesler HW, Mitsui K, Tsuchikawa S (2010) Difference of the crystal structure of cellulose in wood after hydrothermal and aging degradation: a NIR spectroscopy and XRD Study. Biomacromolecules 11:2300–2305

    CAS  Article  Google Scholar 

  9. Inoue M, Norimoto M, Otsuka Y, Yamada T (1990) Surface compression of coniferous lumber I. A new technique to compress the surface layer. Mokuzai Gakkaishi 36:969–975

    Google Scholar 

  10. Inoue M, Norimoto M, Tanahashi M, Rowell RM (1993) Steam or heat fixation of compressed wood. Wood Fiber Sci 25:224–235

    CAS  Google Scholar 

  11. Inoue M, Sekino N, Morooka T, Rowell RM, Norimoto M (2008) Fixation of compressive deformation in wood by pre-steaming. J Trop For Sci 20(4):273–281

    Google Scholar 

  12. Ito Y, Tanahashi M, Shigematsu M, Shinoda Y, Otha C (1998a) Compressive-molding of wood by 1-pressure steam-treatment: part 1. Development of compressively molded squares from thinnings. Holzforschung 52:211–216

    CAS  Article  Google Scholar 

  13. Ito Y, Tanahashi M, Shigemitsu M, Shinoda Y (1998b) Compressive-molding of wood by high-pressure steam treatment: part 2. Mechanism of permanent fixation. Holzforschung 52:217–221

    CAS  Article  Google Scholar 

  14. Kuribayashi T, Ogawa Y, Rochas C, Matsumoto Y, Heux L, Nishiyama Y (2016) Hydrothermal transformation of wood cellulose crystals into pseudo-orthorhombic structure by cocrystallization. ACS Macro Lett 5:730–734

    CAS  Article  Google Scholar 

  15. Kutnar A, Kamke F, Sernek M (2009) Density profile and morphology of viscoelastic thermal compressed wood. Wood Sci Technol 43:57–68

    CAS  Article  Google Scholar 

  16. Navi P, Girardet F (2000) Effects of thermos-hydro-mechanical treatment on the structure and properties of wood. Holzforschung 54:287–293

    CAS  Article  Google Scholar 

  17. Obataya E, Chen S (2018) Shape recovery and anomalous swelling of steam-compressed wood by swimming ring-like expansion of cell lumina. Wood Sci Technol 52(4):1009–1023

    CAS  Article  Google Scholar 

  18. Obataya E, Higashihara T, Tomita B (2002) Hygroscopicity of heat-treated wood III. Effect of steaming on the hygroscopicity of wood. Mokuzai Gakkaishi 48:348–355

    CAS  Google Scholar 

  19. Rüggeberg M, Burgert I (2015) Bio-inspired wooden actuators for large scale applications. PLoS One. https://doi.org/10.1371/journal.pone.0120718

    Article  PubMed  PubMed Central  Google Scholar 

  20. Sandberg D, Haller P, Navi P (2013) Thermo-hydro and thermo-hydro-mechanical wood processing: an opportunity for future environmentally friendly wood products. Wood Mater Sci Eng 8:64–88

    CAS  Article  Google Scholar 

  21. Seborg RM, Stamm AJ (1941) The compression of wood. Forest Products Laboratory, Forest Service US Department of Agriculture, Madison

    Google Scholar 

  22. Stamm AJ, Seborg RM (1944) Forest Products Laboratory resin-treated, laminated, compressed wood (compreg). For Prod Lab Rep, No, p 1381

    Google Scholar 

  23. Wikberg H, Maunu SL (2004) Characterisation of thermally modified hard-and softwoods by 13C CPMAS NMR. Carbohydr Polym 58:461–466

    CAS  Article  Google Scholar 

  24. Yin Y, Berglund L, Salmén L (2011) Effect of steam treatment on the properties of wood cell walls. Biomacromolecules 12:194–202

    CAS  Article  Google Scholar 

  25. Yin J, Yuan T, Lu Y, Song K, Li H, Zhao G, Yin Y (2017) Effect of compression combined with steam treatment on the porosity, chemical composition and cellulose crystalline structure of wood cell walls. Carbohydr Polym 155:163–172

    CAS  Article  Google Scholar 

Download references

Author information

Affiliations

  1. Graduate School of Life and Environmental Sciences, Tsukuba University, Tsukuba, Ibaraki, 305-8572, Japan

    Eiichi Obataya

  2. Graduate School of Bioagricultural Sciences, Nagoya University, Furo-cho, Chikusa-ku, Nagoya, 464-8601, Japan

    Shuoye Chen

Authors
  1. Eiichi Obataya
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Shuoye Chen
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Eiichi Obataya.

Ethics declarations

Conflict of interest

On behalf of all authors, the corresponding author states that there is no conflict of interest.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Obataya, E., Chen, S. Significant and reversible dimensional changes in hydrothermally compressed cedar wood and its potential as humidity-sensitive actuator. Eur. J. Wood Prod. 77, 1021–1028 (2019). https://doi.org/10.1007/s00107-019-01463-2

Download citation