European Journal of Wood and Wood Products

, Volume 76, Issue 6, pp 1737–1743 | Cite as

Effect of mineral fillers on mechanical, thermal and morphological properties of kenaf recycled polyethylene wood plastic composite

  • Ros Azlinawati Ramli
  • Nur Zuriati Zakaria
  • Ummu Umaira Abdul Rahman
  • Nur Basyirah Ahmad Bakhtiar
  • Siti Noor Hidayah Mustapha
  • Yuen Mei Lian
Original
  • 23 Downloads

Abstract

This contribution presents the effect of mineral filler on mechanical, thermal and morphological properties of wood recycled plastic composite (WrPC). WrPC was prepared using kenaf wood flour, recycled polyethylene (rPE) and maleic anhydride polyethylene (MAPE) with different types of mineral filler. All materials were premixed manually and fed into a twin screw extruder. The effect of graphite, mica and talc filler on impact strength, glass transition temperature (Tg), thermal degradation and morphological properties of WrPC was studied. The highest impact strength was achieved by graphite/WrPC at 6.99 kJ/m2 compared to WrPC at 4.29 kJ/m2. This is due to the presence of filler particles in WrPC leading to effective distribution of applied stress to overcome crack. DSC results indicated only one peak of Tg observed within 132–134 °C as a result of miscible blending. Decomposition of WrPC was slightly affected by incorporation of mineral fillers. The internal structure of WrPC with graphite/mica/talc fillers showed smooth morphology and better dispersion.

Notes

Acknowledgements

The authors would like to thank Universiti Malaysia Pahang for the financial support under University Grant No. (RDU1703286).

References

  1. Adhikary KB, Pang S, Staiger MP (2008) Dimensional stability and mechanical behaviour of wood–plastic composites based on recycled and virgin high-density polyethylene (HDPE). Compos Part B Eng 39:807–815CrossRefGoogle Scholar
  2. Araujo J, Waldman W, De Paoli M (2008) Thermal properties of high density polyethylene composites with natural fibres: coupling agent effect. Polym Degrad Stab 93:1770–1775CrossRefGoogle Scholar
  3. Ashori A (2008) Wood–plastic composites as promising green-composites for automotive industries! Bioresour Technol 99:4661–4667CrossRefGoogle Scholar
  4. Azadeh K, Mohsen S, Behzad K (2011) Comparative investigation on the mechanical properties of wood plastic composites made of virgin and recycled plastics. World Appl Sci J 14:735–738Google Scholar
  5. Bai G, Guo C, Li L (2014) Synergistic effect of intumescent flame retardant and expandable graphite on mechanical and flame-retardant properties of wood flour-polypropylene composites. Constr Build Mater 50:148–153CrossRefGoogle Scholar
  6. Bajwa DS, Bhattacharjee S (2016) Current progress, trends and challenges in the application of biofiber composites by automotive industry. J Nat Fibers 13:660–669Google Scholar
  7. Benthien JT, Ohlmeyer M (2013) Thickness swelling and water absorption of WPC after immersion in cold and boiling water. Eur J Wood Prod 71:437–442CrossRefGoogle Scholar
  8. Chafidz A, Ali I, Mohsin MA, Elleithy R, Al-Zahrani S (2012) Atomic force microscopy, thermal, viscoelastic and mechanical properties of HDPE/CaCO3 nanocomposites. J Polym Res 19:9860CrossRefGoogle Scholar
  9. Essabir H, Boujmal R, Bensalah MO, Rodrigue D, Bouhfid R, el kacem Qaiss A (2016) Mechanical and thermal properties of hybrid composites: oil-palm fiber/clay reinforced high density polyethylene. Mech Mater 98:36–43CrossRefGoogle Scholar
  10. Huang R, Mei C, Xu X, Kärki T, Lee S, Wu Q (2015) Effect of hybrid talc-basalt fillers in the shell layer on thermal and mechanical performance of co-extruded wood. Plast Compos Mater 8:8510–8523Google Scholar
  11. Huda MS, Drzal LT, Mohanty AK, Williams K, Mielewski D, Misra M (2005) Mechanical, thermal and morphological studies of poly (lactic acid) PLA/talc/recycled newspaper fiber hybrid ‘Green’ Composites. In: 8th International Conference on Woodfiber-Plastic Composites, pp 23–25Google Scholar
  12. Kamdem DP, Jiang H, Cui W, Freed J, Matuana LM (2004) Properties of wood plastic composites made of recycled HDPE and wood flour from CCA-treated wood removed from service. Compos Part A Appl Sci Manuf 35:347–355CrossRefGoogle Scholar
  13. Klyosov AA (2007) Wood-plastic composites. Wiley, HobokenCrossRefGoogle Scholar
  14. Kordkheili HY, Farsi M, Rezazadeh Z (2013) Physical, mechanical and morphological properties of polymer composites manufactured from carbon nanotubes and wood flour. Compos Part B Eng 44:750–755CrossRefGoogle Scholar
  15. Li X, Lei B, Lin Z, Huang L, Tan S, Cai X (2014) The utilization of bamboo charcoal enhances wood plastic composites with excellent mechanical and thermal properties. Mater Design 53:419–424CrossRefGoogle Scholar
  16. Li L, Guo W, Guo C (2017) Synergistic effect of melamine polyphosphate and aluminum hypophosphite on mechanical properties and flame retardancy of HDPE/wood flour composites. Wood Sci Technol 51:493–506CrossRefGoogle Scholar
  17. Maldas D, Kokta B (1990) Mechanical properties of hybrid mica/wood fiber reinforced thermoplastic composites ANTEC 90 plastics in the environment: yesterday, today & tomorrow, pp 1196–1199Google Scholar
  18. Martikka O, Huuhilo T, Butylina S, Kärki T (2012) The effect of mineral fillers on the thermal properties of wood-plastic composites. Wood Mater Sci Eng 7:107–114CrossRefGoogle Scholar
  19. Najafi SK (2013) Use of recycled plastics in wood plastic composites—a review. Waste Manag 33:1898–1905CrossRefGoogle Scholar
  20. Najafi SK, Mostafazadeh-Marznaki M, Chaharmahali M, Tajvidi M (2009) Effect of thermomechanical degradation of polypropylene on mechanical properties of wood-polypropylene composites. J Compos Mater 43:2543–2554CrossRefGoogle Scholar
  21. Noel O, Clark R (2005) Recent advances in the use of talc in wood-plastic composites. In: The 8th International Conference on Wood Fiber-plastic Composites, Madison, WisconsinGoogle Scholar
  22. Onuegbu GC, Igwe IO (2011) The effects of filler contents and particle sizes on the mechanical and end-use properties of snail shell powder filled polypropylene. Mater Sci Appl 2:810Google Scholar
  23. Partanen A, Carus M (2016) Wood and natural fiber composites current trend in consumer goods and automotive parts. Reinf Plast 60:170–173CrossRefGoogle Scholar
  24. Ramesh M (2016) Kenaf (Hibiscus cannabinus L.) fibre based bio-materials: a review on processing and properties. Prog Mater Sci 78:1–92CrossRefGoogle Scholar
  25. Renneckar S, Zink-Sharp AG, Ward TC, Glasser WG (2004) Compositional analysis of thermoplastic wood composites by TGA. J Appl Polym Sci 93:1484–1492CrossRefGoogle Scholar
  26. Rodríguez-Llamazares S, Zuñiga A, Castaño J, Radovic LR (2011) Comparative study of maleated polypropylene as a coupling agent for recycled low-density polyethylene/wood flour composites. J Appl Polym Sci 122:1731–1741CrossRefGoogle Scholar
  27. Saba N, Paridah M, Jawaid M (2015) Mechanical properties of kenaf fibre reinforced polymer composite: a review. Constr Build Mater 76:87–96CrossRefGoogle Scholar
  28. Sheshmani S, Ashori A, Fashapoyeh MA (2013) Wood plastic composite using graphene nanoplatelets. Int J Biol Macromol 58:1–6CrossRefGoogle Scholar
  29. Shiroma L, Beraldo AL (2008) Wood-plastic composite. In: Proceedings of the 51st International Convention of Society of Wood Science and TechnologyGoogle Scholar
  30. Sommerhuber PF, Welling J, Krause A (2015) Substitution potentials of recycled HDPE and wood particles from post-consumer packaging waste in wood–plastic. Compos Waste Manag 46:76–85CrossRefGoogle Scholar
  31. Tai Q, Yuen RK, Song L, Hu Y (2012) A novel polymeric flame retardant and exfoliated clay nanocomposites: preparation and properties. Chem Eng J 183:542–549CrossRefGoogle Scholar
  32. Yasmin A, Daniel IM (2004) Mechanical and thermal properties of graphite platelet/epoxy composites. Polymer 45:8211–8219CrossRefGoogle Scholar
  33. Yu Y-Y, Chen W-C (2003) Transparent organic–inorganic hybrid thin films prepared from acrylic polymer and aqueous monodispersed colloidal silica. Mater Chem Phys 82:388–395CrossRefGoogle Scholar
  34. Yu F, Liu T, Zhao X, Yu X, Lu A, Wang J (2012) Effects of talc on the mechanical and thermal properties of polylactide. J Appl Polym Sci 125:E99–E109CrossRefGoogle Scholar
  35. Zhou Y, Ning L, Li X, Zhang J, Lu Y, He J (2015) Effect of natural flake graphite on triboelectrification electrostatic potential of bamboo flour/high-density polyethylene composites. Wood Sci Technol 49:1269–1280CrossRefGoogle Scholar

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2018

Authors and Affiliations

  1. 1.Material Technology Program, Faculty of Industrial Sciences & TechnologyUniversiti Malaysia Pahang (UMP)Gambang, KuantanMalaysia

Personalised recommendations