Enhanced bonding strength of heat-treated wood using a cold atmospheric-pressure nitrogen plasma jet
- 47 Downloads
In this work, the bonding strength enhancement of heat-treated wood using a cold atmospheric-pressure nitrogen plasma jet for several lengths of treatment time was investigated. The enhancement of bonding strength was assessed by measurement of the contact angle of aqueous adhesive and water borne finish along with determination of compressive shear strength of wood samples bonded with an aqueous adhesive and pull-off strength of a water borne finish coating on wood samples. Additionally, the elemental composition and crystallinity index of the heat-treated wood surface were characterized using X-ray photoelectron spectroscopy and X-ray diffraction. As expected, the measurements demonstrated that contact angle decreased after atmospheric-pressure nitrogen plasma jet treatment, and the optimal treatment time was 100 s. X-ray photoelectron spectroscopy shows that hydrophilic groups such as C=O, OH, and COOH appeared on the surface of the HW. The atmospheric-pressure nitrogen plasma jet treatment had a positive effect on the crystallinity of heat-treated wood because of a slight degradation of hemicelluloses. Increasing the bonding strength of heat-treated wood is beneficial for broadening the fields of its applications.
This work is financially supported by National Project Upgrading Project of Applied Technology Research and Development Program of Heilongjiang Province (GX16A002).
- ASTM (2009) ASTM D4541 Standard test method for pull-off strength of coatings using portable adhesion testers. Auris Nasus Larynx 33:93–96Google Scholar
- GB/T17517 (1988) Adhesives-wood to wood adhesive bonds-determination of shear strength by compression loading. Chinese national standardization management committee, ChinaGoogle Scholar
- Kocaefe D, Poncsak S, Boluk Y (2008) Effect of thermal treatment on the chemical composition and mechanical properties of birch and aspen. Bioresources 3:117Google Scholar
- Li j (2002) Wood science. China Higher Education Press, Beijing (in Chinese) Google Scholar
- Nastasi P (2013) Effect of heat treatment on sorption properties and dimensional stability of wood. Mater Sci-Medzg 19:291–294Google Scholar
- Nguyen TT, Ji X, Van Nguyen TH et al (2017) Wettability modification of heat-treated wood (HTW) via cold atmospheric-pressure nitrogen plasma jet (APPJ). Holzforschung 71:543–680Google Scholar
- Tuong VM, Li J (2010) Effect of heat treatment on the change in color and dimensional stability of acacia hybrid wood. Bioresources 5:1257–1267Google Scholar
- Yi̇ldi̇z S (2011) The effects of natural weathering on the properties of heat treated alder wood. Bioresources 6:2504–2521Google Scholar