Experimental determination of the compression resistance of differently shaped wood particles as influencing parameter on wood-reduced particleboard manufacturing
- 75 Downloads
The price for industrial wood and, thus, particles for the manufacture of particleboard has been rising in the past and will be a topic of current interest in the future as economic growth is targeted at limited resources. One of the strategies to overcome this development is to reduce the amount of wood used for panel production. However, a simple reduction in the amount of wood used for panel manufacture leads to panels of lower density and, consequently, reduced properties. One approach to solving this problem is to re-engineer the particle mat structure to improve the panels’ density profile and, thus, meet required panel properties and at the same time lower board densities. As the particles’ compressibility is one of the main influencing parameters for density profile formation, it is the intention of this study to use a previously developed measurement method to give compression resistances of particles of various shapes and dimensions. It was found that the bulk density alone is not decisive for the particles’ compression resistance. The compression resistance derived from the change of particle shape is lower than that derived from wood substance compression. The compression resistance of large-sized particles was found to be higher than that of small-sized particles. It was concluded that a targeted combination of face and core layer particles improves the panels’ density profile.
The authors thank the Fachagentur Nachwachsende Rohstoffe e.V. (FNR), Gülzow, Germany, for its financial support, and all those persons who were engaged in the experimental realization, namely Mrs. Sabrina Heldner, Mrs. Dörte Bielenberg and Mr. Hannes Wagner (all Thünen Institute of Wood Research). The firm Kronopol Sp z o.o. (Zary, Poland), namely Prof. Dr. Joachim Hasch and Mr. Maik Hirschberg, the firm Pallmann Maschinenfabrik GmbH & Co. KG, namely Dr. Helmut Roll, the firm Dold Holzwerke GmbH (Buchenbach, Germany), and Dr. Martin Dressler (Leuco) are gratefully acknowledged for providing test materials.
- Aßmann J (2015) Kostendruck macht erfinderisch [Cost pressure is the mother of invention]. In: Proc of 11th Holzwerkstoffkolloquium, 10–12. Dezember 2015. Dresden, GermanyGoogle Scholar
- EPF-European Panel Federation (2013) Annual Report 2013–2014. Bruges, BelgiumGoogle Scholar
- Grigoriou A (1981) Die Eigenschaften von Feinspänen aus sieben verschiedenen Holzarten [The properties of fine wood particles made of seven different wood species]. Holzforsch Holzverw 33(1):1–5Google Scholar
- Mihailova J, Tritchkov N (2009) Theoretical model for determination of the maximum difference in particleboards vertical density. In: Proc of COST Action E49, Processes and performance of wood-based panels - adding value through physical functionality, 28.-29. April 2009. Istanbul, TurkeyGoogle Scholar
- Sosin MJ (1974) Untersuchung der Elastizität und Verformbarkeit der Spanvliese bei der Spanplattenherstellung [Investigation of elasticity and deformability of the particle mats in particleboard manufacture]. Holztechnologie 15(1):45–48Google Scholar