European Journal of Wood and Wood Products

, Volume 70, Issue 5, pp 735–740

Industrial production of pine tannin-bonded particleboard and MDF

  • J. Valenzuela
  • E. von Leyser
  • A. Pizzi
  • C. Westermeyer
  • B. Gorrini
Originals Originalarbeiten

Abstract

This article reports on the industrial particleboard and MDF production and trial results obtained over a period of nine years using pine tannin adhesives in Chile. The industrial panels obtained clearly showed that pine tannin extract, a renewable raw material, can be industrially used as an adhesive to manufacture particleboard and medium density fiberboard (MDF) of excellent quality and of very low formaldehyde emission, and this at a reasonable cost. The technology revealed itself suitable both for very old multi-daylight particleboard lines and for more modern single daylight MDF lines. Panels were manufactured initially with addition of small percentages of pMDI to the pine tannin adhesive. Later, adhesive formulations in which pine tannin alone without pMDI was used still showed good results. Industrial results where either paraformaldehyde or hexamethylenetetramine was used as hardener are reported. In the former case the panels satisfied with ease the E1 formaldehyde emission class of European norms. In the case of either pMDI-added adhesives, or hexamine-hardened adhesives without pMDI the emission was lower than the requirements of the F**** Japanese standard.

Industrielle Produktion von mit Kieferntannin verklebten Spanplatten und MDF

Zusammenfassung

In diesem Artikel werden die industrielle Produktion von Spanplatten und mitteldichten Faserplatten mit Tanninkleber in Chile und die Erfahrungen damit über einen Zeitraum von neun Jahren beschrieben. Die industriell und zu angemessenen Kosten hergestellten Platten zeigten, dass Kieferntanninextrakt, ein nachwachsender Rohstoff, zur industriellen Produktion von qualitativ hochwertigen Spanplatten und MDF mit niedriger Formaldehydemission verwendet werden kann. Die Technologie erwies sich sowohl für sehr alte Mehretagenpressen für Spanplatten als auch für modernere Einetagenpressen für MDF als geeignet. Zuerst wurden die Platten unter Zugabe von kleinen Mengen an pMDI zum Tanninkleber hergestellt. Später zeigten Klebstoffrezepturen, bei denen nur Kieferntannin ohne pMDI verwendet wurde, gute Ergebnisse. Über Ergebnisse mit Paraformaldehyd oder Hexamethylentetramin als Härter wird berichtet. Im ersten Fall erfüllten die Platten problemlos die Anforderungen der Emissionsklasse E1 der europäischen Normen. Bei Klebstoffen mit Zugabe von pMDI bzw. Klebstoffen mit Hexamin als Härter und ohne pMDI war die Emission geringer als die Anforderungen der Klasse F**** der japanischen Norm.

References

  1. EN 120 (1995) Wood based panels. Determination of formaldehyde content. Perforator extraction method Google Scholar
  2. EN 312 (1995). Wood particleboard-specifications Google Scholar
  3. JIS A5908 (2003) Particleboards Google Scholar
  4. Kamoun C, Pizzi A (2000a) Mechanism of hexamine as a non-aldehyde polycondensation hardener, part 1. Holzforsch Holzverwert 52(1):16–19 Google Scholar
  5. Kamoun C, Pizzi A (2000b) Mechanism of hexamine as a non-aldehyde polycondensation hardener, part 2: recomposition of intermediate reactive compound. Holzforsch Holzverwert 52(3):66–67 Google Scholar
  6. Pichelin F, Kamoun C, Pizzi A (1999) Hexamine hardener behaviour—effects on wood glueing, tannin and other wood adhesives. Holz Roh- Werkst 57(5):305–317 CrossRefGoogle Scholar
  7. Pichelin F, Nakatani M, Pizzi A, Wieland S, Despres A, Rigolet S (2006) Thick wood panels bonded industrially with formaldehyde free tannin adhesives. For Prod J 56(5):31–36 Google Scholar
  8. Pizzi A (1979) Hybrid interior particleboard using wattle tannin adhesives. Holzforsch Holzverwert 31(4):86–88 Google Scholar
  9. Pizzi A (1982) Pine tannin adhesives for particleboard. Holz Roh- Werkst 40:293–301 CrossRefGoogle Scholar
  10. Pizzi A (1983) Wood adhesives chemistry and technology. Marcel Dekker, New York Google Scholar
  11. Pizzi A, Stephanou A (1993) Comparative and differential behaviour of pine vs. pecan nut tannin adhesives for particleboard. Holzforsch Holzverwert 45(2):30–33 Google Scholar
  12. Pizzi A, Stracke P, Trosa A (1997) Industrial tannin/hexamine low emission exterior particleboard. Holz Roh- Werkst 55(3):168 CrossRefGoogle Scholar
  13. Pizzi A, Von Leyser EP, Valenzuela J, Clark JG (1993) The chemistry and development of pine tannin adhesives for exterior particleboard. Holzforschung 47:164–172 Google Scholar
  14. Sealy-Fisher J, Pizzi A (1992) Increased pine tannins extraction and wood adhesives development by phlobaphenes minimization. Holz Roh- Werkst 50:212–220. CrossRefGoogle Scholar

Copyright information

© Springer-Verlag 2012

Authors and Affiliations

  • J. Valenzuela
    • 1
  • E. von Leyser
    • 2
  • A. Pizzi
    • 3
  • C. Westermeyer
    • 4
  • B. Gorrini
    • 5
  1. 1.Georgia-Pacific South AmericaConcepcionChile
  2. 2.Diteco LtdaConcepcionChile
  3. 3.ENSTIB-LERMABUniversity of Nancy 1EpinalFrance
  4. 4.Rebisa-Resinas del Bio-Bio SAConcepcionChile
  5. 5.Cellulosa AraucoRanquilChile

Personalised recommendations