Surface finishes by mechanically induced wood surface fusion

  • A. PizziEmail author
  • J. -M. Leban
  • M. Zanetti
  • F. Pichelin
  • S. Wieland
  • M. Properzi
Originalarbeiten/Originals

Abstract

Mechanically induced vibration wood fusion welding techniques can also be used to obtain wood surface finishes of increased surface hardness and performance in presence of polymerizing unsaturated oils such as sunflower oil, or other polymerizing finishes. Wood surface hardness values more than double than those for the untreated control timber can be obtained by this method. This result is obtained due to two effects induced by the sharp increase in temperature induced by the mechanical welding vibration (i) the polymerization to a hardened network of the unsaturated oil and (ii) the densification proven to occur in the surface layer of the timber during mechanically-induced vibration-welding. The first of these effects predominates at shorter welding times while at slightly longer welding times both effects occur with the second one progressively becoming the bigger contributor. In the latter case the some μm thin densified surface is a surface composite formed by the networked unsaturated oil permeating the wood fibre/fused lignin composite.

Keywords

Welding Wood Density Wood Surface Water Repellancy Friction Welding 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Oberflächenvergütung mittels mechanisch induzierter Holzoberflächenverschmelzung

Zusammenfassung

Mechanisch induzierte Vibrations-Schweiß-Techniken bei Holz können ebenso angewandt werden, um Holzdeckschichten von erhöhter Härte und Widerstandsfähigkeit in Gegenwart von polymeren ungesättigten Ölen, wie z.B. Sonnenblumenöl, oder anderen polymerisierenden Beschichtungen zu erhalten. Auf diese Weise lassen sich mehr als doppelt so hohe Härtewerte für Oberflächenschichten von Holz erreichen, als für Kontrollproben von unbehandeltem Holz. Dieses Ergebnis ist die Folge von zwei Einflüssen, welche durch den steilen Temperaturanstieg der mechanischen Schweißvibration hervorgerufen werden (i) die Einwirkung der Polymerisierung auf ein gehärtetes Netzwerk des ungesättigten Öls, und (ii) durch die Verdichtung, welche nachweislich in Deckschichten von Schnittholz während des mechanisch induzierten Vibrationsschweißvorgangs auftritt. Erster überwiegt bei kurzen Schweißzeiten, während bei etwas längeren Schweißzeiten beide Einflüsse auftreten, wobei der zweite sich nach und nach zum stärkeren Faktor entwickelt. In letzterem Fall stellt die einige μm dünne, verdichtete Oberfläche einen Oberflächenverbund dar, welcher dadurch entsteht, dass das vernetzte ungesättigte Öl die faserverschmolzene Ligninmasse durchdringt.

References

  1. Decoux V, Varcin E, Leban J-M (2004) Relationships between the intra-ring wood density assessed by X-ray densitometry and optical anatomical measurements in conifers. Consequences for the cell wall apparent density determination. Ann For Sci 61:251–262CrossRefGoogle Scholar
  2. Gfeller B, Zanetti M, Properzi M, Pizzi A, Pichelin F, Lehmann M, Delmotte L (2003) Wood bonding by vibrational welding. J Adhes Sci Technol 17(11):1425–1590CrossRefGoogle Scholar
  3. Gfeller B, Pizzi A, Zanetti M, Properzi M, Pichelin F, Lehmann M, Delmotte L (2004) Solid wood joints by in situ welding of structural wood constituents. Holzforschung 58(1):45–52CrossRefGoogle Scholar
  4. Leban J-M, Pizzi A, Wieland S, Zanetti M, Properzi M, Pichelin F (2003) X-ray microdensitometry analysis of vibration-welded wood. J Adhes Sci Technol 13:673–685Google Scholar
  5. Mothe F, Duchanois G, Zannier B, Leban J-M (1998) Analyse microdensitométrique appliquée au bois: méthode de traitement des données utilisée à l’INRA-ERQB (programme Cerd). Ann Sci For 53(3):301–313CrossRefGoogle Scholar
  6. Norme Française NF B51–126 (1976) Brinell hardness for wood fiberboard.Google Scholar
  7. Pizzi A (1990) Extended durability by chemical fixation of unsaturated alkyd surface finishes to wood. Holzforschung Holzverwertung 42(6):107–109Google Scholar
  8. Pizzi A (1993) A new approach to non-toxic, wide-spectrum, ground-contact wood preservatives, Part 1: approach and reaction mechanisms. Holzforschung 47: 253–260CrossRefGoogle Scholar

Copyright information

© Springer-Verlag 2005

Authors and Affiliations

  • A. Pizzi
    • 1
    Email author
  • J. -M. Leban
    • 2
  • M. Zanetti
    • 1
  • F. Pichelin
    • 3
  • S. Wieland
    • 3
  • M. Properzi
    • 3
  1. 1.Enstib - LermabUniversity of NancyÉpinal Cedex 9France
  2. 2.INRA, Institut National de la Recherche Agronomique, Centre de ChampenouxChampenouxFrance
  3. 3.SWOOD, Swiss School of Engineering for the Wood IndustryBielSwitzerland

Personalised recommendations