Influence of Spodumene Added as a Fluxing Agent on the Properties of Alumina Porcelain Insulator

  • D. A. Abdel Aziz
  • E. El-Fadaly
High-Performance Ceramics

Abstract

Alumina porcelain electrical insulators were prepared using Li2O-bearing spodumene flux as a partial substitute for feldspar. The effects of spodumene on microstructure, crystalline phases, physical properties, modulus of rupture, dielectric breakdown strength and volume resistivity were investigated. The samples with spodumene content >5 mass-% sintered at 1350°C showed both zero percent water absorption (WA) and apparent porosity (AP). Density was found to decrease with increasing spodumene content from 2.39 g/cm3 (at 5 mass-% spodumene) to 2.37 g/cm3 (10 mass-%) to 2.33 g/cm3 (15 mass-%). This may be due to the irreversible phase transformation of α-spodumene to β-spodumene, which accompanies a change in density of spodumene from α-phase (3.20 g/cm3) to β-phase (2.35 g/cm3). The crystalline phases were characterised by X-ray diffraction and scanning electron microscope. They showed that spodumene favours crystallisation of elongated needle-like mullite and spodumene solid solution that coexist with alumina particles embedded in the glassy matrix of bodies sintered at 1350°C. This resulted in an increase in modulus of rupture and enhanced the electrical properties of the porcelain bodies. The maximum 71 N/mm2 modulus of rupture (MOR), dielectric strength of 21 KV/mm and electrical resistivity equal to 10×1012 Ω·cm were recorded with 10 mass-% spodumene.

Keywords

alumina insulators spodumene volume resistivity 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Buchanan, R.C.: Properties of Ceramic Insulators. Ceramic Materials for Electronics. 2nd ed., Marcel Dekker Inc., New York (1991)Google Scholar
  2. [2]
    Moulson, A.J., Herbert, J.M.: Electroceramics. 2nd ed., John Wiley & Sons, England (2003)CrossRefGoogle Scholar
  3. [3]
    Norton, F.H.: Fine Ceramics, Technology and Applications. McGraw-Hill Book Co., New York, (1970) 387–407Google Scholar
  4. [4]
    Oberzan, J.M., Holc, Buh, M., Kuscer, D., Lavrac, I., Kosec, M.: High-alumina porcelain with the addition of a Li2O-bearing fluxing agent. J. of the Europ. Ceram. Soc. 29 (2009) 2143–2152CrossRefGoogle Scholar
  5. [5]
    Tulyaganov, D.U., Agathopoulos, S., Fernandes, H.R., Ferreira, J.M.F.: Influence of lithium oxide as auxiliary flux on the properties of triaxial porcelain bodies J. of the Europ. Ceram. Soc. 26 (2006) 1131–1139CrossRefGoogle Scholar
  6. [6]
    Gamal A. Khater, Morsi M. Morsi: Applicable thermally stable articles of glass-ceramics based on spodumene-enstatite system from natural raw materials. Thermochimica Acta 519 (2011) [1–2] 6–11CrossRefGoogle Scholar
  7. [7]
    Lvting, He, Guobin, Xia, De’an Yang: Synthesis and characterization of LTCC composites based on the spodumene/anorthite crystallizable glass. J. of Alloys and Compounds 556 (2013) 12–19CrossRefGoogle Scholar
  8. [8]
    Sallam, E.H., Serry, M.A., Naga, S.M.: Iow thermal expansion electrical insulators. J. Mater. Sci. 81 (1986) 3269CrossRefGoogle Scholar
  9. [9]
    Tadzhiew, F.Kh., Ismatova, R.I., Nabiev, Kh.M.: Lithium containing material intended for production of domestic porcelain. Glass and Ceramic 45 (1989) [9–10] 397Google Scholar
  10. [10]
    Abdel Aziz, D.A.: Effect of composition and mineralizers on the physical electrical and mechanical properties of alumina porcelain insulators. Ph.D. Thesis, Univ. Zagazig (1997)Google Scholar
  11. [11]
    Xiaohong Xu, Xiaoyang Xu, Jianfeng Wu, Yaxiang Zhang, Xinbin Lao, Kun Li, Yu Xu: Effect of dolomite and spodumene on the performances of andalusite composite ceramics for solar heat transmission pipeline. Ceram. Internat. 41 (2015) [9B] 11861–11869Google Scholar
  12. [12]
    Long Xia, Xinyu Wang, Guangwu Wen, Bo Zhong, Liang Song: Nearly zero thermal expansion of β-spodumene glass ceramics prepared by sol-gel and hot pressing method. Ceram. Internat. 38 (2012) [6] 5315–5318CrossRefGoogle Scholar
  13. [13]
    Kitouni, S.: Dielectric Properties of Triaxial Porcelain Prepared Using Raw Native Materials Without Any Additions. Balkan Journal of Electrical & Computer Engineering 2 (2014) [3] 128–131Google Scholar
  14. [14]
    Ghaffari, M., Salahi, E., Rajabi, A.: Effect of Alumina Substitution on Porosity and Thermal Expansion of Triaxial Porcelain-Like Bodies. J. Ceram. Sci. Tech. 05 (2014) [04] 287–292Google Scholar
  15. [15]
    Ismatova, R.: Properties and structure of spodumene-porcelain. Steklo ikeramika (1987) [7] 27–28CrossRefGoogle Scholar
  16. [16]
    Parmelee, C.W., Rodriguez, A.R.: Catalytic mullitization of kaolinite by metallic oxides. J. Amer. Ceram. Soc. 25 (1942) [1]CrossRefGoogle Scholar
  17. [17]
    Xue Dong, Jiachen Liu, Haiyan Du, Anran Guo, Mengxia Liu: Microstructure characterization of in situ synthesized porous Si2N2O ceramics using spodumene additive. Ceram. Internat. 39 (2013) [4] 4657–4662CrossRefGoogle Scholar
  18. [18]
    Lvting He, Guobin Xia, De’an Yang: Synthesis and characterization of LTCC composites based on the spodumene/anorthite crystallizable glass. J. of Alloys and Compounds 556 (2013) 12–19CrossRefGoogle Scholar
  19. [19]
    Lakatos, T., Johansson, L.-G., Simmingsköld B.: The effect of some glass components on the viscosity of glass. Glasteknisk Tidskrift 27 (1972) [2] 25–28Google Scholar
  20. [20]
    Lundin, S.T.: In Studies on Triaxial Whiteware bodies. Almqvist and Wiksell, Stockholm, Sweden (1959)Google Scholar
  21. [21]
    Shartsis, L., Spinner, S., Capps, W.: Density, expansivity and viscosity of molten alkali silicates. J. Amer. Ceram. Soc. 35 (1952) [6] 155–160CrossRefGoogle Scholar
  22. [22]
    Swapan Kr. Das, Kausik, D.: Differences in densification behavior of K- and Na-feldspar-containing porcelain bodies. Thermochimica Acta 406 (2003) 199–206CrossRefGoogle Scholar
  23. [23]
    Jongprateep Oratai, Petrovsky Vladimir, Dogan Fatih.: Effects of yttria concentration and microstructure on electric breakdown of yttria stabilized zirconia. J Metal Mater Miner 18 (2008) [1] 9–1Google Scholar
  24. [24]
    Richerson, D.W.: Modern Ceramic Engineering, Marcel and Dekker, Inc., New York, USA (1982) 47Google Scholar
  25. [25]
    Chaudhuri, S.P., Sarkar, P., Chakraborty, A.K.: Electrical resistivity of porcelain in relation to constitution. Ceram. Internat. 25 (1999) 91–99CrossRefGoogle Scholar
  26. [26]
    Olupot, Peter W., Jonsson, Stefan, Byaruhanga, Joseph K.: Development and characterization of triaxial electrical porcelains from Ugandan ceramic minerals. Ceram. Internat. 36 (2010) 1455–1461]CrossRefGoogle Scholar
  27. [27]
    Fink, D.G., Beaty, H.W.: Standard hand book for electrical Engineers. Eleventh Edition, MCGRAW-Hill Book Company, New York (1978)Google Scholar
  28. [28]
    Chaudhuri, S.P., Bandyopadhyay, S., Mitra, N.: Electrical resistivity of mullite obtained by sintering Al2O3-SiO2 mixtures. Internat. Ceram. 44 (1995) [5]Google Scholar
  29. [29]
    Looms, J.S.T.: Insulators for High Voltages. Institution of Electrical Engineers, Power Engineering Series 7 IEE (1988) 26Google Scholar
  30. [30]
    Sukran Demirkiran, A., Recep Artir, Esref Avci: Electrical resistivity of porcelain bodies with natural zeolite addition. Ceram. Internat. 36 (2010) 917–921CrossRefGoogle Scholar

Copyright information

© Springer Fachmedien Wiesbaden GmbH, part of Springer Nature 2017

Authors and Affiliations

  1. 1.Ceramic Dept.National Research CentreCairoEgypt
  2. 2.Environmental Studies and Research InstituteUniversity of Sadat CitySadatEgypt

Personalised recommendations