Microwave Hydrothermal Assessment for CSH Formation in Silica-Lime-Water Systems

  • A. Tawfik
  • F. Abd El-Raoof
  • H. F. Youssef
  • S. A. S. El-Hemaly
Building Materials

Abstract

Microwave energy as a fast technique was utilized for the preparation of calcium silicate hydrates using hydrothermal reaction of silica quartz and/or silica fume with active lime in a solution. The silica/lime ratio was selected to be 60/40 in a mix as compared with the composition of sand-lime-based construction industries. The CSH formation was assessed after treatment at 140 and 160 °C under saturated steam microwave hydrothermal conditions. Moreover, the CSH formation was studied at 160 °C for periods up to 180 min. The prepared samples were characterized through XRD and FTIR. Further, DSC and SEM tools were used to investigate selected samples. The results led to the conclusion that the complete reaction of lime with the available silica sand was pronounced for samples prepared under saturated steam at 160°C/2 h, forming cross network needle structure morphology as seen from SEM results. Moreover, the results confirm the conversion phenomenon of CSH compounds changing in reaction time or in reactive silica percentage into another form of CSH. An amorphous structure like tobermorite is formed in samples containing silica fume as source of silica and microwave hydrothermally cured at 160 °C/2 h.

Keywords

sand-lime reaction CSH FTIR DTA microstructure 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    El-Hemaly, S.A.S., Taha, A.S., Tawfik A.: Influence of some industrial waste by-products on the properties of the aerated blocks. Egyptian J. of Applied Sci. 21 [4A] (2006) 99–108Google Scholar
  2. [2]
    Tawfik, A., Taha, A.S., El-Hemaly, S.A.S., El-Didamony, H.: Influence of the Autoclaving Conditions on Some Properties of Lightweight Building Blocks. Silic. Indus. 72 (2007) [5–6] 89–94Google Scholar
  3. [3]
    Tawfik, A., El-Hemaly, S.A.S., El-Sokary, T.M.: Assessment of Autoclaved Aerated Concrete Samples Incorporated with Cement Kiln Dust within the Raw Materials. Amer. Soc. of Civil Engineers (ASCE), 6th International Engineering and construction Conference (IECC’6) of Advances in Affordable Housing & Green Construction, Cairo, Egypt, (2010) 171–179Google Scholar
  4. [4]
    Tawfik, A., Soltan, A.M., El-Hemaly, S.A.S., Abd-El-Raoof, F.: Marble Stone Waste as Raw Material for Autoclaved Sand-Lime Bricks. Interceram 61 [3] 96–100Google Scholar
  5. [5]
    Gabrovšek, R., Kurbus, B., Mueller, D., Weiker, W.: Tobermorite formation in the system CaO, C3S-SiO2-Al2O3-NaOH-H2O under hydrothermal conditions. Cem. Concr. Res. 23 (1993) 321–328CrossRefGoogle Scholar
  6. [6]
    Wu, J., Zhu, Y.J., Chen, F.: Ultrathin calcium silicate hydrate nanosheets with large specific surface areas: synthesis, crystallization, layered self-assembly and applications as excellent adsorbents for drug, protein, and metal ions”. Small 9 [17] (2013) 2911–2925CrossRefGoogle Scholar
  7. [7]
    Xiaoxuan Guo, Zhiqiang Wang, Jin Wu, Yun-Mui Yiu, Yongfeng Hu, Ying-Jie Zhu, Tsun-Kong Sham: Tracking Drug Loading Capacities of Calcium Silicate Hydrate Carrier: A Comparative X-ray Absorption Near Edge Structures Study. J. Phys. Chem. B 119 [31] (2015) 10052–10059CrossRefGoogle Scholar
  8. [8]
    Guan, W., Jin, F., Fang, Z., Fang, D., Cheng, Y., Yan, P., Chen, Q.: Low hydrothermal temperature synthesis of porous calcium silicate hydrate with enhanced reactivity SiO2. Ceram. Internat. 40 (2014) 4415–4420CrossRefGoogle Scholar
  9. [9]
    Masahiko Saigusa, Akiko Yamamoto, Kyoichi Shibuya: Agricultural Use of Porous Hydrated Calcium Silicate: Effect of porous hydrated calcium silicate on resistance of rice plant (Oryza sativa L.) to rice blast (Pyriculariaolyzae)”. Plant Prod. Sci. 3 [1] (2000) 51–54CrossRefGoogle Scholar
  10. [10]
    Ping Yu. R., James Kirkpatrick, Brent Poe, Paul F. McMillan, Xiandong Cong: Structure of Calcium Silicate Hydrate (C-S-H): Near-, Mid-, and Far-Infrared Spectroscopy. J. Amer. Ceram. Soc. 82 (1999) [3] 742–748Google Scholar
  11. [11]
    Baltakys, K., Jauberthie, R., Siauciunas, R., Kaminskas, R.: Influence of modification of SiO2 on the formation of calcium silicate hydrate. Mater. Sci-Poland 25 [3] (2007) 663–670Google Scholar
  12. [12]
    Ray, A.: Hydrothermally treated cement-based building materials — Past, present, and future Pure. Appl. Chem. 74 [11] (2002) 2131–2135CrossRefGoogle Scholar
  13. [13]
    Rouhollah Alizadeh, Laila Raki, Jon M. Makar, James J., Beaudoin, Igor Moudrakovski: Hydration of tricalcium silicate in the presence of synthetic calcium-silicate-hydrate. J. Mater. Chem. 19 (2009) 7937–7946CrossRefGoogle Scholar
  14. [14]
    Ramachandran, V.S.: Application of differential thermal analysis in cement chemistry. VII. Autoclaved cementitious products. Chemical Publishing Company Inc., New York (1969)Google Scholar

Copyright information

© Springer Fachmedien Wiesbaden GmbH, part of Springer Nature 2017

Authors and Affiliations

  • A. Tawfik
    • 1
  • F. Abd El-Raoof
    • 1
  • H. F. Youssef
    • 1
  • S. A. S. El-Hemaly
    • 1
  1. 1.Department of Refractories, Ceramics and Building MaterialsNational Research CenterDokki, CairoEgypt

Personalised recommendations