High Temperature Erosion of Dense Refractory Castables for CFBC Boilers

  • K. Prasad
  • V. G. Kadirvell
  • L. N. Satapathy
  • R. Sanakaranarayana
Refractories
  • 1 Downloads

Abstract

The erosion resistance of dense refractory bricks or castables used in CFBC boilers is tested as per ASTM C 704. This method of testing determines the relative erosion of a refractory at room temperature only. Hence, solid particle erosion at elevated temperatures is desired in selecting the suitable refractory quality for boiler applications. The dense refractory materials for CFBC boilers are usually eroded at operating temperature (∼900°C) by hot circulating solids at high temperatures. In this work, low cement castable−45, low cement castable−80 and an 80% alumina-based plastic refractory castable, three varieties of dense refractory castables used in CFBC boilers, were selected for testing of erosion properties. The erosion tests were conducted at room temperature and boiler operating temperature of 900°C at three different angles of impingement (30°, 45° and 90°) using specially developed high temperature erosion test equipment following the ISO 16349 (2015) standard. The erosion loss result values (in cm3) were compared, and this comparison is useful in selection of suitable material for various erosion prone zones of the boiler.

Keywords

circulating fluidized bed combustor (CFBC) fluidization refractories bed material dense bricks low cement castable plastic ramming mix erosion resistance 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Anand Arjunwadkar, Prabir Basu, Bishnu Acharya: A review of some operation and maintenance issues of CFBC boilers. Appl. Therm. Eng. 102 (2016) 672–694CrossRefGoogle Scholar
  2. [2]
    Snyder, G.E.D., Ehrlich, S.: Refractories in CFB applications. Proc. 12th Int. Conf. Fluidised Bed Combustion, 09.05.–13.05.1993, ASME 2 (1993) 967–982Google Scholar
  3. [3]
    Crowley, M.S., Bakker, W.T., Stalling, J.: Refractory applications in circulating fluid bed combustors. Proc. 11th Int. Conf. Fluidised Bed Combustion, ASME (1991) 417–423Google Scholar
  4. [4]
    Heard, N.E.: A historical perspective of experience based design enhancements for the refractory lining systems of circulating fluidised bed combustors. Proc. 12th Int. Conf. Fluidised Bed Combustion, 09.05.–13.05.1993, ASME 2 (1993) 949–953Google Scholar
  5. [5]
    Schacht, C.A.: Refractories Handbook. 10th Ed., Marcel Dekker Inc., New York, Basel (2004) 280–281 and 395–414, ISBN: 0-8247-5654-1CrossRefGoogle Scholar
  6. [6]
    Johnson, R.C., Seshamani, M.: Refractory lining system for circulating fluidised bed (CFB) water cooled cyclones. Proc. 10th Int. Conf. Fluidized Bed Combustion, 30.04.–03.03. 1989, ASME 1 (1989) 419–425Google Scholar
  7. [7]
    Vincent, R.Q.: Refractory experience in circulating fluidized bed combustors. Task 7: Final Report — Contract No.: DE-AC21-85MC22012. U.S. Department of Energy, Office of Fossil Energy, Morgantown Energy Technology Center, Morgantown, West Virginia, November (1989)Google Scholar
  8. [8]
    Jing-Zhou Yang, Ming-Hao-Fang, Zhao-Hui-Huang, Xio-Zhi Hu, Yan-Gai-Liu, Hao-Ran Sun, Jun-Tong Huang, Xiao-Chao Li: Solid Particle impact erosion of alumina-based refractories at elevated temperatures. J. Eur. Ceram. Soc. 32 (2012) 283–289CrossRefGoogle Scholar
  9. [9]
    Franc, A., Roberts, S.G.: The effect of impact angle on the erosion rate of polycrystalline α-Al2O3, J. Eur. Ceram. Soc. 18 (1998) 269–214CrossRefGoogle Scholar
  10. [10]
    Heuer, V., Walter, G., Hutchings, I.M.: High temperature erosion of fibrous ceramic components by solid particle impact. Wear 233–235 (1999) 257–262CrossRefGoogle Scholar
  11. [11]
    Jianren Zhou, Shyam Bahadur: Erosion characteristics of alumina ceramics at high temperatures. Wear 181–183 (1995) 178–188Google Scholar
  12. [12]
    Bakker, W.T., Liebhard, M., Brekke, D.: Erosion of refractories in CFBC’c, effect of bed materials and refractory properties: A laboratory study. Proc. 12th Int. Conf. Fluidised Bed combustion, ASME 2 (1993) 955–965Google Scholar
  13. [13]
    Prestes, E., Medeiros, J., Gomes, D.T., Veiga, J.L.B.C., Pandolfelli, V.C.: Hot-erosion of nano-bonded refractory castables for petrochemical industries. Ceram. Int. 39 (2013) 2611–2617CrossRefGoogle Scholar
  14. [14]
    Luz, A.P., Silva, A.B., Santos Jr., N.T., Medeiros, J., Pandolfelli, V.C.: Mullite-based refractory castable engineering for the petrochemical industry. Ceram. Int. 39 (2013) 9063–9070CrossRefGoogle Scholar
  15. [15]
    Zawrah, M.F.M., Khali, N.M.: Effect of mullite formation on properties of refractory castables. Ceram. Int. 27 (2001) 689–694CrossRefGoogle Scholar
  16. [16]
    ASTM International Designation C704/C704M-12, Standard test for abrasion resistance of refractory materials at room temperatureGoogle Scholar
  17. [17]
    ACI 547.1R-89 Refractory plastics and ramming mixes. Reapproved State of the Art Report (1997)Google Scholar

Copyright information

© Springer Fachmedien Wiesbaden GmbH, part of Springer Nature 2017

Authors and Affiliations

  • K. Prasad
    • 1
  • V. G. Kadirvell
    • 1
  • L. N. Satapathy
    • 2
  • R. Sanakaranarayana
    • 3
  1. 1.Process and Captive Power SystemsBharat Heavy Electricals Ltd.Tiruchirappalli, Tamil NaduIndia
  2. 2.Ceramic Technological Institute, Corporate R & DBharat Heavy Electricals Ltd.Bengaluru, KarnatakaIndia
  3. 3.Dept. of Metallurgical and Materials EngineeringNational Institute of TechnologyTiruchirappalli, Tamil NaduIndia

Personalised recommendations