Preparation of 11-Å Al-substituted Tobermorite from Egyptian Trachyte Rock and its Effect on the Specific Properties of Portland Cement

  • H. Youssef
  • H. M. Darweesh
Raw Materials Worldwide

Abstract

Tobermorite (TOB), the cement phase that results from the hydration of the cement, was laboratory prepared from trachyte rock (TR). The effect of the prepared TOB on the specific properties of ordinary Portland cement (OPC) was investigated. The results showed that the water of consistency or w/c ratio as well as setting times (initial and final) were increased with the addition of TOB. Also, combined water and free lime contents, bulk density, and compressive strength also increased with curing times up to 90 days, but they only increased up to 10 mass-% TOB content and then decreased. The free lime content decreased with increasingTOB content due to the deficiency of the cement. The SEM images showed that the formed hydration products with the pure OPC are the same with the prepared TOB, but with more developed crystals.

Keywords

OPC setting time tobermorite trachyte rock density porosity strength 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Hewlett, P.C.: Lea’s Chemistry of Cement and Concrete. 4th Ed., John Wiley & Sons Inc., New York/Toronto (1998), ISBN 10: 0-340-56589-6Google Scholar
  2. [2]
    Darweesh, H.H.: Effect of the combination of some pozzolanic wastes on the properties of Portland cement pastes. L’industria italiana del Cemento 808 (2005) 298–311Google Scholar
  3. [3]
    Darweesh, H.H.: Characteristics of metakaoline blended cement pastes. Sil. Ind. 72 (2007) [1–2] 24–32Google Scholar
  4. [4]
    El-Didamony, H., Darweesh, H.H., Mostafa, R.A.: Characteristics of pozzolanic cement pastes, Part I: Physico-mechanical properties. Sil. Ind. 73 (2008) [11–12] 193–200Google Scholar
  5. [5]
    Kersener, Z., Darweesh, H.H.M., Routil, L.L.: Mortar composites from waste materials. Cem. Hormigon 2 (2011) [943] 12–19Google Scholar
  6. [6]
    Darweesh, H.H.M.: Setting, hardening and st. properties of cement pastes with zeolite alone or in combination with slag. Interceram 62 (2012) [1] 52–57Google Scholar
  7. [7]
    Darweesh, H.H., Abdel-Kader, A.H., El-Meligy, M.G.: Utilization of pulp black liquor waste as a cement admixture. Inter. J. Basic and Appl. Sci. 2 (2013) [3] 230–238Google Scholar
  8. [8]
    Youssef, H., Ibrahim, D., Komarneni, S., Mackenzie, K.J.D.: Synthesis of 11 Å Al-substituted tobermorite from trachyte rock hydrothermal treatment. Ceramics Inter. 36 (2010) [1] 203–209CrossRefGoogle Scholar
  9. [9]
    ASTM-Standards: Standard test method for normal water of consistency of hydraulic cement. C187 (1993) [86] 148–150Google Scholar
  10. [10]
    ASTM-Standards: Standard test method for setting time of hydraulic cement. C191 (1993) [92] 866–868Google Scholar
  11. [11]
    ASTM-Standards: Standard test method for compressive strength of dimension stone. C170 (1993) [90] 828–830Google Scholar
  12. [12]
    Darweesh, H.H.M., El-Alfi, E.A.: Effect of some water-soluble polymer admixtures on the hydration characteristics of Portland cement pastes. Sil. Ind. 71. (2005) [1–2] 27–32Google Scholar
  13. [13]
    Echart, A., Ludwig, H.M., Stark, J.: Hydration of the four main Portland cement clinker phases. Zement-Kalk-Gips 28 (1995) [8] 443–452Google Scholar
  14. [14]
    Ramachandran, V.S., Feldman, R.F.: Concrete admixtures handbook. Properties, science and technology. 2nd Ed., Noyes Publications, New Jersey (1995), ISBN 13: 9780815513735Google Scholar

Copyright information

© Springer Fachmedien Wiesbaden 2014

Authors and Affiliations

  1. 1.Department of Refractories, Ceramics and Building MaterialsNational Research CenterCairoEgypt

Personalised recommendations