Rolling Textures in Compacts of Copper and Steel

  • Herbert A. J. Chin
  • Craig S. Hartley
Material Research Summary


This study was undertaken to determine whether differences exist in the rolling textures of materials rolled with and without cladding and whether such differences are affected by bonding the clad and core by hot isostatic pressing (HIP’ing) prior to rolling/ Both steel-clad copper and copper-clad steel were studied, using compacts having nominal volume fractions of core equal to.33 and.50. Unclad core material having the same initial thicnkess as the cores was rolled to similar reductions for comparison with material rolled with cladding. No significant difference in the deformation textures, compared to unclad material, were observed for steel-clad copper. However, for copper-clad steel, a pronounced deformation texture developed in the core at lower total reductions than those required to developed the same degree of texture in unclad material. In these cases, the cladding showed evidence of a shear texture. Prebonding of the compacts by HIP’ing intensified this effect.


Pole Figure Stack Fault Energy Total Reduction Deformation Texture Rolling Texture 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. 1.
    I.L. Dillamore and W.T. Roberts, Acta Met, 12 (1964), p. 281.CrossRefGoogle Scholar
  2. 2.
    I.L. Dillamore and W.T. Roberts, Met. Rev., 10 (1965), p. 271.CrossRefGoogle Scholar
  3. 3.
    R.A. Vandermeer and J.C. Ogle, Trans. Met. Soc. AIME, 242 (1968), p. 1317.Google Scholar
  4. 4.
    G.R. Love (Report ORNL/TM-2018, Oak Ridge National Laboratory, 1968).Google Scholar
  5. 5.
    H.A.J. Chin (Ph.D. Dissertation, University of Florida, 1979).Google Scholar

Copyright information

© TMS 1986

Authors and Affiliations

  • Herbert A. J. Chin
    • 1
  • Craig S. Hartley
    • 2
  1. 1.Pratt and Whitney’s Engineering Division South in West Palm BeachUSA
  2. 2.Louisiana State UniversityUSA

Personalised recommendations