An evaluation of cast stainless steel (CF8M) fracture toughness caused by thermal aging at 430°C

  • Jae Do Kwon
  • Jae Hyun Ihn
  • Joong Cheul Park
  • Sung Jong Choi
  • Yun Won Park
Article
Received:
Revised:

Abstract

Cast stainless steel may experience embrittlement when it is exposed approximately to 300°C for a long period. In the present investigation, the three classes of the thermally-aged CF8M specimen were prepared using an artificially-accelerated aging method. After the specimens were held for 300, 1800 and 3600hrs. at 430°C, respectively, the specimens were quenched in water which is at room temperature. Load versus load line displacement curves andJ- R curves were obtained using the unloading compliance method,J IC values were obtained using the ASTM E 813–87 and ASTM E 813–81 methods. In addition to these methods,J IC values were obtained using the SZW (stretch zone width) method described in JSME S 001–1981. The results of the unloading compliance method areJ Q = 543.9kj/m2 for virgin materials. The values ofJ IC for the degraded materials at 300, 1800 and 3600hrs. are obtained 369.25kJ/m2, 311.02kJ/2, 276.7kJ/2, respectively. The results obtained by the SZW method are compared with those obtained by the unloading compliance method. Both results are quite similar. Through the elastic-plastic fracture toughness test, it is found that the value ofJ IC is decreased with an increase of the aging time.

Key Words

CF8M Virgin Material Degraded Material Elastic-Plastic Fracture Toughness Test Unloading Compliance Method Stretch Zone Width Method 
This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. ASTM, 1989, Standard Test Method forJ IC,A Measure of Fracture Toughness,ASTM E813–87.Google Scholar
  2. ASTM, 1995, Standard Test Method for DeterminingJ-R Curves,ASTM El 152–87.Google Scholar
  3. Bamford, W. H.. Kunta, M. K., Spitznagel, J. and Witt, F. J., 1983,The Effect of Thermal Aging on the Structural Integrity of Cast Stainless Steel Piping for Westinghouse Nuclear Steam Supply System, Westinghouse Proprietary Class 2.Google Scholar
  4. Brothers, A. J., Hill, M., Parker, M. T., Spitzig, W. A. Wiebe, W. and Wolff, U, E., 1971,ASTM STP 493.Google Scholar
  5. Chopra, O. K. and Chung, H. M., 1988, “Aging Degradation of Cast Stainless Steels : Effect on Mechanical Properties, Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors,” edited by G. J. Theus and J. R. Weeks,The Metallurgical Society, Warrendale, PA., pp. 737–748.Google Scholar
  6. Chopra, O.K. and Sather, A., 1990,Initial Assessment of the Mechanism and Significance of Low-Temperature Embrittlement of Cast Stainless Steels in LWR System, NUREG/ CR-5385, ANL-89/17 R5.Google Scholar
  7. Chopra, O.K., 1993,Long-Term Embrittlement of Cast Duplex Stainless Steels in LWR System : Semi-annual Report, NUREG/CR- 4744, Vol. 7, No. 1, ANL-92/42 R5.Google Scholar
  8. Clarke, G. A., Andrews, W. R., Paris, P. C. and Schmidt, D. W., 1976,ASTM STP 590, p. 27.Google Scholar
  9. Handbook of Stainless Steel, 1992, SHEWHA Publisher, in Korea.Google Scholar
  10. JSME, 1981, The Method of Elastic-Plastic Fracture Toughness (J),JSME S 001-1981.Google Scholar
  11. Kobayashi, H., Hirano, K., Nakamura, H. and Nakazawa, H., 1977,Proc. ICF 4, p. 583.Google Scholar
  12. Kwon Jae-Do, Park Joong-Cheul, Lee Yong- Son, Lee Woo-Ho and Park Yun-Won, 2000, “An Investigation of Degradation for Casting Stainless Steel, CF8M, under High Temperature,”Nuclear Engineering and Design, Vol. 198, pp. 227–240.CrossRefGoogle Scholar
  13. Kwon Jae-Do, Woo Seung-wan, Lee Yong- Son, Park Joong-Cheul and Park Yun-Won, 2001, “Effects of Thermal Aging on the Low Cycle Fatigue Behavior of Austenitic-ferritic Duplex Cast Stainless Steel,”Nuclear Engineering and Design, Vol. 206, pp. 35–44.CrossRefGoogle Scholar
  14. Nichol, T. J., Datta, A. and Aggen, G., 1980, “Embrittlement of Ferritic Stainless Steels,”Metallurgical Transactions A, Vol. 11 A, pp.573–585.CrossRefGoogle Scholar
  15. Seok, C. S., 2000, “Effect of Temperature on the Fracture Toughness of A516 Gr70 Steel,”KSME International Journal, Vol. 14, No. 1, pp. 11–18.Google Scholar
  16. Solomon, H. D. and Levinson, Lionel M., 1978, “Mössbauer Effect Study of 475°C Embrittlement of Duplex and Ferritic Stainless Steels,dud”Acta Metallurgica, Vol. 26, pp. 429–442.CrossRefGoogle Scholar
  17. Trautwein, A. and Gysel, W., 1982, “Influence of Long-time Aging of CF8 and CF8M Cast Steel at Temperatures Between 300°C and 500°C on Impact Toughness and Structural Properties, Stainless Steel Castings,”ASTM STP 756, pp. 165–189.Google Scholar
  18. Ustinovshokov, Y., Shirobokova M. and Push- karev„ 1996, “A Structural Study of the Fe-Cr System Alloys,”Acta Metallurgica, Vol. 44, No. 12, pp. 5021–5032.Google Scholar
  19. Vrinat, M., Cozar, R. and Meyzaud. Y., 1986, “Precipitated Phase in the Ferrite of Aged Cast Duplex Stainless Steels,”Scripta Metallurgica, Vol. 20, pp. 1101–1106.CrossRefGoogle Scholar
  20. Williams, R. O., 1958.Trans. TMS-A1ME, Vol. 212, pp. 497–502.Google Scholar

Copyright information

© The Korean Society of Mechanical Engineers (KSME) 2002

Authors and Affiliations

  • Jae Do Kwon
    • 1
  • Jae Hyun Ihn
    • 1
  • Joong Cheul Park
    • 1
  • Sung Jong Choi
    • 1
  • Yun Won Park
    • 2
  1. 1.Department of Mechanical EngineeringYeungnam UniversityGyeongbukKorea
  2. 2.Korea Institute of Nuclear SafetyDaejeonKorea

Personalised recommendations