Abstract
This study describes a novel paint technology that meets the recycling needs of industrial products. The decomposable crosslinking paint exhibits good properties throughout its use in the natural environment, and after use, it can be easily eliminated in a special process to recover the substrates.
The paint was cured by a reaction between a carbonyl group of resins and a hydrazide group of crosslinking agents. The reverse reaction could be promoted by three essential components: water (reactive material), an acid (catalyst), and a solvent (diluent between active groups). The paint film was eliminated by dipping the paint in the solution containing these three components. The rates of dissolution were determined by water content, acid strength, swelling intensity of solvent, and dipping temperature.
Keywords
Coating Film Dissolution Time DMAEMA Paint Film Pencil HardnessPreview
Unable to display preview. Download preview PDF.
References
- (1).Nakayama, Y.,Prog. Org. Coat., 31, 105 (1997).CrossRefGoogle Scholar
- (2).Nakayama, Y., “High Performance Coating Films Cured by Novel Penetrating Method: Anionic Resin Paints,”Journal of Coatings Technology,69, No. 870, 61 (1997).CrossRefGoogle Scholar
- (3).Nakayama, Y., “High Performance Coatings Based on Novel Penetrative Curing: Cationic Electrodeposition Coatings Cured at Ambient Temperature,”Journal of Coatings Technology,69, No. 875, 33 (1997).CrossRefGoogle Scholar
- (4).Nakayama, Y., “Research of Coatings,” Technical Report of Kansai Paint Co., Ltd., No. 128, 2 (1997).Google Scholar
- (5).Okamoto, Y., Hasegawa, Y., and Yoshino, F.,Prog. Org. Coat., 29, 175 (1996).CrossRefGoogle Scholar
- (6).JIS Handbook 1990, Paint and Varnishes, in English, p. 279.Google Scholar
- (7).JIS Handbook 1990, Paint and Varnishes, in English, p. 208.Google Scholar
- (8).JIS Handbook 1990, Paint and Varnishes, in English, p. 200.Google Scholar
- (9).JIS Handbook 1990, Paint and Varnishes, in English, p. 210.Google Scholar
- (10).JIS Handbook 1990, Paint and Varnishes, in English, p. 205.Google Scholar