The transgranular SCC of a Mg-Al alloy: Crystallographic, fractographic and acoustic-emission studies

  • D. G. Chakrapani
  • E. N. Pugh
Environmental Interactions

Abstract

A study has been made of the propagation of transgranular stress-corrosion cracks in a Mg−7.5 wt pct Al alloy tested at room temperature in an aqueous NaCl-K2CrO4 solution; the studies were carried out on single cracks which initiated and propagated within single grains in coarse-grained bend specimens. The resulting fracture surfaces were flat, and two-surface analysis established their orientation to be {ie1155-01}. Specimens fractured at liquid-nitrogen temperature cleaved on {ie1155-02}, indicating that the {ie1155-03} are not the normal cleavage planes in this material. The stress-corrosion fracture surfaces were cleavage-like in appearance, containing shallow steps which were matching and interlocking on opposite faces. Discrete acoustic signals were emitted during crack propagation, and these are considered to result from discontinuous crack advance. It is concluded that stress-corrosion cracking in this system occurs by discontinuous cleavage on {ie1155-04} planes.

Keywords

Fracture Surface Metallurgical Transaction Tension Face Cleavage Step Bend Specimen 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    G. Siebel:Der Deutschen Luftfahrt Forschung, p. 528, R. Oldenbourgh, Munich and Berlin, 1937.Google Scholar
  2. 2.
    H. L. Logan:J. Res. Nat. Bur. Stand., 1958, vol. 61, p. 503.Google Scholar
  3. 3.
    D. K. Priest, F. N. Beck, and M. G. Fontana:Trans. ASM, 1955, vol. 47, p. 473.Google Scholar
  4. 4.
    G. Oryall and D. Tromans:Corrosion, 1971, vol. 27, p. 8.Google Scholar
  5. 5.
    L. Fairman and J. M. West:Corros. Sci., 1965, vol. 5, p. 711.CrossRefGoogle Scholar
  6. 6.
    E. N. Pugh, J. A. S. Green, and P. W. Slattery:Fracture 1969, p. 387, Chapman and Hall, London, 1969.Google Scholar
  7. 7.
    F. Meller and M. Metzger: NACA Technical Note 4019, 1957.Google Scholar
  8. 8.
    D. G. Chakrapani: Ph.D. Thesis, University of Illinois at Urbana-Champaign, 1975.Google Scholar
  9. 9.
    B. Clark:Acta Met., 1968, vol. 16, p. 141.CrossRefGoogle Scholar
  10. 10.
    D. A. Meyn:Corrosion, 1970, vol. 26, p. 427.Google Scholar
  11. 11.
    B. Cox:Corrosion, 1974, vol. 30, p. 191.Google Scholar
  12. 12.
    D. G. Chakrapani and E. N. Pugh:Corrosion, in press.Google Scholar
  13. 13.
    T. P. Hoar:Proc. Intl. Conf. on Stress-Corrosion Cracking and Hydrogen Embrittlement of Iron-Base Alloys, Firminy, June, 1973, in press (discussion following paper by T. P. Hoar).Google Scholar
  14. 14.
    J. Kruger:Ibid. (discussion following paper by J. C. Scully).Google Scholar
  15. 15.
    D. Haneman and E. N. Pugh:J. Appl. Phys., 1963, vol. 34, p. 2269.CrossRefADSGoogle Scholar
  16. 16.
    J. D. Venables:J. Appl. Phys., 1960, vol. 31, p. 1503.CrossRefADSGoogle Scholar
  17. 17.
    J. R. Low, Jr.:Proceedings of Swampscott Conf. on Fracture, p. 68, Wiley, 1958.Google Scholar

Copyright information

© American Society for Metals, The Melallurgical Society of AIME 1975

Authors and Affiliations

  • D. G. Chakrapani
    • 1
  • E. N. Pugh
    • 2
  1. 1.Physical Plant at that UniversityUSA
  2. 2.Materials Research LaboratoryUniversity of IllinoisUSA

Personalised recommendations