Fracture of steels containing pearlite

  • A. R. Rosenfield
  • G. T. Hahn
  • J. D. Embury
Symposium on the Cellular and Pearlite Reactions

Abstract

The relative effects of pearlite and spherodite on ductile, cleavage, and fatigue failure are summarized. Neither the cleavage strength nor the fatigue endurance limit appear to depend directly on cementite contentper se. Spherodized steels cleave less readily than ferrite/pearlite steels. Ductile fracture resistance is lowered considerably by both types of cementite, pearlite being more deleterious. Ferrite/pearlite steels appear to exhibit slower fatigue crack growth rates at low stress intensity levels than high strength steels. At high stress intensity levels the behavior is reversed. Slip-incuded cracking of carbide lamellae appears easier than that of spherodized carbides. In ductile fracture situations the crack spreads progressively through a pearlite colony via preferential cracking of carbides and rupture of the intervening ferrite accompanied by large local shear strains. Fatigue fracture proceeds with formation of frequent branches, preferentially along the pearlite colony interface.

Keywords

Ferrite Cementite Pearlite Ductile Fracture Pearlite Coloni 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    K. W. Burns and F. B. Pickering:J. Iron Steel Inst., 1964, vol. 202, p. 899.Google Scholar
  2. 2.
    I. L. Mogford:Met. Rev., 1967, vol. 12, no. 114, p. 49.CrossRefGoogle Scholar
  3. 3.
    F. B. Pickering and T. Gladman:Iron Steel Inst. Spec. Rep., 1963, vol. 81, p. 36.Google Scholar
  4. 4.
    R. Phillips and J. A. Chapman:J. Iron Steel Inst., 1966, vol. 204, p. 615.Google Scholar
  5. 5.
    A. R. Rosenfield and G. T. Hahn:Trans. ASM, 1966, vol. 59, p. 963.Google Scholar
  6. 6.
    A. S. Tetelman, T. R. Wilshaw, and C. A. Rau, Jr.:Int. J. Fract. Mech., 1969, vol. 4, p. 147.Google Scholar
  7. 7.
    G. T. Hahn, R. G. Hoagland, and A. R. Rosenfield:Met. Trans., 1971, vol. 2, p. 537.CrossRefGoogle Scholar
  8. 8.
    J. R. Griffiths and G. Oates:Fracture 1969, P.L. Pratt,et al, eds., p. 229, Chapman and Hall, London, 1969.Google Scholar
  9. 9.
    J. L. Uvira, D. B. Clay, P. J. Worthington, and J. D. Embury:Can. Met. Quart, in press.Google Scholar
  10. 10.
    D. E. Hodgson and A. S. Tetelman:Fracture dy1969, P. L. Pratt,et al, eds., p. 266, Chapman and Hall, London, 1969.Google Scholar
  11. 11.
    U.M. Gensamer, E. B. Pearsall, W. S. Pellini, and J. R. Low:Trans. ASM, 1942, vol. 30, p. 983.Google Scholar
  12. 12.
    D. C. Lemmon and 0. D. Sherby:J. Mater., 1969, vol. 4, p. 444.Google Scholar
  13. 13.
    T. Gladman, B. Holmes, and F. B. Pickering:J. Iron Steel Inst, 1970, vol. 208, p. 172.Google Scholar
  14. 14.
    C. T. Liu and J. Gurland:Trans. ASM, 1968, vol. 61, p. 157.Google Scholar
  15. 15.
    S. Fukui and N. Uehara:Proc. 2nd Int. Conf. Strength of Metals and Alloys, p. 616, ASM, 1970.Google Scholar
  16. 16.
    L. Roesch:Mem. Sci. Rev. Met., 1969, vol. 66, p. 29.Google Scholar
  17. 17.
    T. C. Lindley, G. Oates, and C. E. Richards:ActaMet, 1970, vol. 18, p. 1127.Google Scholar
  18. 18.
    J.A. Reinbolt and W.J. Harris, Jr.:Trans. ASM, 1951,vol. 43, p. 1175.Google Scholar
  19. 19.
    R. Phillips, W. E. Duckworth, and F. E. L. Copley:J. Iron Steel lnst., 1964, vol. 202, p. 593.Google Scholar
  20. 20.
    E. Epremian and R. F. Mehl:Amer. Soc. Test. Mater., Spec. Tech. Publ. 137, p. 25,1952.Google Scholar
  21. 21.
    G. E.Dieter, R. F. Mehl, and G. T. Hörne:Trans.ASM, 1955, vol. 47, p. 424.Google Scholar
  22. 22.
    G. T. Hahn, M. Sarrate, and A. R. Rosenfield: Report AFFDL TR-70-144, Wright-Patterson Air Force Base, Ohio, 1970, p. 425.Google Scholar
  23. 23.
    J. M. Barsom: Proc. 1st Nat. Cong, on Pressure Vessels and Piping. Congress held San Francisco, May 1971.Google Scholar
  24. 24.
    P. R. V. Evans, N. B. Owen, and B. E. Hopkins:J. Iron Steel lnst, 1970, vol. 208, p. 560.Google Scholar
  25. 25.
    T. Kawasaki, T. Yokobori, S. Nakanishi, Y. Ogawara, and M. Horiguchi:Rep. Res. Inst. Strength Fract. Mater., Tohoku Univ., 1970, vol. 6, p. 25.Google Scholar
  26. 26.
    W. H. Bruckner:Weld. J. Res. Supp., 1950, vol. 29, p. 467-s.Google Scholar
  27. 27.
    A. R. Rosenfield, E. Votava, and G. T. Hahn:Trans. ASM, 1968, vol. 61, p. 807.Google Scholar
  28. 28.
    L. E. Miller and G. C. Smith:J. Iron Steel lnst., 1970, vol. 208, p. 998.Google Scholar
  29. 29.
    J. T. Barnby and M. R. Johnson:Met. Sci. J., 1969, vol. 3, p. 155.Google Scholar
  30. 30.
    D. P. Clausing:Trans. ASM, 1967, vol. 60, p. 504.Google Scholar
  31. 31.
    B.J. Brindly:Acta Met., 1970, vol. 18, p. 325.CrossRefGoogle Scholar
  32. 32.
    B. R. Butcher and H. R. Pettit:J. Iron Steel lnst., 1968, vol. 204, p. 469.Google Scholar
  33. 33.
    R.J.Henry:Met. Trans., 1970; vol. 1, p. 1073.Google Scholar
  34. 34.
    P. B. Hirsch and F. J. Humphrey:Physics of Strength and Plasticity, A. S. Argon, ed., M.I.T. Press, 1969.Google Scholar
  35. 35.
    M. F. Ashby:Phil. Mag., 1966, vol. 15, p. 1157.CrossRefGoogle Scholar
  36. 36.
    T. Kumakuka:Bull, Jap. Soc. Mech. Eng., 1968, vol. 11, p. 427.Google Scholar
  37. 37.
    K. Tanaka, T. Mori, and T. Nakamura:Phil. Mag., 1970, vol. 21, p. 267.CrossRefGoogle Scholar
  38. 38.
    I. G. Palmer, G. C. Smith, and R. D. Warda:Physical Basis of Yield and Frac-ture, A. C. Strickland, ed., Inst, of Physics and Physical Society, London, 1966.Google Scholar
  39. 39.
    U. Lindborg:Trans. ASM, 1968, vol. 61, p. 511.Google Scholar
  40. 40.
    F. A. McClintock:Physics of Strength and Plasticity, A. S. Argon, ed., p. 307, M.I.T. Press, 1969.Google Scholar
  41. 41.
    P. T. Heald, T. C. Lindley, and C. E. Richards:Mat. Sci. Eng., 1972, vol. 10, p. 235.CrossRefGoogle Scholar

Copyright information

© The Metallurgical of Society of AIME 1972

Authors and Affiliations

  • A. R. Rosenfield
    • 1
  • G. T. Hahn
    • 1
  • J. D. Embury
    • 2
  1. 1.Battelle Columbus LaboratoriesColumbus
  2. 2.Department of Metallurgy and Materials ScienceMcMaster UniversityHamiltonCanada

Personalised recommendations