, Volume 3, Issue 11, pp 2757–2767 | Cite as

The genesis of the cellular precipitation reaction

  • R. A. Fournelle
  • J. B. Clark
Symposium on the Cellular and Pearlite Reactions

Abstract

The morphology of cellular precipitation in a Cu-9.5 at. pet In alloy has been investigated by light and electron microscopy. Both cellular and general precipitation were observed to occur simultaneously in quenched and aged alloys while only cellular precipitation was observed to occur in isothermally aged alloys. Because of the presence of wide, solute rich, precipitate free zones in the vicinity of grain boundaries in the quenched and aged alloys, the early development of cellular precipitation was found to be identical for both types of heat treatment. From light and electron microscopy observations of the early stages of cellular precipitation a mechanism for the formation of cells was developed. At the start of aging, the unoccupied grain boundary begins to migrate under the influence of grain boundary migration forces as if it were in a single phase alloy. As the boundary migrates, solute segregates along it to form allotriomorphs which pin the boundary. The boundary continues to migrate and bows between the simultaneously forming allotriomorphs. With further aging, the allotriomorphs lengthen following the bowing boundary and the allotriomorphs become the initial precipitate lamellae of the developing cell as a steady-state lamellar structure develops. Assuming that the critical step in the development of a cell is the ability of the boundary to bow between the initial allotriomorphs, a criterion for the occurrence of cellular precipitation was developed.

Keywords

Metallurgical Transaction Aging Temperature Aged Alloy Boundary Migration Precipitate Free Zone 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    C. S. Smith:Trans. ASM, 1953, vol. 45, pp. 533–75.Google Scholar
  2. 2.
    P. A. Beck and P. R. Sperry:J. Appl. Phys., 1950, vol. 21, pp. 150–52.CrossRefGoogle Scholar
  3. 3.
    D. Turnbull:Acta Met., 1955, vol. 3, pp. 55–63.CrossRefGoogle Scholar
  4. 4.
    J. W. Cahn:Acta Met, 1959, vol. 7, pp. 18–28.CrossRefGoogle Scholar
  5. 5.
    K. N. Tu and D. Turnbull:Acta Met., 1967, vol. 15, pp. 369–76.CrossRefGoogle Scholar
  6. 6.
    N. Tu and D. Turnbull:Acta Met., 1967,vol. 15,pp. 1317–23.CrossRefGoogle Scholar
  7. 7.
    K. N. Tu and D. Turnbull:Acta Met, 1969, vol. 17, pp. 1263–79.CrossRefGoogle Scholar
  8. 8.
    D. Turnbull and K. N. Tu:Phase Tranformations, pp. 487-95, American Society for Metals, 1970.Google Scholar
  9. 9.
    G. R. Speich:Trans. TMS-AIME, 1968, vol. 242, pp. 1359–67.Google Scholar
  10. 10.
    J. M. Shapiro: Ph.D. thesis, McMaster University, 1966.Google Scholar
  11. 11.
    J. M. Shapiro and J. S. Kirkaldy:Acta Met, 1968, vol. 16, pp. 1239–52.CrossRefGoogle Scholar
  12. 12.
    J. B. Clark:Acta Met, 1968, vol. 16, pp. 141–52.CrossRefGoogle Scholar
  13. 13.
    J. B. Clark:High Temperature, High Resolution Metallography, H. I. Aaronson and G. Ansell, eds., pp. 347-75, Gordon and Breach Science Publications, 1967.Google Scholar
  14. 14.
    M. Hansen and K. Anderko:Constitution of Binary Alloys, 2nd ed., pp. 590- 92, McGraw-Hill Book Co., New York, 1958.Google Scholar
  15. 15.
    J. Reynolds, W. A. Wiseman, and W. Hume-Rothery:J. Inst. Metals, 1951-52, vol. 80, pp. 63740.Google Scholar
  16. 16.
    D. J. H. Corderoy and R. W. K. Honeycombe:J. Inst. Metals, 1963-64, vol. 92, pp. 65–69.Google Scholar
  17. 17.
    H. Böhm:Z Metallk., 1959, vol. 50, pp. 87–93.Google Scholar
  18. 18.
    G. L. Kehl:The Principles of Metallographic Laboratory Practice, 3rd ed., p. 420, McGraw-Hill Book Co., New York, 1949.Google Scholar
  19. 19.
    R. A. Fournelle: Ph.D. thesis, University of Missouri-Rolla, 1971.Google Scholar
  20. 20.
    N. A. Gjostein and F. M. Rhines:Acta Met., 1959, vol. 7, pp. 319–30.CrossRefGoogle Scholar
  21. 21.
    J. C. M. Li:Recovery, Recrystallization, Grain Growth, and Textures, pp. 45-97, American Society for Metals, 1966.Google Scholar
  22. 22.
    J. E. Bailey:Phil. Mag., 1960, vol. 5, pp. 83342.Google Scholar
  23. 23.
    J. E. Bailey and P. B. Hirsch:Proc. Roy. Soc, Ser. A, 1962, vol. 267, pp. 11–30.CrossRefGoogle Scholar

Copyright information

© The Metallurgical of Society of AIME 1972

Authors and Affiliations

  • R. A. Fournelle
    • 1
  • J. B. Clark
    • 2
  1. 1.Department of Mechanical EngineeringMarquette UniversityMilwaukee
  2. 2.Metallurgical EngineeringUniversity of Missouri-RollaRolla

Personalised recommendations