Metallurgical and Materials Transactions A

, Volume 27, Issue 8, pp 2178–2186 | Cite as

The role of coincident site lattice boundaries during selective growth in interstitial-free steels

  • Peter Gangli
  • Leo Kestens
  • John J. Jonas
Transformations
Received:

Abstract

The development of textures in interstitial-free (IF) steels as a result of annealing after cold rolling is described with the help of a combined nucleation and growth model. Nucleation is simulated by assuming that high stored energy nucleation occurs preferentially in high Taylor factor regions in the 75 to 85 pct cold reduced materials. Growth of the nuclei then takes place by means of Σ (110) type as well as by Σ 7 (111) type coincident site lattice (CSL) transformations. Of the six symmetrically equivalent (110) transformation axes, only the ones near the maximum shear stress poles are assumed to operate. The effects of the migration of individual Σ 9, Σ 11, Σ 17c, Σ 19a, Σ 33a, and Σ 33c (110) boundaries are analyzed. Their relative mobilities and contributions to the final texture are deduced by matching the simulated and experimental preferred orientations using a /ldleast-squares” method. On the basis of experimental results for two steels, the various boundary types are observed to have the following mobility ratios: Σ 33a: 12, Σ 19a:4, Σ 9:1, Σ 33c:l, and Σ 17c: 2.

Keywords

Material Transaction Selective Growth Recrystallization Texture Coincident Site Lattice Deformation Texture 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    F.J. Humphreys and M. Hatherly:Rectystallization and Related Annealing Phenomena, Elsevier Science Ltd., Oxford, United Kingdom, 1995.Google Scholar
  2. 2.
    T. Urabe and J.J. Jonas:Iron Steel Inst. Jpn. Int., 1994, vol. 34, pp. 435–42.Google Scholar
  3. 3.
    J.J. Jonas and T. Urabe:Int. Forum for Physical Metallurgy of IF Steels (IF IFS-94), The Iron and Steel Institute of Japan, 1994, Tokyo, pp. 77–94.Google Scholar
  4. 4.
    T. Urabe, J. Savoie, and J.J. Jonas:Int. Forum for Physical Metallurgy of IF Steels (IF IFS-94), The Iron and Steel Institute of Japan, Tokyo, 1994, pp. 141–44.Google Scholar
  5. 5.
    P. Gangli, J.J. Jonas, and T. Urabe:Metall. Mater. Trans. A, 1995, vol. 26A, pp. 2399–2406.Google Scholar
  6. 6.
    L. Kestens and J.J. Jonas:Metall. Mater. Trans. A, 1996, vol. 27A, Paper No. 95-142A, pp. 155–64.CrossRefGoogle Scholar
  7. 7.
    L. Kestens and J.J. Jonas:16th Rise Symp. on Materials Science, Risø, Denmark, 1995, pp. 393–98.Google Scholar
  8. 8.
    J.J. Jonas and L. Kestens:2nd Int. Conf. on Grain Growth (ICGG-II), Kitakyushu, Japan, 1995, May, in press.Google Scholar
  9. 9.
    T. Watanabe: inGrain Growth in Poly crystalline Materials (1CGG-1), C. Abruzzese and P. Brozzo, eds.;Mater. Sci. Forum, 1992, 1994–96, pp. 209–20.Google Scholar
  10. 10.
    K.T. Aust and J.W. Rutter:Trans. AIME, 1960, vol. 218, pp. 1023–28.Google Scholar
  11. 11.
    P. Gangli, L. Kestens, and J.J. Jonas:2nd Int. Conf. on Grain Growth (ICGG-II), Kitakyushu, Japan, The Iron and Steel Institute of Japan, Tokyo, 1995, May, pp. 667–72.Google Scholar
  12. 12.
    E. Lindh, B. Hutchinson, and P. Bate:(ICOTOM-10) Mater. Sci. Forum, 1994, vols. 157–162, pp. 997–1002.Google Scholar
  13. 13.
    H.J. Bunge:Texture Analysis in Materials Science, Butterworth and Co., London, 1982.Google Scholar
  14. 14.
    D.G. Brandon:Acta Metall., 1966, vol. 14, pp. 1479–84.CrossRefGoogle Scholar
  15. 15.
    D. Vanderschueren:Forum for Physical Metallurgy of IF Steels (IF IFS-94), The Iron and Steel Institute of Japan, Tokyo, 1994, May, pp. 145–48.Google Scholar
  16. 16.
    G. Ibe and K. Lücke:Recrystallization, Grain Growth and Textures, H. Margolin, ed., ASM, Metals Park, OH, 1966, pp. 434–44.Google Scholar
  17. 17.
    D. Wolf:Phil. Mag. B., 1989, vol. 6, pp. 667–80.Google Scholar
  18. 18.
    G. Gottstein and F. Schwarzer: inGrain Growth in Polycrystalline Materials (ICG-I), G. Abruzzeze and P. Brozzo, eds.;Mater. Sci. Forum, 1992, vols. 94–96, pp. 187–208.Google Scholar
  19. 19.
    W.B. Hutchinson and E. Lindh:Forum for Physical Metallurgy of IF Steels (IFIFS-94), The Iron and Steel Institute of Japan, Tokyo, 1994, May, pp. 127–40.Google Scholar
  20. 20.
    B. Hutchinson and L. Ryde:16th Risø Symp. on Materials Science, Risø, Denmark, 1995, pp. 105–17.Google Scholar
  21. 21.
    R. Watanabe, A. Nogami, and T. Matsumiya:2nd Int. Conf. on Grain Growth (ICGG-II), Kitakyushu, Japan, The Iron and Steel Institute of Japan, Tokyo, 1995, May, pp. 227–32.Google Scholar

Copyright information

© The Minerals, Metals & Material Society 1996

Authors and Affiliations

  • Peter Gangli
    • 1
  • Leo Kestens
    • 2
  • John J. Jonas
    • 3
  1. 1.FE2000 Inc.VaudreuilCanada
  2. 2.Department of Flat RollingCenter for Research in MetallurgyGentBelgium
  3. 3.Department of Metallurgical EngineeringMcGill UniversityMontrealCanada

Personalised recommendations