Holz als Roh- und Werkstoff

, Volume 37, Issue 10, pp 389–393 | Cite as

The properties of UF-resins with low formaldehyde content and particle boards bounded with these resins

Part 1: Influence of the molar ratio on the properties of uncondensed resins
  • R. Marutzky
  • L. Ranta
Forschung und Praxis

Abstract

The influence of the molar ratio of urea: formaldehyde on the chemical, physical, and technological properties of the uncondensed resins was investigated. The molar ratio of the industrial resins varied between 1:2,1 and 1:1,2. Viscosity, water compatibility, stability and free formaldehyde content of the uncondensed resins are influenced significantly by the molar ratio. Using common ammonium salt hardeners, the hardening reaction decreased considerably for resins with low formaldehyde content.

Keywords

Formaldehyde Content Formaldehyd Ammonium Peroxodisulfate Free Formaldehyde Content Industrial Resin 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Die Eigenschaften formaldehydarmer HF-Leimharze und daraus hergestellter Holzspanplatten

Zusammenfassung

Untersucht wurde der Einfluß des Molverhältnisses Harnstoff zu Formaldehyd im Bereich H:F zwischen 1:2,1 und 1:1,2 auf die chemischen, physikalischen und technologischen Eigenschaften industrieller HF-Rohleimharze. Das Molverhältnis beeinflußt besonders Viskosität, Wasserverträglichkeit. Lagerstabilität und Gehalt an freiem Formaldehyd der Vorkondensate. Der geringe Gehalt an freiem Formaldehyd bei den formaldehydärmeren Leimharztypen vermindert die Härtungsgeschwindigkeit bei Verwendung der üblichen Ammoniumsalzhärter erheblich.

This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Literatur

  1. Dankelman, W., de Wit, I. 1976: Moderne Methoden zur Analyse von Harnstoff-Formaldehyd-Harzen. Holz Roh-Werkstoff 34: 131–134Google Scholar
  2. Marutzky, R., Ranta, L., Schriever, E. 1978: Untersuchungen zum Molverhältnis und zum Melamingehalt von Harnstoff-Formaldehyd-Leimharzen. Holz-Zbl. 104: 1747Google Scholar
  3. Marutzky, R., Roffael, E., Ranta, L. 1979: Untersuchungen über den Zusammenhang zwischen dem Molverhältnis und der Formaldehydabgabe bei Harnstoff-Formaldehyd-Leimharzen. Holz Roh-Werkstoff 35: 303–307CrossRefGoogle Scholar
  4. Plath, E. 1958: Die Härtung von Duroplasten bei der Herstellung von Holzwerkstoffen. Holz Roh-Werkstoff 16: 490–494Google Scholar
  5. Roffael, E. 1975: Messung der Formaldehydabgabe. Holz-Zbl. 101: 1403Google Scholar
  6. Schindlbauer, H. 1979: Aminoplastharze: Neue Untersuchungsmethoden und Folgerungen. Vortrag auf dem Mobil Oil Symposium in AugsburgGoogle Scholar
  7. Schindlbauer, H., Holzhöfer, B., Schuster, I. 1979: Fortschritte in der Analyse von Harnstoff-Formaldehyd-Kondensaten. Kunststoffe 69: 158–162Google Scholar
  8. Sell, J. 1977: Schadensfälle bei der Verwendung von Holz im Bauwesen. Bauforum 10: 20–22Google Scholar
  9. Staudinger, H., Wagner, K., 1954: Über die Konstitution der Harnstoff-resp. Thioharnstoff-Formaldehydkondensate, Makromolekulare Chem. 12: 168–235CrossRefGoogle Scholar
  10. Verbestel, I. 1967: Proceedings of the Formalin Committee. 18th Meeting of Engineering Committee FESYPGoogle Scholar

Copyright information

© Springer-Verlag 1979

Authors and Affiliations

  • R. Marutzky
  • L. Ranta

There are no affiliations available

Personalised recommendations