, Volume 45, Issue 5, pp 1167–1174 | Cite as

Dynamic mechanical analysis

Thermal degradation of a diglycidyl ether of bisphenol A and 1,3-bisaminomethylcyclohexane epoxy resin system
  • L. Barral
  • J. Cano
  • A. J. López
  • J. López
  • P. Nogueira
  • C. Ramírez
Oral and Poster Presentations Inorganic Materials Organic Materials Polymers

Abstract

Using dynamic mechanical analysis (DMA) we have studied thermal degradation for a system containing a diglycidyl ether of bisphenol A (DGEBA) and 1,3-bisaminomethylcylohexane (1,3-BAC). The changes of dynamic mechanical properties during thermal degradation indicated a shift of the glass transition temperature (T g) to higher temperatures and a decrease in the peak value of the dynamic loss factor (tan δ) with an increasing of aging time. The value of dynamic storage modulus (E′) at the rubbery state showed an increase with aging time, whiteE′ at the glassy state only underwent a moderate change with increased thermal degradation. From these results it can be argued that thermal degradation during the stage prior to the onset of the severe degradation involves structural changes in the epoxy system, as further crosslinking and loss of dangling chains in the crosslinked network.

Keywords

DMA epoxy resins thermal degradation 

Zusammenfassung

Mittels Dynamischer Mechanischer Analyse (DMA) wurde der thermische Abbau eines Systemes mit Gehalt an Diglycidylester von Bisphenol A (DGEBA) und 1,3-Bisaminomethylcyclohexan (1,3-BAC) untersucht. Die Änderungen der dynamischen mechanischen Eigenschaften während des thermischen Abbaues zeigen eine Verschiebung des Glasumwandlungspunktes (T g) in Richtung höherer Temperaturen und eine Abnahme des Peakwertes von tan δ bei zunehmender Alterungszeit. Der Wert vonE′ im gummiartigen Zustand zeigt eine Zunahme mit der Alterungszeit, währendE′ im glasartigen Zustand mit zunehmendem thermischen Abbau nur einer mäßigen Änderung unterliegt. Anhand dieser Ergebnisse kann darauf geschlossen werden, daß der thermische Abbau während des Zustandes vor Einsetzen des starken Abbaues strukturelle Veränderungen im Epoxysystem umfaßt, wie zum Beispiel Vernetzung und der Verlust von freien Ketten im Netzwerk.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    N. Grassie and G. Scott, Polymer Degradation and Stabilization, Cambridge University Press, 1985, p. 9.Google Scholar
  2. 2.
    N. Grassie and M. I. Guy, Polym. Degrad. Stabil., 13 (1985) 11.CrossRefGoogle Scholar
  3. 3.
    N. Grassie and M. I. Guy, Polym. Degrad. Stabil., 14 (1986) 125.CrossRefGoogle Scholar
  4. 4.
    A. Jiménez, V. Berenguer, J. López, and A. Sánchez, J. Appl. Polym. Sci., 50 (1993) 1565.CrossRefGoogle Scholar
  5. 5.
    S. D. Smith, T. E. Long and J. E. McGrath, J. Polym. Sci., Part A, Polym. Chem. 32 (1994) 1747.CrossRefGoogle Scholar
  6. 6.
    J. Unsworth and Y. Li, J. Appl. Polym. Sci., 46 (1992) 1375.CrossRefGoogle Scholar
  7. 7.
    L. Barral, J. Cano, A. J. López, P. Nogueira, and C. Ramírez, J. Thermal Anal., 41 (1994) 1463.Google Scholar
  8. 8.
    L. Barral, J. Cano, A. J. López, J. López, P. Nogueira and C. Ramírez, 13th IUPAC Conference on Chemical Thermodynamics, Clermont-Ferrand, July 17–22, 1994.Google Scholar
  9. 9.
    L. E. Nielsen and R. F. Landel, Mechanical Properties of Polymer and Composites, 2nd ed., Marcel Dekker, 1994.Google Scholar
  10. 10.
    T. Kamon and H. Furukawa, Advances in Polymer Sci., Vol. 80; Epoxy Resins and Composites IV, K. Dusek, Springer-Verlag, Berlin 1986.Google Scholar

Copyright information

© Akadémiai Kiadó 1995

Authors and Affiliations

  • L. Barral
    • 1
  • J. Cano
    • 1
  • A. J. López
    • 1
  • J. López
    • 1
  • P. Nogueira
    • 1
  • C. Ramírez
    • 1
  1. 1.E.U.P. Ferrol, Departamento de FísicaUniversidad de la CoruñaFerrolSpain

Personalised recommendations