Reaction Kinetics and Catalysis Letters

, Volume 36, Issue 2, pp 447–453 | Cite as

Effect of Rh/Al2O3 on the reduction of ZnO in a mechanical mixture of these components

  • W. K. Jóżwiak
  • P. Zieliński
  • T. Paryjczak
Article
Received:
Accepted:

Abstract

The effect of reoxidation temperature on TPR of 5% Rh/Al2O3 catalyst and its mechanical mixture with ZnO has been investigated. The results suggest bimodal character of supported rhodium and surprisingly high effect of this metal on ZnO reduction in the mixture.

Keywords

Physical Chemistry Catalysis Rhodium High Effect Mechanical Mixture 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Abstract

Исследовано влияние температуры переокисления на ТПВ катализатора 5% Rh/Al2O3 и его механической смеси с ZnO. Нанесенному родию приписывают бимодальный характер, который оказывает исключительно сильный эффект на восстановление ZnO в смеси.

This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    W.K. Jóżwiak, T. Paryjczak: J. Catal.,79, 196 (1983)Google Scholar
  2. 2.
    T. Paryjczak, W.K. Jóźwiak, J. Góralski: J. Chromatogr.,166, 65 (1978)Google Scholar
  3. 3.
    T. Paryjczak, W.K. Jóźwiak: J. Chromatogr.,111, 443 (1975)Google Scholar
  4. 4.
    W.K. Jóźwiak, P. Zielinski, T. Paryjczak: React. Kinet. Catal. Lett., submitted for publicationGoogle Scholar
  5. 5.
    H.F. J. Van't Blik: Ph.D. dissertation, Technical University of Eindhoven, 1984.Google Scholar
  6. 6.
    H.C. Yao, S. Japav, M. Shelef: J. Catal.,50, 407 (1977)Google Scholar
  7. 7.
    F. Runge, F. Gopal: Z. Phys. Chem.,123, 175 (1980)Google Scholar

Copyright information

© Akadémiai Kiadó 1988

Authors and Affiliations

  • W. K. Jóżwiak
    • 1
  • P. Zieliński
    • 1
  • T. Paryjczak
    • 1
  1. 1.Institute of General ChemistryTechnical University of LódzLódzPoland

Personalised recommendations