Thermal analysis of eucalptus camaldulensis and cotton stalks at different heating rates

  • Zenat Adeeb Nagieb
Article
Received:

Abstract

The thermal decomposition of Eucalptus Camaldulensis and Cotton Stalks at different heating rates showed three exothermic peaks. The heating rate is the factor that affects their sharpness and position. The peaks are sharp at low heating rates. IR spectra of pyrolized residue at different temperature were also studied.

Keywords

Polymer Physical Chemistry Inorganic Chemistry Heating Rate Thermal Analysis 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Zusammenfassung

Bei der thermischen Zersetzung von Eucalptus Camaldulensis und Baumwollstengeln bei verschiedenen Aufheizgeschwindigkeiten zeigen sich drei exotherme Peaks. Ihre Breite und Lage wird durch die Aufheizgeschwindigkeit beeinflu\t. Bei niedrigen Aufheizgeschwindigkeiten ergeben sich scharfe Peaks. IR-Spektren des pyrolisierten Rückstandes wurden bei verschiedenen Temperaturen ebenfalls untersucht.

This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    F. Kollmann, Holz Als Roh und Werkstoff, 18 (1960) 193.Google Scholar
  2. 2.
    A. Gillet and J. Urlings, Chimie & Industrie 67 (1952) 909.Google Scholar
  3. 3.
    A. Gillet and J. Urlings, Chimie & Industrie 68 (1953) 55.Google Scholar
  4. 4.
    A. Gillet and J. Urlings, Chimie & Industrie, 70 (1953) 64.Google Scholar
  5. 5.
    L. F. Hawley, In Wood Chemistry; L. E. Wise, and E. C. Jahn, Eds. Reinhold Publ. Corp., New York, N. Y. 1952; Chap. 19. pp 817–825.Google Scholar
  6. 6.
    F. L. Browne, Theories on the Combustion of Wood and its Control. U. S. Forest Prod. Lab, 1958; Rep. 2136 59 pp., Madison, Wis.Google Scholar
  7. 7.
    L. Amy, The Physico-Chemical Bases of the Combustion of Cellulose and Ligneous Materials. Cah. du Centre Tech. du Bois, 1961: No. 45, 30 pp.Google Scholar
  8. 8.
    V. G. Jayme and H. Knolle, Papier 18 (1964) 249.Google Scholar
  9. 9.
    F. C. Beall, Wood Fiber. 1 (1969) 215.Google Scholar
  10. 10.
    M. Kosik, F. Kozmal, V. Reiser and R. Domansky, Holzforsch. Holzverw, 20 (1968) 11.Google Scholar
  11. 11.
    W. Sandermann, and H. Augustin, Holz Roh-Werk Stoff, 21 (1963) 305.Google Scholar
  12. 12.
    D. Dollimore and B. Holt, J. Polym. Sci., 11 (1973) 1703.Google Scholar
  13. 13.
    R. Domansky and F. Rendos, Holz Roh-Werkstoff, 20 (1962) 473.Google Scholar
  14. 14.
    G. V. Domburg, M. Sergeeval, F. K. Koshik and A. Kalninsh, New Aspects and Tasks of Differential Thermal Analysis in Wood Chemistry. 1969. Schwenker Jr., R. F.; Garn P. D. Eds. Academic Press, New York p. 623.Google Scholar
  15. 15.
    G. Domburgs and V. N. Sergeeva, Zinatnu-Akad. Vestis, Kim. Ser. 5, (1964) 625.Google Scholar
  16. 16.
    C. Y. Liang and R. H. Marchessault, J. Polym Sci. 37 (1939) 385.CrossRefGoogle Scholar
  17. 17.
    H. W. Eickner, For Prod. J. 12 (1962) 194.Google Scholar
  18. 18.
    J. J. Oren, M. M. Nassar and G. D. M. Mackay, Can. J. Spectroscopy, 29 (1984) 10.Google Scholar
  19. 19.
    K. Kudo and E. J. Yoshida, Japan Wood Res. Soc. 4 (1957) 125.Google Scholar
  20. 20.
    J. D. Ferry, Viscoelastic Properties of Polymers. John Wiley and Sons, Inc., New York, (1961) 482.Google Scholar
  21. 21.
    K. Okano, S. Iwayanagi, T. Hideshima, Molecular Motion in Solid State Polymers. (1963). In S. Frederick and T. David, eds. Academic Press, New York p. 343.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1990

Authors and Affiliations

  • Zenat Adeeb Nagieb
    • 1
  1. 1.Cellulose and Paper laboratoryNational Research CentreDokki, CairoEgypt

Personalised recommendations