Czechoslovak Journal of Physics B

, Volume 39, Issue 6, pp 669–672 | Cite as

The effect of high temperature rolling on structure of copper single crystals of different orientation

  • Włodzimierz Bochniak
Article
Received:
  • 29 Downloads

Abstract

The work brings the data about the substructure development in single crystals of copper deformed up to about 50% of cross section reduction in rolling at high temperature. No recrystallization process was found. Instead a tendency toward inhomogeneous deformation manifesting itself in crystallographicaly oriented microbands was observed. The results are discussed in terms of the role of dynamical recovery on development of structure and its evolution in the microbands areas.

Keywords

Copper Recrystallization Dynamical Recovery Substructure Development Recrystallization Process 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Bourelier F., LeHericy J.: Ecrouissage, Restauration Recristallisation. Press Univ. France, Paris, 1963, p. 33.Google Scholar
  2. [2]
    Korbel A., Martin P.: Acta Metall.34 (1986) 1905.Google Scholar
  3. [3]
    Korbel A., Szczerba M.: Acta Metall.30 (1982) 1961.Google Scholar
  4. [4]
    Ray R. K., Hutchinson W. B., Duggan B. J.: Acta Metall.23 (1975) 831.Google Scholar
  5. [5]
    Rossard C.:in Proc. 3rd Inter. Conf. Strength Met. Alloys, Cambridge, 1973, p. 175.Google Scholar
  6. [6]
    Bochniak W.:in Proc. 7th Inter. Symp. Annealing Processes... (eds. Hansen et al.). RisØ, 1986, p. 235.Google Scholar
  7. [7]
    Korbel A., Bochniak W., Blaz L., Embury J. D.: Met. Sci.18 (1984) 216.Google Scholar
  8. [8]
    Karduck P., Gottstein G., Mecking H.: Acta Metall.31 (1983) 1525.Google Scholar
  9. [9]
    Korbel A., RyŚ J., Szczerba M.: Acta Metall.33 (1985) 2215.Google Scholar
  10. [10]
    Morii K., Mecking H., Nakayama Y.: Acta Metall.33 (1985) 379.Google Scholar
  11. [11]
    Duggan B. J., Hatherly M., Hutchinson W. B., Wakefleld P. T.: Met. Sci.12 (1978) 343.Google Scholar
  12. [12]
    Duggan B. J., Hutchinson W. B., Hatherly M.; Scr. Metall.12 (1978) 293.Google Scholar
  13. [13]
    Morii K., Mera M., Nakayama Y.: Trans. Jpn. Inst. Met.21 (1980) 20.Google Scholar

Copyright information

© Academia, Publishing House of the Czechoslovak Academy of Sciences 1989

Authors and Affiliations

  • Włodzimierz Bochniak
    • 1
  1. 1.Institute for Metals Working and Physical MetallurgyAcademy of Mining and MetallurgyKrakówPoland

Personalised recommendations