Particle size and sol stability in metal colloids

  • G. Frens
Originalarbeiten Kolloide

Summary

It is shown experimentally that the stability of metal sols depends on particle size. Sols with small particles are more stable against electrolyte coagulation than coarser suspensions. It is possible to separate metal particles of different radii by fractionated coagulation. Results are explained from the diminishedvan der Waals attraction between small particles. Consequences for the repeptization of metal sols and for the measurement ofHamaker constants are discussed. It is concluded that the smallness of the particles is a decisive factor for the stability of metal colloids.

Keywords

Polymer Particle Size Physical Chemistry Small Particle Metal Particle 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Zusammenfassung

Es wird gezeigt, daß die Stabilität von Metallkolloiden von der Teilchengröße abhängig ist. Systeme aus kleinen Teilchen sind bei Elektrolytkoagulation wesentlich stabiler als Systeme mit größeren Teilchen. Durch fraktionierte Flockung werden Kolloidteilchen dem Teilchenradius nach getrennt. Die Erklärung dieser Ergebnisse folgt aus der verringertenvan der Waalsschen Anziehung zwischen kleinen Teilchen. Konsequenzen für die Repeptisierung von Metallkolloiden und für die Bestimmung derHamakerschen Konstante werden diskutiert. Die Stabilität der Metallkolloide wird von der Teilchengröße weitgehend beeinflußt.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1).
    Krupp, H., Adv. Coll. Int. Sc.1, 111 (1967).Google Scholar
  2. 2).
    Deryagin, B. V., V. M. Muller, andYa. T. Rabinovich, Koll. Zh.31, 304 (1969).Google Scholar
  3. 3).
    Rouweler, G. C. J., Chem. Phys. Lett.8, 275 (1971).Google Scholar
  4. 4).
    Ottewill, R. H. andJ. N. Shaw, Disc. Far. Soc.42, 154 (1966).Google Scholar
  5. 5).
    Reerink, H. andJ. Th. G. Overbeek, Disc. Far. Soc.18, 74 (1954).Google Scholar
  6. 6).
    Turkevich, J., J. Hillier, andP. C. Stevenson, Disc. Far. Soc.11, 55 (1951).Google Scholar
  7. 7).
    Frens, G., to be published.Google Scholar
  8. 8).
    Zsigmondy-Thiessen, Das kolloide Gold. pg. 48, 64 (Leipzig 1925).Google Scholar
  9. 9).
    Frens, G., Kolloid-Z. u. Z. Polymere233, 922 (1969).Google Scholar
  10. 10).
    Holliday, A. K., Trans. Far. Soc.43, 661 (1947).Google Scholar
  11. 11).
    Hamaker, H. C., Physica4, 1058 (1937).Google Scholar
  12. 12).
    Hoskin, N. E. andS. Levine, Phil. Trans. Roy. Soc.A248, 433 (1956).Google Scholar
  13. 13).
    McCartney, L. N. andS. Levine, J. Coll. Int. Sc.30, 345 (1969).Google Scholar
  14. 14).
    Frens, G., J. Coll. Int. Sc., in press.Google Scholar
  15. 15).
    Langbein, D., J. Phys. Chem. Solids32, 1657 (1971).Google Scholar

Copyright information

© Dr. Dietrich Steinkopff Verlag 1972

Authors and Affiliations

  • G. Frens
    • 1
  1. 1.Philips Research LaboratoriesN. V. Philips' GloeilampenfabriekenEindhovenThe Netherlands

Personalised recommendations